Green synthesis of ZnO nanoparticles and their photocatalyst degradation and antibacterial activity

The current study aimed to synthesize nanoparticles of Zinc oxide (ZnO) using the extract of Acalypha indica leaves and their photocatalyst degradation and antibacterial properties were also measured. The biosynthesized nanoparticles were analyzed using XRD, UV-visible, FT-IR, and SEM with EDAX, DLS, PL, and Zeta potential analysis. The synthesized nanoparticles had a mean size of 16 nm measured by XRD which was highly pure, and their spherical shape was confirmed by SEM. The UV-visible confirmed that ZnO nanoparticles have a direct band gap energy is 3.34 eV. The measured zeta size and potential of synthesized nanoparticles were 46 nm and -27 mV, respectively, determined by the DLS technique can be considered moderately stable colloidal solutions. The FT-IR analysis confirmed the presence of functional groups in the leaf extract and the ZnO nanoparticles. The biosynthesized ZnO nanoparticles have a homogeneous spherical morphology and the average particle is 35 nm. The PL analyses performed on synthesized nanoparticles showed a sharp blue band at 362 nm, which was attributed to the defects of structure in ZnO crystals. During natural sunlight illumination, ZnO nanoparticles demonstrated notable degradation of the dye methyl blue (MB). At 90 min of illumination, the degradation efficiency achieved was 96 %. Antibacterial properties were observed for synthesized nanoparticles against four bacterial strains, including Bacillus subtilis, Staphylococcus aureus, Pseudomonas aeruginosa, and Escherichia coli. The highest zone of inhibition was observed against Escherichia coli (25.2 mm). Overall, these studies indicate that Acalypha indica is a good sell for planting, and has the greatest chance of being used to develop nanoparticles for protection against environmental pollution and human health

Study on the Synthesis, Structural, Optical and Electrical Properties of ZnO and Lanthanum Doped ZnO Nano Particles by Sol-Gel Method

International audienceIn this study, pure and lanthanum doped ZnO nano particles have been succaessfully synthesized by sol-gel method using the mixture of Zinc acetate dihydrate and ethanol solution. The powders were calcination at 600°C for 2h. The effect of lanthanum incorporation on the structure, morphology, optical and electrical conductivity were examined by X-ray diffraction (XRD), Scanning Electron Microscope (SEM), Energy Dispersive X-ray Absorption (EDAX), Fourier transform infrared spectroscopy (FTIR), UV and Photo Luminescence (PL) Characterization. The average particle size of the synthesized ZnO nanoparticles is calculated using the Scherrer formula and is found to be of less than 20 nm. Luminescence as well as conductivity properties were found to be enhanced for the La doped ZnO nanoparticles. Introduction. Synthesize and study of nanostructured materials have become a major attractive interdisciplinary area of research over the past few decades. Recently rare earth ion doped II-IV semiconductor nano particles have received much attention because such doping can modify and improve optical properties of II-VI semiconductor nanoparticles by large amount [1-4]. Zinc Oxide is a transparent electro conductive and piezo electric material. Zinc Oxide is an excellent ultraviolet absorber and antibacterial agent. ZnO is one of the metal oxides which attracts due to its direct band gap energy of 3.37eV and large excitation binding energy of 60 meV at room temperature which provides excitonic emission more efficiently even at high temperature. ZnO is particularly important because of their unique optical/electronic properties and promising applications in various fields such as photonic catalysis [5], light emitting diodes [6], field emission, gas sensors [7], fluorescent materials and solar cells [8]

Photoluminescences properties of lanthanum-silver co-doped ZnO nano particles

Recently, transition metal (TM) and rare earth ion doped II–VI semiconductor nanoparticles have received much attention because such doping can modify and improve optical properties of II–VI semiconductor nanoparticles by large amount. In this study, undoped, La doped and La+Ag co-doped ZnO nano particles have been successfully synthesized by sol-gel method using the mixture of Zinc acetate dihydrate and ethanol solution. The powders were calcinated at 600 °C for 2 h. The effect of lanthanum and lanthanum-silver incorporation on the structure, morphology, optical and electrical conductivity were examined by X-ray diffraction (XRD), Scanning Electron Microscope (SEM), Energy Dispersive X-ray Absorption (EDAX), Fourier transform infrared spectroscopy (FTIR), UV and Photo Luminescence (PL) Characterization. The average particle size of the synthesized ZnO nanoparticles is calculated using the Scherrer formula and is found to be of less than 20 nm. Luminescences properties were found to be enhanced for the La and La+Ag co-doped ZnO nanoparticles