Ageing of low-firing prehistoric ceramics in hydrothermal conditions

Remains of a prehistoric ceramic object, a moon-shaped idol from the Bronze Age found in archaeological site Zdiby near Prague in the Czech Republic, were studied especially in terms of the firing temperature. Archaeological ceramics was usually fired at temperatures below 1000 °C. It contained unstable non-crystalline products, residua after calcination of clay components of a ceramic material. These products as metakaolinite can undergo a reverse rehydration to a structure close to kaolinite. The aim of this work was to prove whether the identified kaolinite in archaeological ceramics is a product of rehydration. The model compound containing high amount of kaolinite was prepared in order to follow its changes during calcination and hydrothermal treatment. Archaeological ceramics and the model compound were treated by hydrothermal ageing and studied by XRF, XRD and IR analyses. It was proved that the presence of kaolinite in the border-parts of the archaeological object was not a product of rehydration, but that it originated from the raw materials

The preparation of dental glass-ceramic composites with controlled fraction of leucite crystals

This work is dealing with synthesis of leucite powder, which can be used for the preparation of dental glassceramic composites by subsequent thermal treatment. Newly developed procedure is based on preparation of dental raw material as a mixture of two separate compounds: the crystalline leucite powder prepared at relatively low temperature and a commercial matrix powder.Hydrothermal synthesis of tetragonal leucite particles (KAlSi2O6) with the average size of about 3 μm was developed in our laboratory. The leucite dental raw material was prepared by mixing of 20 wt.% of synthetic tetragonal leucite with commercial matrix. Dental composites were prepared from the dental raw material by uniaxial pressing and firing up to 960°C. Dilatometric measurements confirmed that the coefficient of thermal expansion increased by 32% when 20 wt.% of the tetragonal leucite was added into the basic matrix. In addition, it was showed that the synthesized leucite powder was suitable for the preparation of leucite composites with controlled coefficient of thermal expansion. High value of the thermal expansion coefficient enables application of prepared composite in metal-ceramics restorations

Restoration of the porcelain set from Březová

Přátelská porcelánová souprava byla vyrobena v Březové u Karlových Varů v rozmezí let 1857 ‐ 1873. Je ovlivněna tvorbou v období druhého rokoka a je zdobena technikou ruční malby. Dekorace je provedena pomocí zlata, emailu, naglazurových barev a zlatého listru. Restaurátorský zásah byl prováděn z důvodu mechanického poškození plastických detailů. Součástí bylo provedení a vyhodnocení průzkumů. Pomocí stereomikroskopu byl pozorován stav dekorací a poškozená místa. Dále byla hodnocena střepová hmota, a to jak z hlediska chemického (XRF), tak i mineralogického (XRD) složení. Díky pozorování výbrusu pomocí optického mikroskopu byla zhodnocena mikrostruktura porcelánu. Byly měřeny tloušťky vrstvy glazury a zlatého listru. Na základě vyhodnocení průzkumů byl sestaven restaurátorský záměr a po schválení zadavatelem bylo přistoupeno k samotnému restaurování. Postup spočíval v očištění předmětů a doplnění ztrát plněnými epoxidovými pryskyřicemi. Dále následovalo provedení barevných retuší. Byla imitována bílá barva porcelánu s glazurou, zlatý listr a barevný dekor. Pro tyto retuše byla zvolena epoxidová pryskyřice probarvená pomocí pigmentů, barevné tuše a čirá epoxidová pryskyřice. Dále byla imitována malba zlatem. Byl použit plátkový kov, akrylové barvy obsahující kovové pigmenty a čirá epoxidová pryskyřice. Po provedení restaurátorského zásahu byly navrženy vhodné podmínky uložení předmětů.A porcelain coffee set was made between 1857 and 1873 in Březová in Karlovy Vary region. The set was made in the Rococo revival style and was decorated by hand painting technique. The decoration is realized by gold, email, over‐glaze colours and golden lustre. The reason for the restoration was a mechanical damage of plastic details. The restored object was also examined and characterised by a set of chemical and physical methods. The stereomicroscope was used for a visual evaluation of decorations and damaged parts. The chemical and phase composition was analysed by X‐ray fluorescence resp. X‐ray diffraction. The microstructure of porcelain was evaluated by optical microscopy of thin sections. The thickness of glazing and golden lustre was measured. The restoration plan was arranged on the basis of the obtained results and after approval from submitter. The restoration involved cleaning the items and supplementing lost parts with filled epoxy resin, than followed by colour retouching. The fillings which underwent imitation were as follows: white colour of porcelain with glazing, golden lustre and colour decoration. Epoxy resin coloured with pigments, coloured ink and clear epoxy resin were selected for retouching. Another element to be imitated concerned gold paintings, in which leaf metal, acrylic paints containing metal pigments and clear epoxy resin were used. Suitable placement conditions for storing were suggested when the restoration procedure was completed

Degradation Processes of Medieval and Renaissance Glazed Ceramics

Corrosion effects in deposit environments (soil, waste pit, etc.), together with the glaze adherence and fit, could cause severe deterioration accompanied by different types of defects or growth of corrosion products. The aim of this work was to identify the source of surface degradation of the lead-glazed ceramics sets from the Prague area from the Romanesque to the Renaissance period. A combination of X-ray fluorescence (XRF), X-ray diffraction (XRD), optical microscopy (OM), scanning electron microscopy with energy dispersive X-ray spectroscopy (SEM/EDS), and simultaneous thermal analysis (STA) techniques along with stress state calculations was used to study the defects. Based on the interpretation of the possible sources of the observed defects, four types of degradation effects were schematically expressed for the archaeological samples. It was shown that the glazes were already appropriately chosen during the production of the Romanesque tiles and that their degradation occurred only due to long-term exposure to unsuitable environmental conditions

Metodika konzervování-restaurování nízkopálené nestabilní keramiky

Metodika je zaměřena na konzervování-restaurování nízkopálené nestabilní keramiky. Podává ucelený přehled o vhodných postupech pro zpracování materiálu tohoto typu. Obsahuje souhrn vhodných metod pro hodnocení stupně poškození, postupy odběru vzorku a doporučené analýzy pro identifikaci chemického a mineralogického složení keramiky. Dále popisuje možnosti čištění, postupy konsolidace, lepení a doplňování chybějících fragmentů a případné retuše. Obsahuje rovněž zásady pro vhodné uložení těchto předmětů a pro pochopení jednotlivých metod jsou uvedeny komentované příklady

Metodika konzervování-restaurování glazované keramiky

Metodika je zaměřena na konzervování-restaurování glazované keramiky s ohledem na stabilitu a pórovitost keramického střepu. Podává ucelený přehled o vhodných postupech pro zpracování materiálu tohoto typu. Obsahuje přehled vhodných metod pro hodnocení stupně poškození (jak střepu, tak glazury), postupy odběru vzorku a metody pro identifikaci chemického a mineralogického složení keramiky i glazury a stability jejich celkového systému. Dále popisuje možnosti čištění, postupy konsolidace, lepení a doplňování chybějících fragmentů a případné retuše střepu i glazury. Obsahuje rovněž zásady pro vhodné uložení těchto předmětů a pro pochopení jednotlivých výsledků jsou uvedeny komentované příklady