A micromechanics-based strength prediction methodology for notched metal matrix composites
An analytical micromechanics based strength prediction methodology was developed to predict failure of notched metal matrix composites. The stress-strain behavior and notched strength of two metal matrix composites, boron/aluminum (B/Al) and silicon-carbide/titanium (SCS-6/Ti-15-3), were predicted. The prediction methodology combines analytical techniques ranging from a three dimensional finite element analysis of a notched specimen to a micromechanical model of a single fiber. In the B/Al laminates, a fiber failure criteria based on the axial and shear stress in the fiber accurately predicted laminate failure for a variety of layups and notch-length to specimen-width ratios with both circular holes and sharp notches when matrix plasticity was included in the analysis. For the SCS-6/Ti-15-3 laminates, a fiber failure based on the axial stress in the fiber correlated well with experimental results for static and post fatigue residual strengths when fiber matrix debonding and matrix cracking were included in the analysis. The micromechanics based strength prediction methodology offers a direct approach to strength prediction by modeling behavior and damage on a constituent level, thus, explicitly including matrix nonlinearity, fiber matrix debonding, and matrix cracking
Effect of debond growth on stress-intensity factors in a cracked orthotropic sheet stiffened by a semi-infinite orthotropic sheet
Stress-intensity factors are determined for a cracked infinite sheet adhesively bonded to a stringer, and debonding of the adhesive layer is predicted. The stringer is modeled as a semi-infinite sheet. Adhesive nonlinearity is also included. Both the sheet and stringer are treated as homogeneous, orthotropic materials. A set of integral equations is formulated and solved to obtain the adhesive shear stresses and crack-tip stress-intensity factors. Adhesive debonding is predicted using a rupture criterion based on the combined adhesive stresses. When the crack is not under the stringer, the debond extends along the edge of the stringer. When the crack tip is beneath the stringer, the debond grows to the end of the crack, then along the edge of the stringer. Stress levels required for debond initiation decrease as the crack tip is moved beneath the stringer. With a nonlinear adhesive, the debond initiates at higher applied stress levels than in linear adhesive cases. Compared with the linear adhesive solution, modeling a nonlinear adhesive causes the stress-intensity factor to increase when the bond is assumed to remain intact but causes the stress-intensity factor to decrease when debonding is included
Effects of moisture, elevated temperature, and fatigue loading on the behavior of graphite/epoxy buffer strip panels with center cracks
The effects of fatigue loading combined with moisture and heat on the behavior of graphite epoxy panels with either Kevlar-49 or S-glass buffer strips were studied. Buffer strip panels, that had a slit in the center to represent damage, were moisture conditioned or heated, fatigue loaded, and then tested in tension to measure their residual strength. The buffer strips were parallel to the loading direction and were made by replacing narrow strips of the 0 deg graphite plies with Kevlar-49 epoxy or S-glass epoxy on a 1-for-1 basis. The panels were subjected to a fatigue loading spectrum. One group of panels was preconditioned by soaking in 60 C water to produce a 1 percent weight gain then tested at room temperature. One group was heated to 82 C during the fatigue loading. Another group was moisture conditioned and then tested at 82 C. The residual strengths of the buffer panels were not highly affected by the fatigue loading, the number of repetitions of the loading spectrum, or the maximum strain level. The moisture conditioning reduced the residual strengths of the S-glass buffer strip panel by 10 to 15 percent below the ambient results. The moisture conditioning did not have a large effect on the Kevlar-49 panels
A cracked orthotropic sheet stiffened by a semi-infinite orthotropic sheet
The stress intensity factor is determined for a cracked orthotropic sheet adhesively bonded to an orthotropic stringer. Since the stringer is modeled as a semiinfinite sheet, the solution is most appropriate for a crack tip located near a stringer edge. Both adherends are treated as homogeneous, orthotropic media. It is assumed they are in plane stress and the adhesive is in pure shear. From Green's functions and the complex variable theory of orthotropic elasticity developed by Lekhnitskiy, a set of integral equations is obtained. The integral equations are replaced by an equivalent set of algebraic equations which is solved to obtain the shear stress distribution in the adhesive layer. With these stresses, equations for the stress intensity factors at both crack tips are found. A parametric study is conducted to determine the sensitivity of the system to material properties and specimen configuration. Unless the crack tip is very close to or under the stringer the stress intensity factor is approximately that of an unstiffened sheet. However, as the crack propagates beneath the stringer, the stress intensity factor decreases significantly. Increasing the stiffness of the stringer or the adhesive also results in a decrease in the stress intensity factor
Elastic-plastic stress concentrations around crack-like notches in continuous fiber reinforced metal matrix composites
Continuous fiber silicon-carbide/aluminum composite laminates with slits were tested statically to failure. Five different layups were examined: (0) sub 8, (0 sub 2/ + or - 45) sub s, (0/90) sub 2s), (0/ + or - 45/90 sub s), and (+ or - 45) sub 2s. Either a 9.5 or a 19 mm slit was machined in the center of each specimen. The strain distribution ahead of the slit tip was found experimentally with a series of strain gages bonded ahead of the slit tip. A three-dimensional finite element program (PAFAC) was used to predict the strain distribution ahead of the slit tip for several layups. For all layups, except the (0) sub 8, the yielding of the metal matrix caused the fiber stress concentration factor to increase with increasing load. This is contrary to the behavior seen in homogeneous materials where yielding causes the stress concentration to drop. For the (0) sub 8 laminate, yielding of the matrix caused a decrease in the fiber stress concentration. The finite element analysis predicted these trends correctly
A macro-micromechanics analysis of a notched metal matrix composite
A macro-micromechanics analysis was formulated to determine the matrix and fiber behavior near the notch tip in a center-notched metal matrix composite. Results are presented for a boron/aluminum monolayer. The macro-level analysis models the entire notched specimen using a three dimensional finite element program which uses the vanishing-fiber-diameter model to model the elastic-plastic behavior of the matrix and the elastic behavior of the fiber. The micro-behavior is analyzed using a Discrete Fiber-Matrix (DFM) model containing one fabric and the surrounding matrix. The dimensions of the DFM model were determined by the ply thickness and the fiber volume fraction and corresponded to the size of the notch-tip element in the macro-level analysis. The boundary conditions applied to the DFM model were determined from the macro-level analysis. Stress components within the DFM model were calculated and stress distributions are presented along selected planes and surfaces within the DFM model, including the fiber-matrix interface. Yielding in the matrix was examined at the notch tip in both the macro- and micro-level analyses. The DFM model predicted higher stresses (24 percent) in the fiber compared to the global analysis. In the notch-tip element, the interface stresses indicated that a multi-axial criterion may be required to predict interfacial failure. The DFM analysis predicted yielding to initiate in the notch-tip element at a stress level 28 percent lower than predicted by the global analysis
Effect of fiber-matrix debonding on notched strength of titanium metal matrix composites
Two specimen configuration of a (0/90)2s SCS-6/Ti-15-3 laminate were tested and analyzed: a center hole (CH) specimen and a double edge notch (DEN) specimen. The two specimen configurations failed at similar stress levels. Two analytical techniques, a 3-D finite-element analysis and a macro-micromechanical analysis were used to predict the overall stress-deformation behavior and the notch-tip fiber-matrix interface stresses in both configurations
Finite-element analyses and fracture simulation in thin-sheet aluminum alloy
A two-dimensional, elastic-plastic finite-element analysis was used with a critical crack-tip-opening angle (CTOA) fracture criterion to model stable crack growth in thin-sheet 2024-T3 aluminum alloy under monotonic loading after precracking at different cyclic stress levels. Tests were conducted on three types of specimens: middle-crack, three-hole-crack and blunt-notch tensile specimens. An experiment technique was developed to measure CTOA during crack growth initiation and stable tearing using a high-resolution video camera and recorder. Crack front shapes were also measured during initiation and stable tearing using a fatigue marker-load technique. Three-dimensional elastic-plastic finite-element analyses of these crack shapes for stationary cracks were conducted to study the crack-front opening displacements. Predicted load against crack extension on middle-crack tension specimens agreed well with test results even for large-scale plastic deformations. The analyses were able to predict the effects of specimen size and precracking stress history on stable tearing. Predicted load against load-line displacements agreed well with test results up to maximum load bu the analyses tended to overpredict displacements as crack grew beyond the maximum load under displacement-controlled conditions. During the initiation phase, the measured CTOA values were high but decreased and remained nearly constant after a small amount of stable tearing. The constant value of CTOA agree well with the calculated value from the finite-element analysis. The larger CTOA values measured at the sheet surface during the initiation phase may be associated with the crack tunneling observed in the tests. Three-dimensional analyses for nonstraight crack fronts predicted much higher displacements near the free surface than in the interior
Manufacturing a thin wire electrostatic trap (TWIST) for ultracold polar molecules
We present a detailed description on how to build a Thin WIre electroStatic
Trap (TWIST) for ultracold polar molecules. It is the first design of an
electrostatic trap that can be superimposed directly onto a magneto optical
trap (MOT). We can thus continuously produce ultracold polar molecules via
photoassociation from a two species MOT and instantaneously trap them in the
TWIST without the need for complex transfer schemes. Despite the spatial
overlap of the TWIST and the MOT, the two traps can be operated and optimized
completely independently due to the complementary nature of the utilized
trapping mechanisms.Comment: 5 pages, 8 figures, updated conten
Three-dimensional elastic-plastic finite-element analyses of constraint variations in cracked bodies
Three-dimensional elastic-plastic (small-strain) finite-element analyses were used to study the stresses, deformations, and constraint variations around a straight-through crack in finite-thickness plates for an elastic-perfectly plastic material under monotonic and cyclic loading. Middle-crack tension specimens were analyzed for thicknesses ranging from 1.25 to 20 mm with various crack lengths. Three local constraint parameters, related to the normal, tangential, and hydrostatic stresses, showed similar variations along the crack front for a given thickness and applied stress level. Numerical analyses indicated that cyclic stress history and crack growth reduced the local constraint parameters in the interior of a plate, especially at high applied stress levels. A global constraint factor alpha(sub g) was defined to simulate three-dimensional effects in two-dimensional crack analyses. The global constraint factor was calculated as an average through-the-thickness value over the crack-front plastic region. Values of alpha(sub g) were found to be nearly independent of crack length and were related to the stress-intensity factor for a given thickness
- …