Reduction of the hot cracking sensitivity of CM-247LC superalloy processed by laser cladding using induction preheating

In the present work, the repair of CM-247LC superalloy has been investigated by using a laser cladding process. Since this material is well known for its high hot-cracking susceptibility in Heat Affected Zone during welding, repairing is quite challenging. In a first stage, a detailed investigation of the effect of cladding parameters on the crack susceptibility was carried out on coupons that received a low pre-heating condition. However, despite a reduction of crack sensitivity for low energy inputs, this material has systematically shown some evidence of cracking in the HAZ. In a second stage, attempts were made to reduce crack defects by using an induction preheating, with higher temperatures in the range of 800–1100 °C. With the highest pre-heating temperatures near 1100 °C, the partial dissolution of large γ’ precipitates, combined with re-precipitation of secondary and smaller γ' precipitates were helpful to prevent hot cracking

Nouvelles voies de synthèse de structures polyaromatiques soufrées et azotées

L'objectif de la thèse a consisté à mettre au point une voie de synthèse directe de composés de type arylbenzo[b]thiophène afin de pouvoir constituer une bibliothèque de produits possédant ce motif. Nous optimisé une réaction de couplage de type Heck entre un benzo[b]thiophène et un halogénure d'aryle que nous avons ensuite appliquée aux thiophènes. Une fonctionnalisation de benzo[b]thiophènes nous a permis d'accéder à des précurseurs d'acides aminés. Enfin, nous avons proposé une méthodologie originale de synthèse de nouveaux composés polycycliques thioazotés qui pourront constituer une plateforme pour accéder aux quinoléines et tétrahydroquinoléines 2,3-diarylées. Les premiers résultats des tests biologiques entrepris sur les molécules synthétisées, dont certaines possèdent une activité inhibitrice de pompe d'efflux, ont été présentésLYON1-BU.Sciences (692662101) / SudocSudocFranceF

Rechargement laser d'un superalliage à base de nickel (étude expérimentale et modélisation de l'endommagement)

Le rechargement laser est un procédé de type soudage utilisé notamment pour la reconstruction de la géométrie de pièces métalliques aéronautiques en superalliage à base de nickel. Une fissuration de type interdendritique fragile est systématiquement observée au niveau de la zone réparée. Après une étude métallurgique de l endommagement, l hypothèse d une fragilisation par ségrégation interfaciale de soufre a pu être confirmée au moyen de deux techniques: la spectroscopie des électrons Auger et la microsonde de Castaing. L aptitude de cette dernière à la détection et à la quantification des ségrégations interfaciales a été montrée au cours de ces travaux. Une modélisation fine de la thermique du procédé et de la ségrégation interfaciale à l aide des éléments finis a permis de mettre en évidence le caractère inévitable de la ségrégation du soufre aux interfaces. Notamment, il a été montré grâce à la simulation numérique qu il n était pas possible de contrôler la ségrégation interfaciale en jouant sur les paramètres du procédé que sont la puissance et la vitesse du laser. En outre, les procédés de type soudage sont connus pour générer d importantes contraintes et déformations résiduelles. Un état de contraintes résiduelles de traction dans la zone réparée, associé à des déformations plastiques importantes, a été simulé par éléments finis. Il est responsable de la rupture des joints interdendritiques fragilisés par la présence de quantités importantes de soufre. Au final, une étude paramétrique sur la puissance et la vitesse du procédé a été réalisée et a conduit à une solution au problème de fissurationLaser metal cladding is a welding-like process, in particular used to rebuild the shape of aeronautical components made of nickel based superalloys. Interdendritic cracks are systematically observed inside the repaired zone. After a metallurgical study of the damage, the hypothesis of an embrittlement by interfacial sulphur segregation has been confirmed by two techniques: Auger electron spectroscopy and electron probe micro-analysis. The ability of the latter to detect and quantify interfacial segregations has been demonstrated in the study. A fine modelling of the thermal aspects of the process and of interfacial segregation, using finite elements, allowed to show that sulphur segregation could not be avoided. In particular, it has been shown, using numerical simulation, that is not possible to control interfacial segregation through the adjustment of process parameters (laser power and velocity). Furthermore, welding processes are known to generate important residual stresses and plastic strains. A tensile residual stress state in the repaired zone, associated to important plastic strains, has been simulated using finite elements. It is responsible of the cracking of interdendritic boundaries embrittled by important quantities of sulphur. Finally, a parametric study of the process parameters (laser power and velocity) has been performed and has led to a solution to the cracking problemNANTES-BU Sciences (441092104) / SudocSudocFranceF

Cyclic elastoplastic behaviour of 2198-T8 aluminium alloy welded panels

International audienceThe Friction Stir Welding (FSW) process generally induces a gradient of properties and a softer behaviour along the welded joint. To design aeronautical structures welded by FSW in fatigue, it is necessary to study the impact of this localized soft behaviour on the overall structure. In this study, the 2198-T8 hardening structural aluminium alloy is considered. Monotonic and cyclic mechanical tests are performed by combining conventional extensometric measurements with digital image correlation (DIC) to measure the local displacement fields around the welded zone. Based on these experimental data, constitutive equations are proposed and identified, zone by zone, across the welded joint. In parallel, a quantification of T1 (Al 2 CuLi) strengthening precipitates is performed in different regions of the joint with a transmission electron microscope in order to identify a relationship between the microstructure and the mechanical parameters. Finally, once all the material parameters are identified, the model is validated by a 3D finite element analysis representative of FSW samples

Synthesis and inhibition of cancer cell proliferation of (1.3')-bis-tetrahydroisoquinolines and piperazine systems.

International audienc

Benzo[b]thiophene as a template for substituted quinolines and tetrahydroquinolines

International audienceAn original methodology starting from 3-aroyl-2-(2′-nitro-4′-methoxyphenyl)-benzo[b]thiophene allows the synthesis of unusual fused heterocycles. Direct hydrogenation with nickel catalysts followed by desulfurisation led to 2,3-diarylquinolines or 2,3-diaryltetrahydroquinolines

Towards dual photodynamic and antiangiogenic agents: design and synthesis of a phthalocyanine-chalcone conjugate.

International audienceA phthalocyanine-chalcone conjugate has been designed to combine the vascular disrupting effect of chalcones with the photodynamic effect of phthalocyanines. This potential dual photodynamic and antiangiogenic agent was obtained by the condensation of a tetrahydroxylated non-peripherally substituted Zn(II) phthalocyanine with an amino chalcone converted into the corresponding activated isocyanate. The conjugate was fully characterized