Removal torque of zirconia abutment screws under dry and wet conditions

The aim of this study was to verify whether screw abutment lubrication can generate higher preload values compared to non-lubricated screws, a titanium abutment was screwed onto an implant analog and scanned with the Procera System to generate 20 zirconia abutments. MKIII Brånemark implants were clamped to a precision torque device, and the abutments were distributed in dry and wet groups with 10 specimens each. In the wet groups, the inner threads of the implants were filled with artificial saliva. All abutments were fastened with a Torqtite screw under 32 Ncm. Ten detorque measurements were performed per group pushing the reverse button of the Torque controller soon after screw tightening with values registered. The mean detorque values were calculated and compared by a Student's t test (?=0.05). The wet condition presented significantly higher mean detorque than the dry condition (31.5 ± 1.2 versus 27.5 ± 1.5 Ncm, respectively; p=0.0000024). In conclusion, there was always a loss in the initial torque values when the removal torque was measured under both conditions. The wet condition presented higher mean torque than the dry condition. Better preload values were established in the wet group, suggesting that the abutment screw must be lubricated in saliva to avoid further loosening.A fim de verificar se a lubrificação do parafuso do pilar pode gerar valores maiores de pré-carga do que nos parafusos não lubrificados, um pilar de titânio foi parafusado no análogo do implante e escaneado pelo Sistema Procera para gerar 20 pilares de zircônia. Depois, os implantes MKIII Brånemark foram presos num dispositivo de torque. Os pilares foram distribuídos em grupos seco e úmido com 10 amostras cada. No grupo úmido, as roscas internas dos implantes foram preenchidas com saliva artificial. Então, todos os pilares foram apertados com parafuso Torqtite a 32 Ncm. Dez medidas de destorque foram realizadas por grupo apertando-se o botão reverso do Torque Controller logo depois do parafusamento, e os valores foram registrados. As medias de destorque foram calculadas e comparadas pelo teste t de Student (?=0,05). Os valores médios obtidos nas condições seca e úmida foram 27,5 ± 1,5 Ncm e 31,7 ± 1,2 Ncm, respectivamente. Diferenças estatisticamente significantes foram observadas (p=0,0000024). Observou-se sempre existir uma perda do torque inicial quando o torque de remoção é mensurado em ambas as condições. A condição úmida demonstrou um valor médio maior de torque do que a condição seca. Valores melhores de pré-carga podem ser estabelecidos no grupo úmido, sugerindo que o parafuso do pilar deve ser lubrificado em saliva para evitar seu afrouxamento

The impact of healing time before loading on orthodontic mini-implant stability: a histomophometric study in minipigs

Objective: To evaluate healing time before loading, areas compression and tension and location of insertion on mini-implant stability. Design: Six minipigs were used. Each animal received 3 mini-implants in each quadrant: 1 mini-implant was used as an unloaded control (G1, n = 24); the other 2 were loaded with 150 g-force at three time intervals (G2: immediate loading, G3: after 15 days and G4: after 30 days), with 16 mini-implant in each experimental group. After 120 days, tissue blocks of the areas of interest were harvested. Clinical analysis (exact Fisher test) determined the survival rate. Histological analysis (Kontron KS 300TM, Zeiss) quantified the fractional bone-toimplant contact (%BIC) and bone area (%BA) at each healing time point, areas of interest, and insertion site (ANOVA and t tests for dependent and independent samples). Results: The mini-implant survival rates were G1: 71%, G2: 50%, G3: 75% and G4: 63%, with no statistical differences between them. The groups presented similar %BIC and %BA. There were no differences between the compression and tension sides or maxillary and mandibular insertion sites. Conclusions: These results suggest that low-intensity immediate or early orthodontic loading does not affect mini-implant stability, because similar histomorphometric results were observed for all the groups, with partial osseointegration of the mini-implants present.CAPE

RESISTÊNCIA À REMOÇÃO POR TRAÇÃO E INFILTRAÇÃO MARGINAL DE COROAS TOTAIS FUNDIDAS, CIMENTADAS EM DENTES NATURAIS RECONSTRUÍDOS COM IONÔMERO DE VIDRO

O objetivo deste estudo foi verificar a resistência à remoção por tração e a infiltração marginal de coroas totais fundidas cimentadas com cimento de ionômero de vidro, em dentes reconstruídos com duas formulações de cimento de ionômero de vidro, ou seja, Cermet e "mistura milagrosa", em comparação às coroas totais cimentadas em dentes com preparo para coroa total (sem reconstrução). Foram selecionados trinta molares superiores recém-extraídos, dez para cada condição experimental. Uma liga do sistema prata/estanho (M3) foi utilizada para obtenção das coroas totais. As amostras foram submetidas a ciclagens térmicas nas temperaturas de 5ºC, 37ºC e 55ºC, por sessenta minutos, durante sete dias. Para a última ciclagem térmica, foi utilizado o corante Rhodamina B a 0,1%, em solução aquosa. A seguir, as amostras foram lavadas e mantidas em condições ambientais por vinte e quatro horas, para serem levadas à máquina de ensaios universal, para os testes de remoção por tração axial. A análise de variância mostrou diferença estatisticamente significante, no nível de 5%, dos dentes sem reconstrução (controle), com relação aos dentes reconstruídos com "mistura milagrosa" e dentes reconstruídos com Cermet. Os dentes sem reconstrução apresentaram maior média aos testes de resistência por tração. Verificou-se, pela comparação individual entre as condições avaliadas, que o grupo reconstruído com "mistura milagrosa" e Cermet não mostrou diferença estatisticamente significante. Da mesma forma, foram elaboradas comparações individuais entre as condições avaliadas dos escores de infiltração, em que se pôde observar que houve significância entre os grupos de "mistura milagrosa" e Cermet com o grupo controle (dentes sem reconstrução). Os dentes reconstruídos com "mistura milagrosa" e Cermet não mostraram diferenças estatisticamente significantes entre si<br>The aim of this work was to measure tensile strength and microleakage of full cast crowns cemented on built-up cores using two formulations of glass-ionomer cement, Cermet and "miracle-mix", as compared to full cast crowns cemented exclusively on tooth structure. Thirty freshly extracted upper molars were selected, ten for each experimental condition. An alloy of the silver/tin system (M3) was employed to obtain the full crowns. The samples were thermocycled at 5ºC, 37ºC and 55ºC, for 60 minutes, during 7 days. For the last thermal cycle, 1% Rhodamine B aqueous solution dye was used. After that, the samples were washed and kept at room temperature for 24 hours, and taken to a universal testing machine for testing. The data were analyzed by parametric and non parametric statistical methods and the following conclusions were drawn: 1 - there was a statistically significant difference in removal resistance of cemented full crowns under the various conditions; 2 - the crowns cemented on the "miracle-mix" and Cermet reconstructed teeth showed statistically significant lower removal resistances than controls (teeth which had not been reconstructed); 3 - no statistically significant difference was found comparing teeth reconstructed either with "miracle-mix" or Cermet; 4 - no statistically significant differences were found between microleakage patterns in teeth rebuilt with the "miracle-mix" and with Cermet; 5 - statistically significant differences were found between microleakage patterns in teeth rebuilt with "miracle-mix" and Cermet cores as compared to the non reconstructed group (control