Effect of cariogenic challenge on the stability of dentin bonds

Objective: The oral environment is subject to biofilm accumulation and cariogenic challenge, and few studies exist on the effect of these factors on the bond strength of adhesive systems. The aim of this study was to test if the exposure of adhesive interfaces to cariogenic challenge under biofilm accumulation could promote higher degradation than the exposure to biofilm accumulation alone. Material And Methods: Five molars were ground until exposure of medium dentin and then restored (Single Bond 2 and Z250 3M ESPE). The tooth/resin sets were cut to obtain beam-shaped specimens, which were distributed according to the aging conditions (n=20): water for 24 h (control); biofilm under cariogenic challenge for 3, 5 or 10 days; biofilm without cariogenic challenge for 10 days; and water for 3 months. Microcosm biofilms were formed from human saliva and grown in a saliva analogue medium, supplemented or not with sucrose to promote cariogenic challenge. Specimens were tested for microtensile bond strength, and failure modes were classified using light microscopy. Bond strength data were analyzed using ANOVA and failure modes were analyzed using ANOVA on ranks (α=0.05). Results: No significant differences in bond strength were detected among the aging methods (P=0.248). The aging period was associated with an increase in the frequency of adhesive failures for the groups aged for 10 days or longer (

Effect of filling technique on the bond strength of methacrylate and silorane-based composite restorations

Abstract The bond strength of methacrylate (Z350, 3M ESPE) and silorane (P90, 3M ESPE) restorations, using different cavity filling techniques, was investigated. Cavities (6 × 3 × 3) in bovine teeth were filled using bulk, oblique, or horizontal increments. A push-out test was carried out after 24 h. Data were statistically analyzed (&#945; = 5%). Methacrylate-based composites and the horizontal filling technique showed the highest bond strength values (10.2 ± 3.9, p < 0.05). Silorane-based composites showed no statistically significant differences regarding the filling techniques (p > 0.05)

Effect of cariogenic challenge on the stability of dentin bonds

Objective: The oral environment is subject to biofilm accumulation and cariogenic challenge, and few studies exist on the effect of these factors on the bond strength of adhesive systems. The aim of this study was to test if the exposure of adhesive interfaces to cariogenic challenge under biofilm accumulation could promote higher degradation than the exposure to biofilm accumulation alone. Material And Methods: Five molars were ground until exposure of medium dentin and then restored (Single Bond 2 and Z250 3M ESPE). The tooth/resin sets were cut to obtain beam-shaped specimens, which were distributed according to the aging conditions (n=20): water for 24 h (control); biofilm under cariogenic challenge for 3, 5 or 10 days; biofilm without cariogenic challenge for 10 days; and water for 3 months. Microcosm biofilms were formed from human saliva and grown in a saliva analogue medium, supplemented or not with sucrose to promote cariogenic challenge. Specimens were tested for microtensile bond strength, and failure modes were classified using light microscopy. Bond strength data were analyzed using ANOVA and failure modes were analyzed using ANOVA on ranks (α=0.05). Results: No significant differences in bond strength were detected among the aging methods (P=0.248). The aging period was associated with an increase in the frequency of adhesive failures for the groups aged for 10 days or longer (P<0.001). Conclusion: Aging leads to a higher prevalence of interfacial adhesive failures, although this effect is not associated with cariogenic challenge or reduction in bond strengths

Effect of cariogenic challenge on the stability of dentin bonds

Objective: The oral environment is subject to biofilm accumulation and cariogenic challenge, and few studies exist on the effect of these factors on the bond strength of adhesive systems. The aim of this study was to test if the exposure of adhesive interfaces to cariogenic challenge under biofilm accumulation could promote higher degradation than the exposure to biofilm accumulation alone. Material And Methods: Five molars were ground until exposure of medium dentin and then restored (Single Bond 2 and Z250 3M ESPE). The tooth/resin sets were cut to obtain beam-shaped specimens, which were distributed according to the aging conditions (n=20): water for 24 h (control); biofilm under cariogenic challenge for 3, 5 or 10 days; biofilm without cariogenic challenge for 10 days; and water for 3 months. Microcosm biofilms were formed from human saliva and grown in a saliva analogue medium, supplemented or not with sucrose to promote cariogenic challenge. Specimens were tested for microtensile bond strength, and failure modes were classified using light microscopy. Bond strength data were analyzed using ANOVA and failure modes were analyzed using ANOVA on ranks (&#945;=0.05). Results: No significant differences in bond strength were detected among the aging methods (P=0.248). The aging period was associated with an increase in the frequency of adhesive failures for the groups aged for 10 days or longer (P<0.001). Conclusion: Aging leads to a higher prevalence of interfacial adhesive failures, although this effect is not associated with cariogenic challenge or reduction in bond strengths

Effect of cariogenic challenge on the stability of dentin bonds

OBJECTIVE: The oral environment is subject to biofilm accumulation and cariogenic challenge, and few studies exist on the effect of these factors on the bond strength of adhesive systems. The aim of this study was to test if the exposure of adhesive interfaces to cariogenic challenge under biofilm accumulation could promote higher degradation than the exposure to biofilm accumulation alone. MATERIAL AND METHODS: Five molars were ground until exposure of medium dentin and then restored (Single Bond 2 and Z250 3M ESPE). The tooth/resin sets were cut to obtain beam-shaped specimens, which were distributed according to the aging conditions (n=20): water for 24 h (control); biofilm under cariogenic challenge for 3, 5 or 10 days; biofilm without cariogenic challenge for 10 days; and water for 3 months. Microcosm biofilms were formed from human saliva and grown in a saliva analogue medium, supplemented or not with sucrose to promote cariogenic challenge. Specimens were tested for microtensile bond strength, and failure modes were classified using light microscopy. Bond strength data were analyzed using ANOVA and failure modes were analyzed using ANOVA on ranks (α=0.05). RESULTS: No significant differences in bond strength were detected among the aging methods (P=0.248). The aging period was associated with an increase in the frequency of adhesive failures for the groups aged for 10 days or longer (P<0.001). CONCLUSION: Aging leads to a higher prevalence of interfacial adhesive failures, although this effect is not associated with cariogenic challenge or reduction in bond strengths