15 research outputs found
STRENGTH DEGRADATION UNDER 'FATIGUE' STIPULATION IN BULK-FILL COMPOSITES: AN IN VITRO APPRAISAL
Master'sMASTER OF SCIENC
Reliability, failure probability, and strength of resin-based materials for CAD/CAM restorations
Objective: This study investigated the Weibull parameters and 5% fracture probability of direct, indirect composites, and CAD/CAM composites. Material and Methods: Discshaped (12 mm diameter x 1 mm thick) specimens were prepared for a direct composite [Z100 (ZO), 3M-ESPE], an indirect laboratory composite [Ceramage (CM), Shofu], and two CAD/CAM composites [Lava Ultimate (LU), 3M ESPE; Vita Enamic (VE), Vita Zahnfabrik] restorations (n=30 for each group). The specimens were polished, stored in distilled water for 24 hours at 37°C. Weibull parameters (m= modulus of Weibull, σ0= characteristic strength) and flexural strength for 5% fracture probability (σ5%) were determined using a piston-on-three-balls device at 1 MPa/s in distilled water. Statistical analysis for biaxial flexural strength analysis were performed either by both one-way ANOVA and Tukey's post hoc (α=0.05) or by Pearson's correlation test. Results: Ranking of m was: VE (19.5), LU (14.5), CM (11.7), and ZO (9.6). Ranking of σ0 (MPa) was: LU (218.1), ZO (210.4), CM (209.0), and VE (126.5). σ5% (MPa) was 177.9 for LU, 163.2 for CM, 154.7 for Z0, and 108.7 for VE. There was no significant difference in the m for ZO, CM, and LU. VE presented the highest m value and significantly higher than ZO. For σ0 and σ5%, ZO, CM, and LU were similar but higher than VE. Conclusion: The strength characteristics of CAD/ CAM composites vary according to their composition and microstructure. VE presented the lowest strength and highest Weibull modulus among the materials
SURFACE CHARACTERIZATION AND MICROBIAL INTERACTION ON GRAPHENE COATED TITANIUM
Ph.DDOCTOR OF PHILOSOPHY (FOD
Translucency, hardness and strength parameters of PMMA resin containing graphene-like material for CAD/CAM restorations
10.1016/j.jmbbm.2019.103388Journal of the Mechanical Behavior of Biomedical Materials100103388-10338
Persistent inhibition of Candida albicans biofilm and hyphae growth on titanium by graphene nanocoating
10.1016/j.dental.2020.11.028DENTAL MATERIALS372370-37
Reliability, failure probability, and strength of resin-based materials for CAD/CAM restorations
ABSTRACT Objective: This study investigated the Weibull parameters and 5% fracture probability of direct, indirect composites, and CAD/CAM composites. Material and Methods: Discshaped (12 mm diameter x 1 mm thick) specimens were prepared for a direct composite [Z100 (ZO), 3M-ESPE], an indirect laboratory composite [Ceramage (CM), Shofu], and two CAD/CAM composites [Lava Ultimate (LU), 3M ESPE; Vita Enamic (VE), Vita Zahnfabrik] restorations (n=30 for each group). The specimens were polished, stored in distilled water for 24 hours at 37°C. Weibull parameters (m= modulus of Weibull, σ0= characteristic strength) and flexural strength for 5% fracture probability (σ5%) were determined using a piston-on-three-balls device at 1 MPa/s in distilled water. Statistical analysis for biaxial flexural strength analysis were performed either by both one-way ANOVA and Tukey's post hoc (α=0.05) or by Pearson's correlation test. Results: Ranking of m was: VE (19.5), LU (14.5), CM (11.7), and ZO (9.6). Ranking of σ0 (MPa) was: LU (218.1), ZO (210.4), CM (209.0), and VE (126.5). σ5% (MPa) was 177.9 for LU, 163.2 for CM, 154.7 for Z0, and 108.7 for VE. There was no significant difference in the m for ZO, CM, and LU. VE presented the highest m value and significantly higher than ZO. For σ0 and σ5%, ZO, CM, and LU were similar but higher than VE. Conclusion: The strength characteristics of CAD/ CAM composites vary according to their composition and microstructure. VE presented the lowest strength and highest Weibull modulus among the materials
Antimicrobial-free graphene nanocoating decreases fungal yeast-to-hyphal switching and maturation of cross-kingdom biofilms containing clinical and antibiotic-resistant bacteria
10.1016/j.bbiosy.2022.100069Biomaterials and Biosystems8100069-10006
Osteogenic potential of graphene coated titanium is independent of transfer technique
10.1016/j.mtla.2020.100604Materialia100604