On Thermal Conductivity of Anisotropic Nanodiamond
Dependence of thermal conductivity of nanocrystalline diamond coating on grain size and form is
theoretically investigated. Nanodiamond is considered as two-phase material composed of dielectric
diamond grains characterizing by three main dimensions and segregated by thin graphite layers with
electron or phonon thermal conductivity. Influence of thermal conductance type and thickness of boundary
layer on nanodiamond thermal conductivity is analysed. Derived dependences of thermal conductivity on
grain dimensions are compared with experimental data.
When you are citing the document, use the following link http://essuir.sumdu.edu.ua/handle/123456789/3519
Model of thermal conductivity of anisotropic nanodiamond
Dependence of thermal conductivity of nanocrystalline diamond on grain size and shape is theoretically
investigated. Nanodiamond is considered as two-phase material composed of diamond grains characterizing by three
main dimensions and segregated by thin graphite layers with electron, phonon or hybrid thermal conductivity.
Influence of type of thermal conductance and thickness of boundary layer on thermal conductivity of nanodiamond
is analyzed. Derived dependences of thermal conductivity on grain dimensions are compared with experimental
data.Теоретически исследуется зависимость теплопроводности нанокристаллического алмаза от величины и
формы кристаллита. Наноалмаз рассматривается как двухфазный материал, состоящий из алмазных зерен,
характеризующихся тремя главными размерами и разделенных тонкими графитовыми слоями с
электронной, фононной или смешанной теплопроводностью. Анализируется влияние типа
теплопроводности пограничного слоя и его толщины на теплопроводность наноалмаза. Полученные
зависимости теплопроводности наноалмаза от размеров зерна сравниваются с имеющимися
экспериментальными данными.Теоретично досліджується залежність теплопровідності нанокристалічного алмазу від величини й форми
кристаліту. Наноалмаз розглядається як двофазний матеріал, що складається з алмазних зерен, що
характеризуються трьома головними розмірами, та розділених тонкими графітовими прошарками з
електронною, фононною або змішаною теплопровідністю. Аналізується вплив типу теплопровідності
прикордонного шару і його товщини на теплопровідність наноалмазу. Отримані залежності
теплопровідності наноалмазу від розмірів зерна порівнюються з наявними експериментальними даними
The Effect of Gas Phase Composition on the Structural Characteristics and Resistivity of Nitrogen-doped Nanostructured Diamond Coatings
The experimental results of the effect of the gas phase composition on nitrogen-doped nanostructured
diamond coatings synthesized in the glow discharge plasma on their structure and resistance have been
presented. It was shown that changes in the electrical conductivity of the nitrogen doped nanostructured
diamond coatings are primarily related to changes in the electrical conductivity of the grain boundaries
and did not to changes in the grain size of the diamond phase.
When you are citing the document, use the following link http://essuir.sumdu.edu.ua/handle/123456789/3518
Registration of high-intensity electron and x-ray fields with polycrystalline CVD diamond detectors
N/
Surface morphology and structure of nanocrystalline diamond films deposited in CH₄/H₂/Ar glow discharge plasma
Diamond films of up to 12 μm thickness have been deposited onto single crystal silicon substrates by CVD method in CH₄/H₂/Ar glow discharge plasma stabilized by magnetic field. X-ray diffraction analysis and atomic force microscopy have shown the films consist of about 1 μm in diameter conglomerates of 30-40 nm average size diamond nanocrystals. The conglomerate size increases by a factor of 2 as the film thickness grows from 1.7 up to 11.7 μm. At the same time, the nanocrystallite size remains essentially unchanged. In the diamond films, texture, compressive residual stresses and high concentration of crystal structure defects have been revealed.Алмазні плівки товщиною до 12 мкм отримано на підкладках з монокристалічного кремнію методом газофазного осадження у CH₄/H₂/Ar плазмі тліючого розряду, стабілізованого магнітним полем. Методами рентгеноструктурного аналізу та атомно-силової мікроскопії встановлено, що плівки складаються з конгломератів діаметром - 1 мкм, утворених нанокристалами алмазу із середнім розміром 30-40 нм. 3 ростом товщини плівки від 1,7 до 11,7 мкм розмір конгломератів збільшується у 2 рази. При цьому розмір нанокристалів практично не змінюється. У плівках виявлено текстуру, залишкові напруження стиску та високий вміст дефектів кристалічної структури.Алмазные пленки толщиной до 12 мкм получены на подложках из монокристаллического кремния методом газофазного осаждения в CH₄/H₂/Ar плазме тлеющего разряда, стабилизированного магнитным полем. Методами рентгеноструктурного анализа и атомно-силовой микроскопии установлено, что пленки состоят из конгломератов диаметром -1 мкм, образованных нанокристаллами алмаза со средним размером 30-40 нм. С ростом толщины rтенки от 1,7 до 11,7 мкм размер конгломератов увеличивается в 2 раза. При этом размер нанокристаллов практически не меняется. В пленках выявлены текстура, остаточные напряжения сжатия и высокое содержание дефектов кристаллического строения