Effect of radiant exposure and UV accelerated aging on physicochemical and mechanical properties of composite resins

Currently, there is no consensus in terms of defining the minimum radiant exposure values necessary for achieving adequate properties of composite resin. In addition, the long-term influence that radiant exposure has on the properties of composite resins is still questionable. Objective: The objective of this study was to evaluate the effect of radiant exposure and UV accelerated aging on the physico-chemical and mechanical properties of micro-hybrid and nanofilled composite resins. Material and Methods: A nanofilled (Filtek Supreme; 3M ESPE) and a micro-hybrid composite resin (Filtek Z250; 3M ESPE) were investigated under different radiant exposures (3.75, 9, and 24 J/cm2) and UV accelerated aging protocols (0, 500, 1000, and 1500 aging hours). The degree of conversion (DC), flexural strength (FS), modulus (M), water sorption (WS), and solubility (WL) were evaluated. The results obtained were analyzed using two-way ANOVA and Tukey’s test. Comparisons were performed using a significance level of α=0.05. Results: The DC, FS, and M were found to be significantly influenced by both radiant exposure and accelerated aging time. The DC and EM increased with radiant exposure in the no-aging group (0-hour aging) for both micro-hybrid and nanofilled composites, whereas no correlation was found after accelerated aging protocols. WS and WL of micro-hybrid and nanofilled composite resins were scarcely affected by radiant exposure (p>0.05), whereas they were significantly reduced by accelerated aging (p<0.001). Conclusions: Although increasing radiant exposure affected the degree of conversion and mechanical properties of micro-hybrid and nanofilled composites, no influence on the hydrolytic degradation of the material was observed. In contrast, UV accelerated aging affected both the physico-chemical and mechanical properties of the composites

Examining the Effect of Radiant Exposure on Commercial Photopolimerizable Dental Resin Composites

The objective of this study was to evaluate the effect of radiant exposure on the chemical and physical properties of four commercial dental resin composites. The four dental resin composites used were Kalore, Admira, Tetric N-Ceram Bulk Fill, and Filtek Z350 XT. The composites were subjected to three curing protocols: 1000 mW/cm2 for 5 s, 1000 mW/cm2 for 10 s, and 400 mW/cm2 for 25 s. The flexural strength, elastic modulus, water sorption, water solubility, degree of conversion, and polymerization shrinkage were evaluated. The results were analyzed by means of ANOVA and Tukey tests. For Admira and Kalore, significant differences between light exposure protocols were observed for the elastic modulus (p < 0.001), which was higher when a higher amount of radiant exposure was used. For Filtek Z350, differences were only observed for the degree of conversion (p < 0.001), and a higher amount of radiant exposure allowed us to obtain higher values. The Tetric N-Ceram Bulk Fill analysis showed significant differences for the elastic modulus and water sorption (p < 0.001), and specimens that had been subject to a radiant exposure of 10 J/cm2 showed a higher elastic modulus. In most cases, the physical and mechanical properties analyzed were not affected by different radiant exposure values. Other resin-based composite (RBC) characteristics seem to have a greater influence on material properties