460 research outputs found
Bioinspired electrohydrodynamic ceramic patterning of curved metallic substrates
Template-assisted electrohydrodynamic atomisation (TAEA) has been used for the first time to pattern curved metallic surfaces. Parallel lines of ceramic titania (TiO2) were produced on titanium substrates, convex and concave with diameters of ~25 mm, at the ambient temperature. Optimal results were obtained with 4 wt% TiO2 in ethanol suspension deposited over 300 s during stable cone-jetting at 20 µl/min, 10kV and collection distance 80 mm. A high degree of control over pattern line width, interline spacing and thickness were achieved. Nanoindentation load-displacement curves were continuous for the full loading and unloading cycle, indicating good adhesion between pattern and substrate. At a loading rate of 1 μN/s and a hold time of 1 s, pattern hardness decreased as load increased up to 7 μN and remained at 0·1 GPa up to higher loads. Elastic modulus behaved similarly, and both were not sensitive to loading rate. The effect of heat treatment to further consolidate the patterned deposits was also investigated. Hardness of the patterns was not markedly affected by heating. This work shows that TAEA is highly controllable and compatible on a range of substrate geometries. Extending TAEA capabilities from flat to curved surfaces, enabling the bioactive patterning of different surface geometries, takes this technology closer to orthopaedic engineering applications
Charge Transfer in Deoxyribonucleic Acid (DNA): Static Disorder, Dynamic Fluctuations and Complex Kinetic.
The fact that loosely bonded DNA bases could tolerate large structural fluctuations, form a dissipative environment for a charge traveling through the DNA. Nonlinear stochastic nature of structural fluctuations facilitates rich charge dynamics in DNA. We study the complex charge dynamics by solving a nonlinear, stochastic, coupled system of differential equations. Charge transfer between donor and acceptor in DNA occurs via different mechanisms depending on the distance between donor and acceptor. It changes from tunneling regime to a polaron assisted hopping regime depending on the donor-acceptor separation. Also we found that charge transport strongly depends on the feasibility of polaron formation. Hence it has complex dependence on temperature and charge-vibrations coupling strength. Mismatched base pairs, such as different conformations of the G・A mispair, cause only minor structural changes in the host DNA molecule, thereby making mispair recognition an arduous task. Electron transport in DNA that depends strongly on the hopping transfer integrals between the nearest base pairs, which in turn are affected by the presence of a mispair, might be an attractive approach in this regard. I report here on our investigations, via the I –V characteristics, of the effect of a mispair on the electrical properties of homogeneous and generic DNA molecules. The I –V characteristics of DNA were studied numerically within the double-stranded tight-binding model. The parameters of the tight-binding model, such as the transfer integrals and on-site energies, are determined from first-principles calculations. The changes in electrical current through the DNA chain due to the presence of a mispair depend on the conformation of the G・A mispair and are appreciable for DNA consisting of up to 90 base pairs. For homogeneous DNA sequences the current through DNA is suppressed and the strongest suppression is realized for the G(anti)・A(syn) conformation of the G・A mispair. For inhomogeneous (generic) DNA molecules, the mispair result can be either suppression or an enhancement of the current, depending on the type of mispairs and actual DNA sequence
Physio-chemical and antibacterial characteristics of pressure spun nylon nanofibres embedded with functional silver nanoparticles
© 2015 The Authors. Published by Elsevier B.V. This is an open access article under the CC BY license (http://creativecommons.org/licenses/by/4.0/). Date of Acceptance: 05/06/2015A novel and facile approach to prepare hybrid nanoparticle embedded polymer nanofibers using pressurised gyration is presented. Silver nanoparticles and nylon polymer were used in this work. The polymer solution's physical properties, rotating speed and the working pressure had a significant influence on the fibre diameter and the morphology. Fibres in the range of 60–500 nm were spun using 10 wt.%, 15 wt.% and 20 wt.% nylon solutions and these bead-free fibres were processed under 0.2 MPa and 0.3 MPa working pressure and a rotational speed of 36,000 rpm. 1–4 wt.% of Ag was added to these nylon solutions and in the case of wt.% fibres in the range 50–150 nm were prepared using the same conditions of pressurised gyration. Successful incorporation of the Ag nanoparticles in nylon nanofibres was confirmed by using a combination of advanced microscopical techniques and Raman spectrometry was used to study the bonding characteristics of nylon and the Ag nanoparticles. Inductively coupled plasma mass spectroscopy showed a substantial concentration of Ag ions in the nylon fibre matrix which is essential for producing effective antibacterial properties. Antibacterial activity of the Ag-loaded nanofibres shows higher efficacy than nylon nanofibres for Gram-negative Escherichia coli and Pseudomonas aeruginosa microorganisms, and both Ag nanoparticles and the Ag ions were found to be the reason for enhanced cell death in the bacterial solutionPeer reviewe
Evolution of self-generating porous microstructures in polyacrylonitrile-cellulose acetate blend fibres
Polyacrylonitrile (PAN), cellulose acetate (CA) and polyacrylonitrile - cellulose acetate (PAN-CA) fibres were formed in single and binary solvents which were subjected to gyration under pressure. Fibres in the diameter range 200–2000 nm were generated using a rotating speed of 36,000 rpm and a working pressure of 3 × 105 Pa. Long fibre morphologies with isotropic distribution of fibre orientation were obtained from PAN polymer solutions with a concentration of 5–15 wt%. Short fibre morphologies with anisotropic distribution of fibre orientation were produced for CA polymer solutions with a concentration of 25 wt% and below this concentration polygonal beads were generated. PAN-CA fibre bundles were generated and these showed remarkable self-generating porous characteristics when the working pressure was changed from 1 to 3 × 105 Pa. For comparison, porous PAN-CA fibres were also generated by solvent etching and porogen leaching techniques and in these the etching time and porogen concentration influenced the pore size of the generated fibres. Fourier transform infrared and Raman spectroscopies were performed to elucidate the bonding characteristics in the fibres. Release characteristics of the porous fibrous structures were studied using vanillin as the active ingredient. A mathematical model which allows the evaluation of the fibre diameter as a function of rotating speed and working pressure is presented and this helps to understand the solvent mass transfer taking place during fibre forming
Beads, beaded-fibres and fibres: Tailoring the morphology of poly(caprolactone) using pressurised gyration
This work focuses on forming bead on string poly(caprolactone) (PCL) by using gyration under pressure. The fibre morphology of bead on string is an interesting feature that falls between bead-free fibres and droplets, and it could be effectively controlled by the rheological properties of spinning dopes and the major processing parameters of the pressurised gyration system which are working pressure and rotating speed. Bead products were not always spherical in shape and tended to be more elliptical, therefore both their width and length were measured. The average bead width and length produced spanned a range 145-660μm and 140-1060μm, respectively. The average distance between two adjacent beads (i.e. inter-bead distance) and the bead size (width and length) are shown to be a function of processing parameters and polymer concentration. An interesting morphology i.e. beads with short fibre was observed when using a high polymer concentration. Bead on string structure agglomeration was promoted by a low polymer concentration. Formation of droplets or agglomerated bead on string is promoted below 5wt% polymer concentration, and beads with short fibre were present in the microstructure beyond a polymer concentration of 20wt%
Simultaneous Application of Pressure-Infusion-Gyration to Generate Polymeric Nanofibers
Polymeric nanofibers are a fascinating class of material that has been widely used in a myriad of applications, including fiber reinforced composites, protective clothing, and chemical sensors. Here, the science of the combined application of external pressure, controlled infusion of polymer solution and gyration, which allows mass production of uniform polymeric nanofibers in a single step, is uncovered. Using poly(ethylene oxide) as an example this study shows the use of this novel method to fabricate polymeric nanofibers and nanofibrous mats under different combinations of processing parameters such as working pressure (1 × 105 to 3 × 105 Pa), rotational speed (10 000–36 000 rpm), infusion rate (500–5000 µL min−1), and fiber collection distance (4–15 cm). The morphologies of the nanofibers are characterized using scanning electron microscopy and anisotropy of alignment of fiber is studied using 2D fast Fourier transform analysis. A correlation between the product morphology and the processing parameters is established. The produced fibers are in a range of 50–850 nm at an orifice-to-collector distance of 10 cm. The results indicate that the pressure coupled infusion gyration (PCIG) offers a facile way for forming nanofibers and nanofiber assemblies
Latest developments in innovative manufacturing to combine nanotechnology with healthcare
Nanotechnology has become increasingly important in advancing the frontiers of many key areas of healthcare, for example, drug delivery and tissue engineering. To fully harness the many benefits of nanotechnology in healthcare, innovative manufacturing is necessary to mass produce nanoparticles and nanofibers, the two major types of nanofeatures currently sought after and of immense utilitarian value in healthcare. For example, nanoparticles are a key drug delivery enabler, the structural and mechanical mimicry are important attributes of nanofiber which are increasingly used as biomimetic agents
A Global Challenge: Sustainability of Submicrometer PEO and PVP Fiber Production
The field of submicrometer polymeric production currently has a predominant research focus on morphology and application. In comparison, the sustainability of the manufacture of submicrometer polymeric fibers, specifically the energy efficiency, is less explored. The principles of Green Chemistry and Green Engineering outline frameworks for the manufacture of “greener” products, where the most significant principles in the two frameworks are shown to be centered on energy efficiency, material wastage, and the use of non-hazardous materials. This study examines the power consumption during the production of Polyethylene oxide (PEO) and Polyvinylpyrrolidone (PVP) submicrometer fibers under magnitudes of the key forming parameters to generate fibers via pressure spinning. The energy consumption, along with the fiber diameter, and production rate during the manufacture of fibers is predominantly attributed to the characteristics of polymeric solutions utilized
Graphene-Based Nanocomposites as Antibacterial, Antiviral and Antifungal Agents
Over the past decade, there have been many interesting studies in the scientific literature about the interaction of graphene-based polymeric nanocomposites with microorganisms to tackle antimicrobial resistance. These studies have reported variable intensities of biocompatibility and selectivity for the nanocomposites toward a specific strain, but it is widely believed that graphene nanocomposites have antibacterial, antiviral, and antifungal activities. Such antibacterial activity is due to several mechanisms by which graphene nanocomposites can act on cells including stimulating oxidative stress; disrupting membranes due to sharp edges; greatly changing core structure mechanical strength and coarseness. However, the underlying mechanisms of graphene nanocomposites as antiviral and antifungal agents remain relatively scarce. In this review, recent advances in the synthesis, functional tailoring, and antibacterial, antiviral, and antifungal applications of graphene nanocomposites are summarized. The synthesis of graphene materials and graphene-based polymeric nanocomposites with techniques such as pressurized gyration, electrospinning, chemical vapor deposition, and layer-by-layer self-assembly is first introduced. Then, the antimicrobial mechanisms of graphene membranes are presented and demonstrated typical in vitro and in vivo studies on the use of graphene nanocomposites for antibacterial, antiviral, and antifungal applications. Finally, the review describes the biosafety, current limitations, and potential of antimicrobial graphene-based nanocomposites
Current methodologies and approaches for the formation of core–sheath polymer fibers for biomedical applications
The application of polymer fibers has rocketed to unimaginable heights in recent years and occupies every corner of our day-to-day life, from knitted protective textile clothes to buzzing smartphone electronics. Polymer fibers could be obtained from natural and synthetic polymers at a length scale from the nanometer to micrometer range. These fibers could be formed into different configurations such as single, core–sheath, hollow, blended, or composite according to human needs. Of these several conformations of fibers, core–sheath polymer fibers are an interesting class of materials, which shows superior physical, chemical, and biological properties. In core–sheath fiber structures, one of the components called a core is fully surrounded by the second component known as a sheath. In this format, different polymers can be applied as a sheath over a solid core of another polymer, thus resulting in a variety of modified properties while maintaining the major fiber property. After a brief introduction to core–sheath fibers, this review paper focuses on the development of the electrospinning process to manufacture core–sheath fibers followed by illustrating the current methodology and approaches to form them on a larger scale, suitable for industrial manufacturing and exploitation. Finally, the paper reviews the applications of the core–sheath fibers, in particular, recent studies of core–sheath polymer fibers in tissue engineering (nerve, vascular grafts, cardiomyocytes, bone, tendons, sutures, and wound healing), growth factors and other bioactive component release, and drug delivery. Therefore, core–sheath structures are a revolutionary development in the field of science and technology, becoming a backbone to many emerging technologies and novel opportunities
- …