This study aims to evaluate different methodologies in the preparation of zeolite MCM-22. These materials were
characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and thermogravimetry (TG). The
preparation of zeolite MCM-22 broke the hydrogels with the following molar composition: 0.511 SiO2: 0.039
NaOH: 0.024 Al2O3: H2O 23.06 (Method A) and 0.511 SiO2: 0.048 NaOH: 0.038 Al2O3: H2O 23.06 (method B).
Obtention of zeolite MCM-22 can be confirmed by the peaks of X-ray diffraction showed that the typical topology
of lamellar layers intercalated with organic molecules, the director of structures hexametilenoimina (HMI). SEM
images showed that the zeolites are composed of clusters of spherical particles and identifies a change in
morphology depending on the method employed. Through the results it is concluded that it is possible to
synthesize zeolite MCM-22 with the two methods (A and B).En este estudio se evaluaron diferentes metodologías en la preparación de la zeolita MCM-22. Estos materiales
se caracterizaron por difracción de rayos X (DRX), microscopía electrónica de barrido (SEM) y termogravimetría
(TG). La preparación de la zeolita MCM-22 fracturó los hidrogeles con la siguiente composición molar: 0.511
SiO2: 0.039 NaOH: 0.024 Al2O3: 23.06 H2O (método A) y 0.511 SiO2: 0.048 NaOH: 0.038 Al2O3: 23.06 H2O
(método B). La obtención de la zeolita MCM-22 puede ser confirmada por los picos de difracción de rayos X que
mostró la topología típica de las capas laminares intercaladas con moléculas orgánicas, como conductor de
estructuras hexametilendiamina (HMI). Imágenes SEM mostraron que las zeolitas se componen de conjuntos de
partículas esféricas e identifican un cambio en la morfología en función del método empleado. A través de los
resultados se concluye que es posible sintetizar zeolita MCM-22 con los dos métodos (A y B)