Possible Role of Microcrystallinity on Surface Properties of Titanium Surfaces for Biomedical Application

Dental implantology has grown tremendously, since the introduction of titanium. To enhance osseointegration, roughening techniques such as grit blasting, chemical etch, electrochemical anodization have been used with good results. An oxide layer mainly composed of TiO2 covers the surface of dental implants ensuring excellent corrosion resistance and chemical stability. Despite its biological role in achieving bone interlock, surprisingly, little is known about the structure of TiO2, which may be either amorphous or crystalline. Furthermore, at least two crystalline polymorph phases can be found at the bone–implant interface: anatase (tetragonal) and rutile (tetragonal). Therefore, besides the recognized importance of surface topography, energy, and charge, a more refined knowledge of surface chemistry is advisable when studying the bone–implant interface. Recently, sophisticated analysis techniques have been applied to dental implants such as Raman spectroscopy and X-ray diffraction to obtain structural-crystallographic characterization

Mechanical, electrical, thermal and tribological behavior of epoxy resin composites reinforced with waste hemp-derived carbon fibers

Short hemp fibers, an agricultural waste, were used for producing biochar by pyrolysis at 1000°C. The so-obtained hemp-derived carbon fibers (HFB) were used as filler for improving the properties of an epoxy resin using a simple casting and curing process. The addition of HFB in the epoxy matrix increases the storage modulus while damping factor is lowered. Also, the incorporation of HFB induces a remarkable increment of electrical conductivity reaching up to 6 mS/m with 10 wt% of loading. A similar trend is also observed during high frequency measurements. Furthermore, for the first time wear of these composites has been studied. The use of HFB is an efficient method for reducing the wear rate resistance and the friction coefficient (COF) of the epoxy resin. Excellent results are obtained for the composite containing 2.5 wt% of HFB, for which COF and wear rate decrease by 21% and 80%, respectively, as compared with those of the unfilled epoxy resin. The overall results prove how a common waste carbon source can significantly wide epoxy resin applications by a proper modulation of its electrical and wear properties

Effect of Hemp Hurd Biochar and Humic Acid on the Flame Retardant and Mechanical Properties of Ethylene Vinyl Acetate

In this work, the combination of biochar produced through a pyrolytic process of hemp hurd with commercial humic acid as a potential biomass-based flame-retardant system for ethylene vinyl acetate copolymer is thoroughly investigated. To this aim, ethylene vinyl acetate composites containing hemp-derived biochar at two different concentrations (i.e., 20 and 40 wt.%) and 10 wt.% of humic acid were prepared. The presence of increasing biochar loadings in ethylene vinyl acetate accounted for an increasing thermal and thermo-oxidative stability of the copolymer; conversely, the acidic character of humic acid anticipated the degradation of the copolymer matrix, even in the presence of the biochar. Further, as assessed by forced-combustion tests, the incorporation of humic acid only in ethylene vinyl acetate slightly decreased both peaks of heat release rate (pkHRR) and total heat release (THR, by 16% and 5%, respectively), with no effect on the burning time. At variance, for the composites containing biochar, a strong decrease in pkHRR and THR values was observed, approaching -69 and -29%, respectively, in the presence of the highest filler loading, notwithstanding, for this latter, a significant increase in the burning time (by about 50 s). Finally, the presence of humic acid significantly lowered the Young’s modulus, unlike biochar, for which the stiffness remarkably increased from 57 MPa (unfilled ethylene vinyl acetate) to 155 Mpa (for the composite containing 40 wt.% of the filler)

Electron-Beam-Induced Grafting of Chitosan onto HDPE/ATZ Composites for Biomedical Applications

The surface functionalisation of high-density polyethylene (HDPE) and HDPE/alumina-toughened zirconia (ATZ) surfaces with chitosan via electron-beam (EB) irradiation technique was exploited for preparing materials suitable for biomedical purposes. ATR–FTIR analysis and wettability measurements were employed for monitoring the surface changes after both irradiation and chitosan grafting reaction. Interestingly, the presence of ATZ loadings beyond 2 wt% influenced both the EB irradiation process and the chitosan functionalisation reaction, decreasing the oxidation of the surface and the chitosan grafting. The EB irradiation induced an increase in Young’s modulus and a decrease in the elongation at the break of all analysed systems, whereas the tensile strength was not affected in a relevant way. Biological assays indicated that electrostatic interactions between the negative charges of the surface of cell membranes and the –NH3+ sites on chitosan chains promoted cell adhesion, while some oxidised species produced during the irradiation process are thought to cause a detrimental effect on the cell viability

Mechanical and Biological Characterization of PMMA/Al2O3 Composites for Dental Implant Abutments

The mechanical and biological behaviors of PMMA/Al2O3 composites incorporating 30 wt.%, 40 wt.%, and 50 wt.% of Al2O3 were thoroughly characterized as regards to their possible application in implant-supported prostheses. The Al2O3 particles accounted for an increase in the flexural modulus of PMMA. The highest value was recorded for the composite containing 40 wt.% Al2O3 (4.50 GPa), which was about 18% higher than that of its unfilled counterpart (3.86 GPa). The Al2O3 particles caused a decrease in the flexural strength of the composites, due to the presence of filler aggregates and voids, though it was still satisfactory for the intended application. The roughness (Ra) and water contact angle had the same trend, ranging from 1.94 microns and 77.2° for unfilled PMMA to 2.45 microns and 105.8° for the composite containing the highest alumina loading, respectively, hence influencing both the protein adsorption and cell adhesion. No cytotoxic effects were found, confirming that all the specimens are biocompatible and capable of sustaining cell growth and proliferation, without remarkable differences at 24 and 48 h. Finally, Al2O3 was able to cause strong cell responses (cell orientation), thus guiding the tissue formation in contact with the composite itself and not enhancing its osteoconductive properties, supporting the PMMA composite’s usage in the envisaged application