Antimicrobial activity of ProRoot MTA in contact with blood

Dental materials based on Portland cement, which is used in the construction industry have gained popularity for clinical use due to their hydraulic properties, the interaction with tooth tissue and their antimicrobial properties. The antimicrobial properties are optimal in vitro. However in clinical use contact with blood may affect the antimicrobial properties. This study aims to assess whether antimicrobial properties of the Portland cement-based dental cements such as mineral trioxide aggregate (MTA) are also affected by contact with blood present in clinical situations. ProRoot MTA, a Portland cement-based dental cement was characterized following contact with water, or heparinized blood after 1 day and 7 days aging. The antimicrobial activity under the mentioned conditions was assessed using 3 antimicrobial tests: agar diffusion test, direct contact test and intratubular infection test. MTA in contact with blood was severely discoloured, exhibited an additional phosphorus peak in elemental analysis, no calcium hydroxide peaks and no areas of bacterial inhibition growth in the agar diffusion test were demonstrated. ProRoot MTA showed limited antimicrobial activity, in both the direct contact test and intratubular infection test. When aged in water ProRoot MTA showed higher antimicrobial activity than when aged in blood. Antimicrobial activity reduced significantly after 7 days. Further assessment is required to investigate behaviour in clinical situations.ERDF (Malta) for the financing of the testing equipment through the project: “Developing an Interdisciplinary Material Testing and Rapid Prototyping R&D Facility” (Ref. no. 012)

In vitro analysis of the cytotoxicity and the antimicrobial effect of four endodontic sealers

<p>Abstract</p> <p>Introduction</p> <p>The aim of this study was to investigate <it>in vitro </it>the cytotoxicity and antibacterial properties of four different endodontic sealers using human periodontal ligament fibroblast cell proliferation and visual analysis of growth inhibition.</p> <p>Methods</p> <p>A silicone (GuttaFlow), silicate (EndoSequence BC), zinc oxide eugenol (Pulp Canal Sealer EWT) and epoxy resin (AH Plus Jet) based sealer were incubated with PDL fibroblasts (10⁴cells/ml, n = 6) up to 96 h. Cell proliferation (RFU) was determined by means of the Alamar Blue assay. Cell growth and morphology was visualized by means of fluorescent dyes. Possible antibacterial properties of the different sealers were visualized by means of SEM (<it>Enterococcus faecalis; Parvimonas micra</it>).</p> <p>Results</p> <p>Fibroblast proliferation depended on sealer and cultivation time. After 72 and 96 h GuttaFlow and EndoSequence BC showed relatively non-cytotoxic reactions, while Pulp Canal Sealer EWT and AH Plus Jet caused a significant decrease of cell proliferation (p < 0.001). Visualization of cell growth and morphology with various fluorescent dyes supplemented the results. No antibacterial effect of EndoSequence BC to <it>P. micra </it>was found, whereas GuttaFlow showed a weak, Pulp Canal Sealer EWT and AH Plus Jet extensive growth inhibition. Also, no antibacterial effect of GuttaFlow, EndoSequence BC or AH Plus Jet to <it>E. faecalis </it>could be detected.</p> <p>Conclusions</p> <p>These <it>in vitro </it>findings reveal that GuttaFlow and EndoSequence BC can be considered as biocompatible sealing materials. However, prior to their clinical employment, studies regarding their sealing properties also need to be considered.</p

Bond strength of different endodontic sealers to dentin: push-out test

OBJECTIVE: The aim of this in vitro study was to evaluate the bond strength of different root canal sealers to dentin. MATERIAL AND METHODS: Forty extracted single-rooted human teeth were examined and the coronal and middle thirds of the canals were prepared with a 1.50 mm post drill (FibreKor Post System, Pentron). The teeth were allocated in two experimental groups, irrigated with 2.5% NaOCl+17% EDTA or saline solution (control group) and instrumented using Race rotary files (FKG) to a size #40 at the working length. Then, the groups were divided into four subgroups and filled with Epiphany sealer (Group 1), EndoREZ (Group 2), AH26 (Group 3) and Grossman's Sealer (Group 4). After 2 weeks of storage in 100% humidity at 37ºC, all teeth were sectioned transversally into 2-mm-thick discs. Push-out tests were performed at a cross-head speed of 1 mm/min using a universal testing machine. The maximum load at failure was recorded and expressed in MPa. RESULTS: Means (±SD) in root canals irrigated with 2.5% NaOCl and 17% EDTA were: G1 (21.6±6.0), G2 (15.2±3.7), G3 (14.6±4.5) and G4 (11.7±4.1).Two-way ANOVA and Tukey's test showed the highest bond strength for the Epiphany's group (p< 0.01) when compared to the other tested sealers. Saline solution decreased the values of bond-strength (p<0.05) for all sealers. CONCLUSION: Epiphany sealer presented higher bond strength values to dentin in both irrigating protocols, and the use of 2.5% NaOCl and 17% EDTA increased the bond strength values for all sealers