Obtención de la zeolita MCM-22 a través de la síntesis hidrotermal utilizando diferentes métodos.

This study aims to evaluate different methodologies in the preparation of zeolite MCM-22. These materials were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and thermogravimetry (TG). The preparation of zeolite MCM-22 broke the hydrogels with the following molar composition: 0.511 SiO2: 0.039 NaOH: 0.024 Al2O3: H2O 23.06 (Method A) and 0.511 SiO2: 0.048 NaOH: 0.038 Al2O3: H2O 23.06 (method B). Obtention of zeolite MCM-22 can be confirmed by the peaks of X-ray diffraction showed that the typical topology of lamellar layers intercalated with organic molecules, the director of structures hexametilenoimina (HMI). SEM images showed that the zeolites are composed of clusters of spherical particles and identifies a change in morphology depending on the method employed. Through the results it is concluded that it is possible to synthesize zeolite MCM-22 with the two methods (A and B).En este estudio se evaluaron diferentes metodologías en la preparación de la zeolita MCM-22. Estos materiales se caracterizaron por difracción de rayos X (DRX), microscopía electrónica de barrido (SEM) y termogravimetría (TG). La preparación de la zeolita MCM-22 fracturó los hidrogeles con la siguiente composición molar: 0.511 SiO2: 0.039 NaOH: 0.024 Al2O3: 23.06 H2O (método A) y 0.511 SiO2: 0.048 NaOH: 0.038 Al2O3: 23.06 H2O (método B). La obtención de la zeolita MCM-22 puede ser confirmada por los picos de difracción de rayos X que mostró la topología típica de las capas laminares intercaladas con moléculas orgánicas, como conductor de estructuras hexametilendiamina (HMI). Imágenes SEM mostraron que las zeolitas se componen de conjuntos de partículas esféricas e identifican un cambio en la morfología en función del método empleado. A través de los resultados se concluye que es posible sintetizar zeolita MCM-22 con los dos métodos (A y B)