2 research outputs found
Adsorção do corante remazol amarelo ouro de solução aquosa por caroço de acerola: estudos cinéticos e de equilÃbrio.
This work was conducted to evaluate the efficiency of the acerola (Malpighia emarginata) core as adsorbent (ACB) and as a precursor of adsorbent charcoal (CAB) and activated charcoal (ACP), to remove the textile dye remazol golden yellow (RGY) in solution. The adsorbents characterization was obtained by Fourier-transform infrared spectroscopy, thermogravimetric analysis (TG) and determination of the specific area and the point of zero charge (pHpzc). The best conditions for adsorption for this adsorbent was reached through adsorbent mass studies and kinetic and equilibrium assays. The adsorption capacity q (mg.g-1) was used to analyze the effects. The pHpzc were 4.15 for ACB, 6.00 for CAB and 4.32 for ACP, demonstrating superficial charge favorable to dye adsorption. Considering the kinetic aspects, the pseudo-first order model adjusted more satisfactorily to experimental data. Related to isotherms, Langmuir was more efficient to represent experimental data of dye adsorption. ACB, CAB and ACP are potential adsorbents for dyes in effluents, presenting maximum adsorption capacity, in the study conditions, of 52.35 mg.g-1, 16.40 mg.g-1, and 119.00 mg.g-1, respectively.Neste trabalho, foi avaliada a eficiência de caroços de acerola (Malpighia emarginata) como adsorvente (ACB) e precursor de carvão (CAB) e carvão ativado (ACP) para a remoção do corante têxtil remazol amarelo ouro (RGY) em solução. A caracterização dos adsorventes foi feita por espectroscopia de infravermelho por transformada de Fourier, análise termogravimétrica (TG) e determinação da área especÃfica e do ponto de carga zero (pHpzc). As melhores condições de adsorção para esses adsorventes foram alcançadas após estudos de massa de adsorvente e testes cinéticos e de equilÃbrio. A capacidade adsortiva q (mg.g-1) foi utilizada para verificar a eficiência de adsorção. Os valores de pHpzc foram de 4,15 para ACB, 6,00 para CAB e 4,32 para ACP, mostrando uma carga superficial favorável para a adsorção do corante. Considerando a cinética, o modelo de pseudo-primeira ordem ajustou-se satisfatoriamente aos dados experimentais. Em relação à s isotermas, o modelo de Langmuir foi mais eficiente para representar os dados experimentais. ACB, CAB e ACP são potenciais adsorventes para corantes em efluentes, apresentando capacidade de adsorção máxima, nas condições desse estudo, de 52,35 mg.g-1, 16,40 mg.g-1 e 119,00 mg.g-1, respectivamente
Imobilização de dióxido de titânio em malha de alumÃnio reciclado para a degradação de corante têxtil por Fotocatálise Heterogênea por Redes Neurais
In this work, aluminum net crafted (recycled) were used as TiO2 support for the treatment of textile dye Remazol golden yellow (RGY 150). The immobilization of 200mg of TiO2 was accomplished after aluminum net calcination. The following experiments were carried out in a photocatalytic bench reactor: preliminary tests, a 23 factorial experimental design with best system and the degradation kinetic in systems with TiO2 supported on aluminum net.It was observed characteristic peaks of aluminum and TiO2 (anatase and rutile) by XRD and the catalyst film formation was verified by SEM. The system UV/H2O2/TiO2 performed higher efficiency, with 99% of dye degradation in 50 minutes, followed by the system UV/H2O2/TiO2sp with 93% of dye degradation. Whereas the supported catalyst presents execution advantages and high degradation rates, the factorial design was realized for this system, displaying best degradation (100% degradation in 35 minutes). It was obtained k = 0.114 min-1 and R² = 0.994 in a pseudo-first-order model adjustment system. The use of artificial neural network was proven to be efficient to predict the degradation of a textile dye, with an absolute error of 0.0181. After treatment, there was a decrease of dye toxicity.Neste trabalho, redes de alumÃnio recicladas foram utilizadas como suporte de TiO2 para o tratamento do corante têxtil Remazol amarelo ouro (RGY 150). A imobilização de 100 mg de TiO2 foi realizada após calcinação do material de alumÃnio. Foram conduzidos em reator de bancada fotocatalÃtico testes preliminares, um experimento fatorial 23 com o melhor sistema e a cinética de degradação em sistemas com TiO2 suportado em rede de alumÃnio. Foram observados picos caracterÃsticos de alumÃnio e TiO2 (anatase e rutilo) por DRX e a formação do filme catalÃtico foi verificada porMEV. O sistema UV/H2O2/TiO2 apresentou maior eficiência, com 99% de degradação do corante em 50 minutos, seguido do sistema UV/H2O2/TiO2sp com 93% de degradação do corante. Enquanto o catalisador suportado apresenta vantagens de execução e altas taxas de degradação, o planejamento fatorial foi realizado para este sistema, apresentando melhor degradação (100% de degradação em 35 minutos). Foi obtido k = 0,114 min-1 e R² = 0,994 em um sistema de ajuste de modelos de pseudo-primeira ordem. O uso da rede neural artificial mostrou-se eficiente para predizer a degradação de um corante têxtil, com erro absoluto de 0,0181. Após o tratamento, houve uma diminuição da toxicidade do corante