6 research outputs found
Evaluation of the Properties of PHB Composite Filled with Kaolin Particles for 3D Printing Applications Using the Design of Experiment
In the presented work, poly(3-hydroxybutyrate)-PHB-based composites for 3D printing as bio-sourced and biodegradable alternatives to synthetic plastics are characterized. The PHB matrix was modified by polylactide (PLA) and plasticized by tributyl citrate. Kaolin particles were used as a filler. The mathematical method “Design of Experiment” (DoE) was used to create a matrix of samples for further evaluation. Firstly, the optimal printing temperature of the first and upper layers was determined. Secondly, the 3D printed samples were tested with regards to the warping during the 3D printing. Testing specimens were prepared using the determined optimal printing conditions to measure the tensile properties, impact strength, and heat deflection temperature (HDT) of the samples. The results describe the effect of adding individual components (PHB, PLA, plasticizer, and filler) in the prepared composite sample on the resulting material properties. Two composite samples were prepared based on the theoretical results of DoE (one with the maximum printability and one with the maximum HDT) to compare them with the real data measured. The tests of these two composite samples showed 25% lower warping and 8.9% higher HDT than was expected by the theory
Effect of Selected Commercial Plasticizers on Mechanical, Thermal, and Morphological Properties of Poly(3-hydroxybutyrate)/ Poly(lactic acid)/Plasticizer Biodegradable Blends for Three-Dimensional (3D) Print
This paper explores the influence of selected commercial plasticizers structure, which are based on esters of citric acid, on mechanical and thermal properties of Poly(3-hydroxybutyrate)/Poly(lactic acid)/Plasticizer biodegradable blends. These plasticizers were first tested with respect to their miscibility with Poly(3-hydroxybutyrate)/Poly(lactic acid) (PHB/PLA) blends using a kneading machine. PHB/PLA/plasticizer blends in the weight ratio (wt %) of 60/25/15 were then prepared by single screw and corotating meshing twin screw extruders in the form of filament for further three-dimensional (3D) printing. Mechanical, thermal properties, and shape stability (warping effect) of 3D printed products can be improved just by the addition of appropriate plasticizer to polymeric blend. The goal was to create new types of eco-friendly PHB/PLA/plasticizers blends and to highly improve the poor mechanical properties of neat PHB/PLA blends (with majority of PHB) by adding appropriate plasticizer. Mechanical properties of plasticized blends were then determined by the tensile test of 3D printed test samples (dogbones), as well as filaments. Measured elongation at break rapidly enhanced from 21% for neat non-plasticized PHB/PLA blends (reference) to 328% for best plasticized blends in the form of filament, and from 5% (reference) to 187% for plasticized blends in the form of printed dogbones. The plasticizing effect on blends was confirmed by Modulated Differential Scanning Calorimetry. The study of morphology was performed by the Scanning Electron Microscopy. Significant problem of plasticized blends used to be also plasticizer migration, therefore the diffusion of plasticizers from the blends after 15 days of exposition to 110 degrees C in the drying oven was investigated as their measured weight loss. Almost all of the used plasticizers showed meaningful positive softening effects, but the diffusion of plasticizers at 110 degrees C exposition was quite extensive. The determination of the degree of disintegration of selected plasticized blend when exposed to a laboratory-scale composting environment was executed to roughly check the biodegradability
Changes of physical properties of PLA-based blends during early stage of biodegradation in compost
Three biodegradable plastics materials, namely pure poly(L-lactide) (PLA), PLA with plasticizer triacetine (TAC) and the mixture PLA/polyhydroxybutyrate (PHB) and TAC were investigated concerning changes of physical properties due to biodegradation in compost at 58 °C up to 16 days. With rising time of degradation in compost, both number and weight molecular masses were decreasing progressively, but only marginal change of the polydispersity index was observed which indicates that biodegradation is not random process. FTIR spectroscopy revealed that in spite of the extensive decrease of molecular weight, no substantial change in chemical composition was found. The most significant modification of the spectra consisted in an appearing of the broad band in region 3100–3300 cm−1, which was assigned to a formation of biofilm on the sample surfaces. This effect appeared for all three materials, however, it was much more pronounced for samples containing also triacetine. Measurement of changes in crystalline portion confirmed that amorphous phase degrades substantially faster compared to crystalline part. The plasticizer triacetine is disappearing also rather fast from the sample resulting besides other effect also in a temporary increase of Tg, which at the beginning grows almost to the value typical for PLA without plasticizer but later the Tg is decreasing due to substantial changes in molecular weight. Generally during composting, the samples keep shape for up to 8 days, after that time the material disintegrates to rough powder. © 2018 Elsevier B.V.1/0122/15, SAV, Slovenská Akadémia Vied; APVV 0301-14, APVV, Agentúra na Podporu Výskumu a Vývoja; APVV 0741-15, APVV, Agentúra na Podporu Výskumu a Vývoja; VEGA 2/0108/14, SAV, Slovenská Akadémia ViedSlovak Research and Development [APVV 0301-14, APVV 0741-15]; Slovak Republic Government Education Department; Slovak Academy of Sciences VEGA [2/0108/14, 1/0122/15
PLA/PHB-based materials fully biodegradable under both industrial and home-composting conditions
In order to make bioplastics accessible for a wider spectrum of applications, ready-to-use plastic material formulations should be available with tailored properties. Ideally, these kinds of materials should also be "home-compostable" to simplify their organic recycling. Therefore, materials based on PLA (polylactid acid) and PHB (polyhydroxybutyrate) blends are presented which contain suitable additives, and some of them contain also thermoplastic starch as a filler, which decreases the price of the final compound. They are intended for various applications, as documented by products made out of them. The produced materials are fully biodegradable under industrial composting conditions. Surprisingly, some of the materials, even those which contain more PLA than PHB, are also fully biodegradable under home-composting conditions within a period of about six months. Experiments made under laboratory conditions were supported with data obtained from a kitchen waste pilot composter and from municipal composting plant experiments. Material properties, environmental conditions, and microbiology data were recorded during some of these experiments to document the biodegradation process and changes on the surface and inside the materials on a molecular level.IGA/FT/2022/006; Agentúra na Podporu Výskumu a Vývoja, APVV: 313011V336, APVV-20-0193, APVV-20-0256; European Regional Development Fund, ERDF: FCH-S-21-7553Internal Grant Agency [IGA/FT/2022/006]; Slovak Research and Development Agency [APVV-20-0256, APVV-20-0193]; European Regional Development Fund [313011V336]; Specific University Research Grant [FCH-S-21-7553
PLA/PHB-Based Materials Fully Biodegradable under Both Industrial and Home-Composting Conditions
In order to make bioplastics accessible for a wider spectrum of applications, ready-to-use plastic material formulations should be available with tailored properties. Ideally, these kinds of materials should also be "home-compostable" to simplify their organic recycling. Therefore, materials based on PLA (polylactid acid) and PHB (polyhydroxybutyrate) blends are presented which contain suitable additives, and some of them contain also thermoplastic starch as a filler, which decreases the price of the final compound. They are intended for various applications, as documented by products made out of them. The produced materials are fully biodegradable under industrial composting conditions. Surprisingly, some of the materials, even those which contain more PLA than PHB, are also fully biodegradable under home-composting conditions within a period of about six months. Experiments made under laboratory conditions were supported with data obtained from a kitchen waste pilot composter and from municipal composting plant experiments. Material properties, environmental conditions, and microbiology data were recorded during some of these experiments to document the biodegradation process and changes on the surface and inside the materials on a molecular level