Morphology and photoluminescence study of titania nanoparticles

Titania nanoparticles are prepared by sol–gel chemistry with a poly(ethylene oxide) methyl ether methacrylate-block-poly(dimethylsiloxane)-block-poly(ethylene oxide) methyl ether methacrylate triblock copolymer acting as the templating agent. The sol–gel components—hydrochloric acid, titanium tetraisopropoxide, and triblock copolymer—are varied to investigate their effect on the resulting titania morphology. An increased titania precursor or polymer content yields smaller primary titania structures. Microbeam grazing incidence small-angle X-ray scattering measurements, which are analyzed with a unified fit model, reveal information about the titania structure sizes. These small structures could not be observed via the used microscopy techniques. The interplay among the sol–gel components via our triblock copolymer results in different sized titania nanoparticles with higher packing densities. Smaller sized titania particles, (∼13–20 nm in diameter) in the range of exciton diffusion length, are formed by 2% by weight polymer and show good crystallinity with less surface defects and high oxygen vacancies

Effects of porosity on dynamic indentation resistance of silica nanofoam

Abstract The dynamic indentation behaviors of monolithic silica nanofoams of various porosities are investigated. When the pore size is on the nm scale, as the porosity increases, despite the decrease in mass density, the resistance offered by silica nanofoam to dynamic indentation is maintained at a high level, higher than the resistance of solid silica or regular porous silica. This phenomenon is related to the fast collapse of nanocells, which produces a locally hardened region and significantly increases the volume of material involved in impact energy dissipation