Formation of ultrafine ferrite by dynamic strain-induced transformation

In the current study, the role of dynamic strain induced transformation on ferrite grain refinement was investigated using different thermomechanical processing routes. A Ni-30Fe austenitic model alloy was also employed to study the evolution of the deformation structure under different deformation conditions. It was shown that the extreme refinement of ferrite is more likely due to the formation of extensive high angle intragranular defects in the austenite through deformation. Among the different thermomechanical parameters, the deformation temperature had a significant effect on the intragranular defect characteristics. There was a transition where the cell dislocation structure changed to laminar microband structures with a decrease in the deformation temperature. Moreover, the ultrafine grained structure was also successfully produced through static transformation using warm deformation process; in other words, concurrent deformation and transformation are not necessary for ultrafine ferrite formation.<br /

A study of the strengthening mechanism in the thermomechanically processed TRIP/TWIP steel

The strengthening mechanism responsible for the unique combination of ultimate tensile strength and elongation in a multiphase Fe-0.2C-1.5Mn-1.2Si-0.3Mo-0.6Al-0.02Nb (wt%) steel was studied. The microstructures with different volume fraction of polygonal fenite, bainite and retained austenite were simulated by controlled thermomechanical processing. The interupted tensile test was used to study the bainitic ferrite, retained austenite and polygonal ferrite behavior as a function of plastic strain. X-ray analysis was used to characterize the volume fraction and carbon content of retained austenite. TEM and heat-tinting were utilized to analyze the effect of bainitic fenite morphology on the strain induced transformation of retained austenite and retained austenite twinning as a function of strain in the bulk material. The study has shown that the austenite twinning mechanism is more preferable than the transformation induced plasticity mechanism during the early stages of deformation for a microstructure containing I5% polygonal ferrite, while the transformation induced plasticity effect is the main mechanism in when there is 50% of polygonal ferrite in the microstructure. The baillitic fenite morphology affects the deformation mode of retained austenite during straining. The polygonal fenite behavior during straining depends on dislocation substructure tonned due to the deformation and the additional mobile dislocations caused by the TRIP effect. TRIP and TWIP effects depend not only on the chemical and mechanical stability of retained austenite, but also on the interaction of the phases during straining.<br /

Nanostructural Engineering of Steel

The concept of microstructural engineering of steels is well established and is the basis for a wide range of processes and products. Recently, though, there has been increasing emphasis in developing microstructures that have submicron length scales and also in understanding in far greater detail the structures and solute effects that are occurring at the nanoscale. In this review it is proposed that we are heading towards the situation where we are applying nanostructural engineering concepts in the development of new steels. A range of examples are given as well as a discussion of the potential impact of new processing routes. Clearly the future advances will be driven through improved characterization methods, such as atom probe tomography, in combination with advanced modeling

The effect of multiple deformations on the formation of ultrafine grained steels

A C-Mn-Nb-Ti steel was deformed by hot torsion to study ultrafine ferrite formation through dynamic strain-induced transformation (DSIT) in conjunction with air cooling. A systematic study was carried out first to evaluate the effect of deformation temperature and prior austenite grain size on the critical strain for ultrafine ferrite formation (&epsilon; C,UFF) through single-pass deformation. Then, multiple deformations in the nonrecrystallization region were used to study the effect of thermomechanical parameters (i.e., strain, deformation temperature, etc.) on &epsilon; C,UFF. The multiple deformations in the nonrecrystallization region significantly reduced &epsilon; C,UFF, although the total equivalent strain for a given thermomechanical condition was higher than that required in single-pass deformation. The current study on a Ni-30Fe austenitic model alloy revealed that laminar microband structures were the key intragranular defects in the austenite for nucleation of ferrite during the hot torsion test. The microbands were refined and overall misorientation angle distribution increased with a decrease in the deformation temperature for a given thermomechanical processing condition. For nonisothermal multipass deformation, there was some contribution to the formation of high-angle microband boundaries from strains at higher temperature, although the strains were not completely additive.<br /

The influence of parent austenite characteristics on the intervariant boundary network in a lath martensitic steel

The influence of the parent austenite deformation state on the intervariant boundary network (i.e., population, plane orientation, and connectivity) of a lath martensitic microstructure was investigated using conventional EBSD mapping and five-parameter boundary analysis approach along with quantification of boundary connectivity using homology metrics. The lath martensite largely revealed a bimodal misorientation angle distribution, closely matched with the Kurdjumov–Sachs (K–S) orientation relationship. The application of deformation significantly changed the distribution, gradually reducing the intensity of the 60° misorientation angle peak. This was largely ascribed to substructure development within the parent austenite upon deformation, which stimulates particular variant/s having a habit plane (011)α′ closely parallel to the primary (111)γ and/or secondary (11¯¯¯1)γ slip plane. The interaction of these variants eventually promoted specific intervariant boundaries (e.g., 60°/[111], 10.5°/[011], and 49.5°/[110]) at the expense of 60°/[011]. The application of deformation in the parent austenite did not change the intervariant boundary plane character distribution, which mostly exhibited an anisotropic character terminated on {110} planes because of the displacive nature of the martensitic transformation. However, the extent of anisotropy progressively decreased with increasing strain in the austenite prior to transformation. The grain boundary network connectivity was markedly altered due to the local variant selection induced by the deformation. Deformation in the austenite regime generally decreased the connectivity of boundaries having a {110} plane orientation. The intervariant boundaries with the {110} twist character also displayed a similar trend, though the connectivity of {110} tilt boundaries progressively enhanced with increasing strain. The former was closely matched with a decrease in the population of 60°/[110] intervariant boundaries with the strain. The current findings suggest that the intervariant boundary network of lath martensite can be manipulated through changes in the parent austenite deformation state which, in turn, can be used to enhance key final product properties such as toughness.publishedVersio

Inequalities in higher education in low‐ and middle‐income countries:A scoping review of the literature

Motivation:  Higher  education  is  regarded  as  a  key  instrument  to  enhance  socioeconomic  mobility  andreduce inequalities. Recent literature reviews have examined inequalities in the higher education systemsof  high-income  countries,  but  less  is  known  about  the  situation  in  low-  and  middle-income  countries,where higher education is expanding fast.Purpose:  The  article  reviews  the  academic  literature  on  higher  education  in  low-  and  middle-incomecountries using a research framework inspired by social justice and capability approaches. It considers the financial,  socio-cultural,  human,  and  political  resource  domains  on  which  people  draw,  and  how  they relate to access, participation, and outcomes in higher education.Methods: A literature search for studies explicitly discussing in-country  inequalities  in  higher  education revealed  22  publications. Substantial  knowledge  gaps remain,  especially  regarding  the  political  (and decision-making)  side  of  inequalities;  the  ideologies  and  philosophies  underpinning  higher  education systems; and the linkages between resource domains, both micro and macro.Findings:  The  review  highlights  key  elements  for  policy-makers  and  researchers:  (1)  the  financial  lens alone  is  insufficient  to  understand  and  tackle  inequalities,  since  these  are  also  shaped  by  human  and other non-financial factors; (2) socio-cultural constructs are central in explaining unequal outcomes; and (3) inequalities develop throughout one’s life and need to be considered during, but also before and afterhigher education.  The scope  of  inequalities  is  wide, and  the literature  offers a  few ideas  for short-term fixes such as part-time and online education.Policy implications: Inclusive policy frameworks for higher education should include explicit goals related to (in)equality,  which  are  best  measured in  terms  of  the  extent  to  which  certain  actions  or  choices are feasible for all. Policies in these frameworks, we argue, should go beyond providing financial support, and also address socio-cultural and human resource constraints and challenges in retention, performance, and labour market outcomes. Finally, they should consider relevant contextual determinants of inequalities.</p

Evolution of microstructure and crystallographic texture during dissimilar friction stir welding of duplex stainless steel to low carbon-manganese structural steel

Electron backscattered diffraction (EBSD) was used to analyze the evolution of microstructure and crystallographic texture during friction stir welding of dissimilar type 2205 duplex stainless steel (DSS) to type S275 low carbon-manganese structural steel. The results of microstructural analyses show that the temperature in the center of stirred zone reached temperatures between Ac 1 and Ac 3 during welding, resulting in a minor ferrite-to-austenite phase transformation in the S275 steel, and no changes in the fractions of ferrite and austenite in the DSS. Temperatures in the thermomechanically affected and shoulder-affected zones of both materials, in particular toward the root of the weld, did not exceed the Ac 1 of S275 steel. The shear generated by the friction between the material and the rotating probe occurred in austenitic/ferritic phase field of the S275 and DSS. In the former, the transformed austenite regions of the microstructure were transformed to acicular ferrite, on cooling, while the dual-phase austenitic/ferritic structure of the latter was retained. Studying the development of crystallographic textures with regard to shear flow lines generated by the probe tool showed the dominance of simple shear components across the whole weld in both materials. The ferrite texture in S275 steel was dominated by D 1, D 2, E, E¯ , and F, where the fraction of acicular ferrite formed on cooling showed a negligible deviation from the texture for the ideal shear texture components of bcc metals. The ferrite texture in DSS was dominated by D 1, D 2, I, I¯ , and F, and that of austenite was dominated by the A, A¯ , B, and B¯ of the ideal shear texture components for bcc and fcc metals, respectively. While D 1, D 2, and F components of the ideal shear texture are common between the ferrite in S275 steel and that of dual-phase DSS, the preferential partitioning of strain into the ferrite phase of DSS led to the development of I and I¯ components in DSS, as opposed to E and E¯ in the S275 steel. The formations of fine and ultrafine equiaxed grains were observed in different regions of both materials that are believed to be due to strain-induced continuous dynamic recrystallization (CDRX) in ferrite of both DSS and S275 steel, and discontinuous dynamic recrystallization (DDRX) in austenite phase of DSS