Semirigid Ligands Enhance Different Coordination Behavior of Nd and Dy Relevant to Their Separation and Recovery in a Non-aqueous Environment

Rare-earth elements are widely used in high-end technologies, the production of permanent magnets (PMs) being one of the sectors with the greatest current demand and likely greater future demand. The combination of Nd and Dy in NdFeB PMs enhances their magnetic properties but makes their recycling more challenging. Due to the similar chemical properties of Nd and Dy, their separation is expensive and currently limited to the small scale. It is therefore crucially important to devise efficient and selective methods that can recover and then reuse those critical metals. To address these issues, a series of heptadentate Trensal-based ligands were used for the complexation of Dy3+ and Nd3+ ions, with the goal of indicating the role of coordination and solubility equilibria in the selective precipitation of Ln3+-metal complexes from multimetal non-water solutions. Specifically, for a 1:1 Nd/Dy mixture, a selective and fast precipitation of the Dy complex occurred in acetone with the Trensalp-OMe ligand at room temperature, with a concomitant enrichment of Nd in the solution phase. In acetone, complexes of Nd and Dy with Trensalp-OMe were characterized by very similar formation constants of 7.0(2) and 7.3(2), respectively. From the structural analysis of an array of Dy and Nd complexes with TrensalR ligands, we showed that Dy invariably provided complexes with coordination number (cn) of 7, whereas the larger Nd experienced an expansion of the coordination sphere by recruiting additional solvent molecules and giving a cn of >7. The significant structural differences have been identified as the main premises upon which a suitable separation strategy can be devised with these kind of ligands, as well as other preorganized polydentate ligands that can exploit the small differences in Ln3+ coordination requirements

Phosphine Oxide Porous Organic Polymers Incorporating Cobalt(II) Ions: Synthesis, Characterization, and Investigation of H-2 Production

International audienceSuitably functionalized porous matrices represent versatile platforms to support well-dispersed catalytic centers. In the present study, porous organic polymers (POPs) containing phosphine oxide groups were fabricated to bind transition metals and to be investigated for potential electrocatalytic applications. Cross-linking of mono- and di-phosphine monomers with multiple phenyl substituents was subject to the Friedel-Crafts (F-C) reaction and the oxidation process, which generated phosphine oxide porous polymers with pore capacity up to 0.92 cm(3)/g and a surface area of about 990 m(2)/g. The formation of the R3P center dot BH3 borohydride adduct during synthesis allows to extend the library of phosphine-based monomeric entities when using FeCl3. The porous polymers were loaded with 0.8-4.2 w/w % of cobalt(II) and behaved as hydrogen evolution reaction (HER) catalysts with a Faradaic efficiency of up to 95% (5.81 x 10(-5) mol H-2 per 11.76 C) and a stable current density during repeated controlled potential experiments (CPE), even though with high overpotentials (0.53-0.68 V to reach a current density of 1 mA.cm(-2)). These studies open the way to the effectiveness of tailored phosphine oxide POPs produced through an inexpensive and ecofriendly iron-based catalyst and for the insertion of transition metals in a porous architecture, enabling electrochemically driven activation of small molecules

Poly[(μ4-phenylphosphonato)zinc(II)]

The title two-dimensional coordination polymer, [Zn(C6H5PO3)]n, was synthesized serendipitously by reacting a tetraphosphonate cavitand Tiiii[C3H7, CH3, C6H5] and Zn(CH3COO)22H2O in a DMF/H2O mixture. The basic conditions of the reaction cleaved the phosphonate bridges at the upper rim of the cavitand, making them available for reaction with the zinc ions. The coordination polymer can be described as an inorganic layer in which zinc coordinates the oxygen atoms of the phosphonate groups in a distorted tetrahedral environment, while the phenyl groups, which are statistically disordered over two orientations, point up and down with respect to the layer. The layers interact through van der Waals interactions. The crystal studied was refined as a two-component twin