7 research outputs found
Matériaux composites Aluminium/Carbone : architecture spécifique et propriétés thermiques adaptatives
Many carbon/metal composites are currently used in several applications. One of them concerns their use as heat sinks in microelectronics. Concerning this application, two conditions are required: a high thermal conductivity (TC) in order to evacuate the heat generated by the electronic chip and a coefficient of thermal expansion (CTE) similar to the used material type of the electronic device (2-8×10-6 /K).Therefore, graphite flakes (GF; TC: 1000 W/m.K and CTE: -1×10-6 /K in the graphite plane) reinforced aluminum matrix (Al; TC: 217 W/m.K and CTE: 25×10-6 /K) composites were fabricated. These composite materials were fabricated by Powder Metallurgy (PM) and Flake Powder Metallurgy (FPM). This process, which consist to use a flattened metallic powder, helped to improve the in-plane orientation (perpendicular to the pressure direction) of GF under uniaxial pressure. Moreover, this process provided a better Al-C interface thanks to a planar contact between the matrix and the reinforcements. This resulted in an improvement of the CT from 400 W/m.K to 450 W/m.K for a reinforcement content of 50 vol.%. Nevertheless, regarding thermal dilation, CTEs of 21.8×10-6 /K and 21.7×10-6 /K were obtained by MP and FPM respectively, which is incompatible with the intended application.To overcome this problem, composite materials with multiple reinforcement were developed by solid-liquid phase sintering. Then, carbon fibers (CF) have been added to aluminum and graphite flakes. The addition of CF to GF reinforcement reduced significantly the CTE of the Al/(GF+CF) composites with a small proportion of CF, while preserving a high TC. In addition, the Al/(GF+FC) composite materials have significantly lower CTEs than the Al/CF composites with a equivalent vol.% of CF. Therefore, Al/(GF+CF) composite materials were developed by solid-liquid phase sintering to obtain a TC of 400 W/m.K (comparable to the TC of copper) and a CTE of 8×10-6 /K (comparable to the CTE of alumina). In addition, the lightweight of aluminum gives composite materials Al/C a low density (d = 2.4 g/cm3). Therefore, the composite materials developed in this study are promising as a lightweight heat sink in microelectronic industries.Les matériaux composites à matrice métallique (CMM) sont actuellement étudiés pour être utilisés dans de nombreux domaines d’application. L’une des applications potentielles concerne leur utilisation en tant que drain thermique pour les modules de puissance. Pour cette application, deux conditions sont requises : une conductivité thermique (CT) élevée pour évacuer la chaleur générée par la puce électronique et un coefficient d’expansion thermique (CTE) proche du substrat céramique (2-8×10-6 /K) utilisé dans le module de puissance.Ainsi des matériaux composites à matrice aluminium (Al : CT de 217 W/m.K et CTE de 24×10-6 /K) et à renfort plaquette de graphite (GF : CT de 1000 W/m.K et CTE de -1×10-6 /K dans le plan de la plaquette) ont été élaborés. Ces matériaux composites ont été fabriqués par Métallurgie des Poudres (MP) conventionnelle mais aussi par un procédé original nommé Flake Powder Metallurgy (FPM). Ce procédé, qui consiste à utiliser une poudre métallique à morphologie plaquette, a permis d’optimiser l’orientation des renforts plaquette dans un plan perpendiculaire à la direction de densification sous l’action d’une pression uniaxiale. De plus, ce procédé a permis d’obtenir une meilleure adhésion entre la matrice et le renfort comparé aux matériaux composites élaborés par MP conventionnelle. Cela a abouti à une amélioration de la CT qui est passée de 400 W/m.K à 450 W/m.K pour un taux de renfort de 50%vol. Néanmoins, concernant la dilatation thermique, des CTE de 21,8×10-6 /K et 21,7×10-6 /K ont été obtenus par MP et FPM respectivement, ce qui est incompatible avec l’application visée.Pour surmonter cette problématique, des matériaux composites à renfort multiple ont été élaborés par frittage en phase liquide. Ainsi des fibres de carbone (FC) ont été rajoutées à l’aluminium et aux plaquettes de graphite. L’ajout de ce second renfort au graphite a permis de diminuer de manière importante le CTE des composites Al/(GF+FC) avec une faible proportion en FC tout en maintenant une haute CT. De plus les matériaux composites Al/(GF+FC) présentent des CTE nettement inférieurs aux composites Al/FC avec un %vol. de FC équivalent. Ainsi des matériaux composites Al/(GF+FC) ont été élaborés par frittage en phase liquide permettant d’obtenir une CT de 400 W/m.K (comparable à la CT du cuivre) et un CTE de 8×10-6 /K (comparable au CTE de l’alumine). De plus la légèreté de l’aluminium confère aux matériaux composites Al/C une faible densité (d=2,4). Par conséquent, les matériaux développés dans cette étude sont prometteur en tant que drain thermique léger, notamment dans le domaine de l’électronique embarquée
Development of bulk MMC materials with specific architectures and thermal properties
Les matériaux composites à matrice métallique (CMM) sont actuellement étudiés pour être utilisés dans de nombreux domaines d’application. L’une des applications potentielles concerne leur utilisation en tant que drain thermique pour les modules de puissance. Pour cette application, deux conditions sont requises : une conductivité thermique (CT) élevée pour évacuer la chaleur générée par la puce électronique et un coefficient d’expansion thermique (CTE) proche du substrat céramique (2-8×10-6 /K) utilisé dans le module de puissance.Ainsi des matériaux composites à matrice aluminium (Al : CT de 217 W/m.K et CTE de 24×10-6 /K) et à renfort plaquette de graphite (GF : CT de 1000 W/m.K et CTE de -1×10-6 /K dans le plan de la plaquette) ont été élaborés. Ces matériaux composites ont été fabriqués par Métallurgie des Poudres (MP) conventionnelle mais aussi par un procédé original nommé Flake Powder Metallurgy (FPM). Ce procédé, qui consiste à utiliser une poudre métallique à morphologie plaquette, a permis d’optimiser l’orientation des renforts plaquette dans un plan perpendiculaire à la direction de densification sous l’action d’une pression uniaxiale. De plus, ce procédé a permis d’obtenir une meilleure adhésion entre la matrice et le renfort comparé aux matériaux composites élaborés par MP conventionnelle. Cela a abouti à une amélioration de la CT qui est passée de 400 W/m.K à 450 W/m.K pour un taux de renfort de 50%vol. Néanmoins, concernant la dilatation thermique, des CTE de 21,8×10-6 /K et 21,7×10-6 /K ont été obtenus par MP et FPM respectivement, ce qui est incompatible avec l’application visée.Pour surmonter cette problématique, des matériaux composites à renfort multiple ont été élaborés par frittage en phase liquide. Ainsi des fibres de carbone (FC) ont été rajoutées à l’aluminium et aux plaquettes de graphite. L’ajout de ce second renfort au graphite a permis de diminuer de manière importante le CTE des composites Al/(GF+FC) avec une faible proportion en FC tout en maintenant une haute CT. De plus les matériaux composites Al/(GF+FC) présentent des CTE nettement inférieurs aux composites Al/FC avec un %vol. de FC équivalent. Ainsi des matériaux composites Al/(GF+FC) ont été élaborés par frittage en phase liquide permettant d’obtenir une CT de 400 W/m.K (comparable à la CT du cuivre) et un CTE de 8×10-6 /K (comparable au CTE de l’alumine). De plus la légèreté de l’aluminium confère aux matériaux composites Al/C une faible densité (d=2,4). Par conséquent, les matériaux développés dans cette étude sont prometteur en tant que drain thermique léger, notamment dans le domaine de l’électronique embarquée.Many carbon/metal composites are currently used in several applications. One of them concerns their use as heat sinks in microelectronics. Concerning this application, two conditions are required: a high thermal conductivity (TC) in order to evacuate the heat generated by the electronic chip and a coefficient of thermal expansion (CTE) similar to the used material type of the electronic device (2-8×10-6 /K).Therefore, graphite flakes (GF; TC: 1000 W/m.K and CTE: -1×10-6 /K in the graphite plane) reinforced aluminum matrix (Al; TC: 217 W/m.K and CTE: 25×10-6 /K) composites were fabricated. These composite materials were fabricated by Powder Metallurgy (PM) and Flake Powder Metallurgy (FPM). This process, which consist to use a flattened metallic powder, helped to improve the in-plane orientation (perpendicular to the pressure direction) of GF under uniaxial pressure. Moreover, this process provided a better Al-C interface thanks to a planar contact between the matrix and the reinforcements. This resulted in an improvement of the CT from 400 W/m.K to 450 W/m.K for a reinforcement content of 50 vol.%. Nevertheless, regarding thermal dilation, CTEs of 21.8×10-6 /K and 21.7×10-6 /K were obtained by MP and FPM respectively, which is incompatible with the intended application.To overcome this problem, composite materials with multiple reinforcement were developed by solid-liquid phase sintering. Then, carbon fibers (CF) have been added to aluminum and graphite flakes. The addition of CF to GF reinforcement reduced significantly the CTE of the Al/(GF+CF) composites with a small proportion of CF, while preserving a high TC. In addition, the Al/(GF+FC) composite materials have significantly lower CTEs than the Al/CF composites with a equivalent vol.% of CF. Therefore, Al/(GF+CF) composite materials were developed by solid-liquid phase sintering to obtain a TC of 400 W/m.K (comparable to the TC of copper) and a CTE of 8×10-6 /K (comparable to the CTE of alumina). In addition, the lightweight of aluminum gives composite materials Al/C a low density (d = 2.4 g/cm3). Therefore, the composite materials developed in this study are promising as a lightweight heat sink in microelectronic industries
Development of bulk MMC materials with specific architectures and thermal properties
Les matériaux composites à matrice métallique (CMM) sont actuellement étudiés pour être utilisés dans de nombreux domaines d’application. L’une des applications potentielles concerne leur utilisation en tant que drain thermique pour les modules de puissance. Pour cette application, deux conditions sont requises : une conductivité thermique (CT) élevée pour évacuer la chaleur générée par la puce électronique et un coefficient d’expansion thermique (CTE) proche du substrat céramique (2-8×10-6 /K) utilisé dans le module de puissance.Ainsi des matériaux composites à matrice aluminium (Al : CT de 217 W/m.K et CTE de 24×10-6 /K) et à renfort plaquette de graphite (GF : CT de 1000 W/m.K et CTE de -1×10-6 /K dans le plan de la plaquette) ont été élaborés. Ces matériaux composites ont été fabriqués par Métallurgie des Poudres (MP) conventionnelle mais aussi par un procédé original nommé Flake Powder Metallurgy (FPM). Ce procédé, qui consiste à utiliser une poudre métallique à morphologie plaquette, a permis d’optimiser l’orientation des renforts plaquette dans un plan perpendiculaire à la direction de densification sous l’action d’une pression uniaxiale. De plus, ce procédé a permis d’obtenir une meilleure adhésion entre la matrice et le renfort comparé aux matériaux composites élaborés par MP conventionnelle. Cela a abouti à une amélioration de la CT qui est passée de 400 W/m.K à 450 W/m.K pour un taux de renfort de 50%vol. Néanmoins, concernant la dilatation thermique, des CTE de 21,8×10-6 /K et 21,7×10-6 /K ont été obtenus par MP et FPM respectivement, ce qui est incompatible avec l’application visée.Pour surmonter cette problématique, des matériaux composites à renfort multiple ont été élaborés par frittage en phase liquide. Ainsi des fibres de carbone (FC) ont été rajoutées à l’aluminium et aux plaquettes de graphite. L’ajout de ce second renfort au graphite a permis de diminuer de manière importante le CTE des composites Al/(GF+FC) avec une faible proportion en FC tout en maintenant une haute CT. De plus les matériaux composites Al/(GF+FC) présentent des CTE nettement inférieurs aux composites Al/FC avec un %vol. de FC équivalent. Ainsi des matériaux composites Al/(GF+FC) ont été élaborés par frittage en phase liquide permettant d’obtenir une CT de 400 W/m.K (comparable à la CT du cuivre) et un CTE de 8×10-6 /K (comparable au CTE de l’alumine). De plus la légèreté de l’aluminium confère aux matériaux composites Al/C une faible densité (d=2,4). Par conséquent, les matériaux développés dans cette étude sont prometteur en tant que drain thermique léger, notamment dans le domaine de l’électronique embarquée.Many carbon/metal composites are currently used in several applications. One of them concerns their use as heat sinks in microelectronics. Concerning this application, two conditions are required: a high thermal conductivity (TC) in order to evacuate the heat generated by the electronic chip and a coefficient of thermal expansion (CTE) similar to the used material type of the electronic device (2-8×10-6 /K).Therefore, graphite flakes (GF; TC: 1000 W/m.K and CTE: -1×10-6 /K in the graphite plane) reinforced aluminum matrix (Al; TC: 217 W/m.K and CTE: 25×10-6 /K) composites were fabricated. These composite materials were fabricated by Powder Metallurgy (PM) and Flake Powder Metallurgy (FPM). This process, which consist to use a flattened metallic powder, helped to improve the in-plane orientation (perpendicular to the pressure direction) of GF under uniaxial pressure. Moreover, this process provided a better Al-C interface thanks to a planar contact between the matrix and the reinforcements. This resulted in an improvement of the CT from 400 W/m.K to 450 W/m.K for a reinforcement content of 50 vol.%. Nevertheless, regarding thermal dilation, CTEs of 21.8×10-6 /K and 21.7×10-6 /K were obtained by MP and FPM respectively, which is incompatible with the intended application.To overcome this problem, composite materials with multiple reinforcement were developed by solid-liquid phase sintering. Then, carbon fibers (CF) have been added to aluminum and graphite flakes. The addition of CF to GF reinforcement reduced significantly the CTE of the Al/(GF+CF) composites with a small proportion of CF, while preserving a high TC. In addition, the Al/(GF+FC) composite materials have significantly lower CTEs than the Al/CF composites with a equivalent vol.% of CF. Therefore, Al/(GF+CF) composite materials were developed by solid-liquid phase sintering to obtain a TC of 400 W/m.K (comparable to the TC of copper) and a CTE of 8×10-6 /K (comparable to the CTE of alumina). In addition, the lightweight of aluminum gives composite materials Al/C a low density (d = 2.4 g/cm3). Therefore, the composite materials developed in this study are promising as a lightweight heat sink in microelectronic industries
Synergetic Effect of Discontinuous Carbon Fibers and Graphite Flakes on Thermo-Mechanical Properties of Aluminum Matrix Composites Fabricated by Solid–Liquid Phase Sintering
Aluminum (Al) matrix composite materials reinforced with graphite flakes (GF) and pitch-based carbon fibers (CF) were fabricated by solid–liquid phase sintering with a small amount of Aluminum–Silicon eutectic alloy (Al-12 wt%Si). The amount of Al–Si is optimized for a carbon content of 50 vol% in order to achieve, in the plane of GF reinforcement, a higher thermal conductivity (TC) and a lower coefficient of thermal expansion (CTE) compared to identical composite material fabricated by conventional powder metallurgy route. Al/(GF + CF) composite materials were characterized by scanning electron microscopy (SEM), energy-dispersive X-ray microscopy and X-ray tomography in order to highlight the distribution of the Al–Si liquid phase and the formation of a carbon network in the aluminum matrix. A small amount of CF allows to control the through-plane CTE without affecting significantly the in-plane TC of the Al-C composites. The (GF + CF) mixture and the solid–liquid phase sintering allow to achieve a TC of 410 W/m K (in-plane direction) and a CTE of 2.4 × 10−6/K (trough-plane direction), which is, for example, applicable for lightweight heat sink material
Effect of flake powder metallurgy on thermal conductivity of graphite flakes reinforced aluminum matrix composites
The optimization of metal–matrix composite material is linked firstly with the intrinsic properties of the matrix and the reinforcement used and secondly with the reinforcement–matrix interfacial zone and the distribution/orientation of the reinforcement inside the metal–matrix. Flake powder metallurgy was used to fabricate graphite flake reinforced aluminum matrix (Al/GF) composites fabricated by vacuum hot pressing. Two types of aluminum powders morphology were used: spherical (AlS) and flake (AlF) powders. A higher thermal conductivity in the in-plane direction of the graphite flakes was obtained for Al/GF composite materials fabricated with aluminum flake powder. In addition to a better orientation of the GF in the flake aluminum matrix, a 3D puckered surface and plane surface are formed at the Al/GF interface in, respectively, AlS/GF and AlF/GF composite materials. Due to the morphology incompatibility between the graphite flakes and the spherical powder, the damaged inner structure of GF contributes to a limited enhancement of thermal conductivity in AlS/GF composite materials