Microhardness assessment of different commercial brands of resin composites with different degrees of translucence

Owing to improvements in its mechanical properties and to the availability of shade and translucence resources, resin composite has become one of the most widely used restorative materials in present day Dentistry. The aim of this study was to assess the relation between the surface hardness of seven different commercial brands of resin composites (Charisma, Fill Magic, Master Fill, Natural Look, Opallis, Tetric Ceram, and Z250) and the different degrees of translucence (translucid, enamel and dentin). Vickers microhardness testing revealed significant differences among the groups. Z250 was the commercial brand that showed the best performance in the hardness test. When comparing the three groups assessed within the same brand, only Master Fill and Fill Magic presented statistically significant differences among all of the different translucencies. Natural Look was the only one that showed no significant difference among any of the three groups. Charisma, Opallis, Tetric Ceram and Z250 showed significant differences among some of the tested groups. Based on the results found in this study, it was not possible to establish a relation between translucence and the microhardness of the resin composites assessed. Depending on the material assessed, however, translucence variation did affect the microhardness values of the resin composites

Theoretical knowledge versus practical performance in dental sculpting – preliminary study

Conhecer a anatomia dos dentes é de fundamental importância na prática das diversas especialidades odontológicas. Todas as faculdades de odontologia possuem obrigatoriamente em sua grade curricular uma disciplina responsável pelo ensino da anatomia dental, na qual um conteúdo teórico é transmitido aos alunos para reprodução na escultura em cera. Assim, o objetivo deste estudo foi avaliar se o conteúdo teórico programático ministrado na Disciplina de Escultura Dental do Departamento de Dentística da Faculdade de Odontologia da Universidade de São Paulo está relacionado com a performance dos alunos na escultura prática. Para isso, 76 provas teóricas, planejadas sobre a localização das características anatômicas do dente 23, e 76 esculturas em cera (prova prática) foram examinadas individualmente por dois examinadores pré-calibrados para cada característica selecionada. Os dados foram organizados em tabelas de acordo com as características analisadas e o tipo de exame (teórico ou prático). O teste de qui-quadrado apontou que não houve diferença estatisticamente significativa entre as provas teórica e prática (p ≥ 0.05). A estrutura dental que os alunos mais acertaram em ambas as provas foi o cíngulo (79%) e a de menor porcentagem de acerto na associação das 2 provas foi a bossa palatina (19%). Os achados são baseados somente nos resultados do desempenho dos alunos com relação à identificação e localização das estruturas anatômicas de um dente anterior. Dentro das limitações deste estudo, concluiu-se que, para os dados avaliados, não foi possível observar uma relação entre os conhecimentos teóricos adquiridos pelos alunos e seu desempenho prático na escultura.Conhecer a anatomia dos dentes é de fundamental importância na prática das diversas especialidades Odontológicas. Todas as escolas de Odontologia possuem obrigatoriamente em sua grade curricular uma disciplina responsável pelo ensino da anatomia dental, na qual um conteúdo teórico é transmitido aos alunos para reprodução na escultura em cera. Assim, o objetivo deste estudo foi avaliar se o conteúdo teórico programático está sendo aplicado na escultura prática. Para isso 76 provas teóricas, planejadas sobre a localização das características anatômicas do dente 23, e 76 esculturas em cera (prova prática), foram examinadas individualmente por 2 examinadores pré-calibrados para cada característica selecionada. Os dados foram organizados em tabelas de acordo com as características analisadas e o tipo de exame (teórico ou prático). O teste do qui-quadrado apontou que não houve diferença estatisticamente significativa entre as provas teórica e prática (p≥0.05). A estrutura dental que os alunos mais acertaram em ambas as provas foi o cíngulo (79%) e a de menor porcentagem de acerto na associação das 2 provas foi a bossa palatina (19%). Os achados são baseados somente nos resultados do desempenho dos alunos com relação a identificação e localização das estruturas anatômicas de um dente anterior. Dentro das limitações deste estudo, concluiu-se que, para os dados avaliados, não foi possível observar uma relação entre os conhecimentos teóricos adquiridos e o desempenho prático dos aluno

Evaluation of the remove possibility of composite resin staining submitted to artificial aging through repolishing

Nesta pesquisa in vitro verificou-se a possibilidade de remoção do manchamento causado por café ou vinho tinto em cinco resinas compostas disponíveis comercialmente, após serem submetidas ao processo de envelhecimento. Trinta e seis espécimes de cada resina composta foram confeccionados em uma matriz de teflon, com 10 mm de diâmetro e 1,5 mm de espessura. Os espécimes foram mantidos em água destilada a 37ºC por 24 horas e, em seguida, polidos com irrigação na politriz (Ecomet Buehler USA) nas duas superfícies, com lixa de carbureto de silício com granulação de número 600, até atingirem a espessura de 1,3 ±0,01 mm. Após o polimento, a cor dos espécimes foi aferida com espectrofotômetro Cintra 10 UV (Visible Spectrometer, GBC, Austrália). Todos os espécimes foram submetidos à ciclagem térmica com temperaturas de 5 e 55ºC, com tempo de imersão de 1 minuto, por 1000 ciclos em solução de 75% álcool-água. Após a ciclagem térmica, os espécimes foram mantidos imersos em água destilada a 37ºC até completar o período de 7 dias da confecção das amostras. Após esse período, todos os espécimes foram levados ao espectrofotômetro para leitura da cor. Os espécimes foram divididos em três grupos, cada um com n=12, de acordo com as soluções em que foram imersos: água destilada (controle), café e vinho tinto. Para que o processo de manchamento acontecesse em uma única superfície do espécime, uma das faces e a superfície lateral do espécime foram isoladas com cera branca. Os espécimes foram imersos nas diferentes soluções e mantidos a 37ºC por 14 dias. Após o período de manchamento, a cera foi removida e a superfície submetida ao manchamento passou por escovação com escova elétrica (Escova Elétrica Braun Oral-B Procter & Gamble do Brasil S.A., Manaus, Brasil) por 30 segundos com pressão leve. Os espécimes foram secos com papel absorvente e novamente levados ao espectrofotômetro para medição da cor. Em seguida, os espécimes foram submetidos a três desgastes de 20 m e a cor foi aferida após cada um dos desgastes. O cálculo da diferença de cor foi realizado através da fórmula CIEDE2000. De acordo com a metodologia utilizada neste estudo, concluiuse que o manchamento provocado por café e vinho tinto nos compósitos avaliados foi superficial e um desgaste de 20 m foi suficiente para remoção de tal manchamento.This in vitro research verified the possible elimination of staining caused by coffee and red wine in five commercial composite resins, after being submitted to thermal cycling. Thirty six specimens were prepared in a teflon mold with 10 mm in diameter and 1.5 mm thick. The specimens were immersed in water at 37ºC for 24 h and polished (Ecomet Buehler - USA) in both surfaces with a # 600 grit silicon carbide paper until achieve 1.3 ±0.01 mm thickness. After polishing, specimens color was measured in a spectrophotometer Cintra 10 UV (Visible Spectrometer, GBC, Austrália). All specimens were submitted to thermal cycling with temperatures of 5 and 55ºC with a dwell time of 1 minute, for 1000 cycles in a 75% ethanol/water solution. After thermal cycling the specimens were immersed in water at 37ºC until complete 7 days from the preparation of the specimens. All the specimens were then taken into spectrophotometer for measuring the color. The specimens were divided into 3 groups (n=12): distilled water (control), coffee and red wine. For the purpose of the staining process to occur in only one surface, all the side and one of the surfaces were isolated with white wax. The specimens were immersed in one of the solutions at 37ºC for 14 days. After the staining period, the wax was removed and the specimens were brushed with electric toothbrush (Braun Oral-B, Procter & Gamble do Brasil S.A., Manaus, Brasil) for 30 seconds with a slight pressure. The specimens were dry with a tissue paper and were taken to spectrophotometer for measuring the color. Following, the specimens were submitted to three wears of 20 m and the color was measured after each one of the wears. The calculation of the color difference was made through CIEDE2000 formula. According to the methodology used in this research, it was concluded that the staining caused by coffee and red wine was superficial and one wear of 20 m was enough for removing the discoloration

In vitro evaluation of the correlation among extrinsic staining, degree of conversion, roughness, sorption and solubility of resin composite

Nesta pesquisa in vitro verificou-se a possível correlação do manchamento superficial de resinas compostas com grau de conversão, rugosidade, sorção e solubilidade. Foram testados cinco compósitos: Charisma Opal, Filtek P90, GrandioSO, IPS Empress Direct e NDurance; todos da cor A2. Foram confeccionados 40 espécimes de cada material. Dez espécimes foram destinados aos testes de sorção e solubilidade, que foram divididos em dois grupos (n=5): Grupo 1 (com desidratação prévia) e Grupo 2 (sem desidratação prévia). Trinta espécimes foram destinados aos testes de grau de conversão, rugosidade e manchamento superficial; que foram divididos em dois grupos: Imediato e 24 horas. No grupo Imediato, a leitura do espectro para o cálculo do grau de conversão e a leitura da cor inicial (baseline) foram realizadas imediatamente após a confecção dos espécimes, que foram imersos nas bebidas corantes na sequência. No grupo 24 horas, os espécimes foram mantidos em água destilada a 37oC por 24 h. A leitura do espetro final para o cálculo do grau de conversão e a leitura da cor inicial (baseline) foram realizadas 24 h após a confecção dos espécimes, que só então foram imersos nas bebidas corantes. O polimento e a leitura da rugosidade foram realizados após a leitura do espectro e antes da imersão nas bebidas. Os espécimes foram divididos em três grupos (n=5): água destilada (controle), café e vinho tinto. A amostra foi mantida imersa nas bebidas por 7 dias, com temperatura em 37oC. A leitura da cor final foi realizada após esse período, em ambos os grupos. A diferença de cor foi calcula a partir da fórmula CIEDE2000. A análise estatística foi realizada e o teste de Pearson foi aplicado para a análise da correlação das propriedades testadas. De acordo com a metodologia utilizada neste estudo, não foi possível estabelecer correlação entre manchamento dos compósitos resinosos com grau de conversão, rugosidade superficial, sorção e solubilidade; não foi encontrada diferença no manchamento do grupo que foi submetido imediatamente às bebidas corantes com o grupo que foi submetido ao manchamento após 24 horas da sua confecção; o vinho tinto causou maior alteração de cor do que o café; e o comportamento dos compósitos na presença das bebidas corantes não foi semelhante. Além disso, não houve diferença significativa nas duas metodologias usadas para o teste de sorção e solubilidade.This in vitro research verified the possible correlation of superficial staining of resin composites with degree of conversion, roughness, sorption and solubility. Five composites were tested: Charisma Opal, Filtek P90, GrandioSO, IPS Empress Direct and NDurance; shade A2. Forty specimens of each material were prepared. Ten specimens were reserved for sorption/solubility tests and were divided into 2 groups (n=5): Group 1 (with previous dehydration) and Group 2 (without previous dehydration). Thirty specimens were reserved for degree of conversion, roughness and staining tests; which were divided into 2 groups: Immediate and 24 hours. In Immediate group, degree of conversion and initial color measurement (baseline) were calculated immediately after sample preparation, which was immersed in coloring beverages. In 24 hours group, specimens were maintained in distilled water at 37oC for 24 h. Initial color measurement (baseline) and degree of conversion were calculated 24 h after sample preparation. Polishing and roughness measurement were made before the immersion of specimens in beverages. Sample was divided into 3 groups (n=5): distilled water (control), coffee and red wine. The specimens were maintained immersed for staining during 7 days at 37oC. Final color measurement was made after this period, in both groups. Color difference was calculated based on CIEDE2000 formula. Statistical analysis was performed and Pearson test was applied to analyze correlation between the properties tested. According to the methodology used in this research, it was not possible to establish correlation between composite staining and degree of conversion, roughness, sorption and solubility; it was not found any difference between Immediate and 24 hours groups; staining caused by red wine were more intense than coffee; the composites behavior in staining was not similar. Despite of this result, there was no significant difference between the sorption/solubility methods tested

Conhecimento teórico versus performance prática em escultura dental – estudo preliminar

Conhecer a anatomia dos dentes é de fundamental importância na prática das diversas especialidades Odontológicas. Todas as escolas de Odontologia possuem obrigatoriamente em sua grade curricular uma disciplina responsável pelo ensino da anatomia dental, na qual um conteúdo teórico é transmitido aos alunos para reprodução na escultura em cera. Assim, o objetivo deste estudo foi avaliar se o conteúdo teórico programático está sendo aplicado na escultura prática. Para isso 76 provas teóricas, planejadas sobre a localização das características anatômicas do dente 23, e 76 esculturas em cera (prova prática), foram examinadas individualmente por 2 examinadores pré-calibrados para cada característica selecionada. Os dados foram organizados em tabelas de acordo com as características analisadas e o tipo de exame (teórico ou prático). O teste do qui-quadrado apontou que não houve diferença estatisticamente significativa entre as provas teórica e prática (p≥0.05). A estrutura dental que os alunos mais acertaram em ambas as provas foi o cíngulo (79%) e a de menor porcentagem de acerto na associação das 2 provas foi a bossa palatina (19%). Os achados são baseados somente nos resultados do desempenho dos alunos com relação a identificação e localização das estruturas anatômicas de um dente anterior. Dentro das limitações deste estudo, concluiu-se que, para os dados avaliados, não foi possível observar uma relação entre os conhecimentos teóricos adquiridos e o desempenho prático dos alunosConhecer a anatomia dos dentes é de fundamental importância na prática das diversas especialidades odontológicas. Todas as faculdades de odontologia possuem obrigatoriamente em sua grade curricular uma disciplina responsável pelo ensino da anatomia dental, na qual um conteúdo teórico é transmitido aos alunos para reprodução na escultura em cera. Assim, o objetivo deste estudo foi avaliar se o conteúdo teórico programático ministrado na Disciplina de Escultura Dental do Departamento de Dentística da Faculdade de Odontologia da Universidade de São Paulo está relacionado com a performance dos alunos na escultura prática. Para isso, 76 provas teóricas, planejadas sobre a localização das características anatômicas do dente 23, e 76 esculturas em cera (prova prática) foram examinadas individualmente por dois examinadores pré-calibrados para cada característica selecionada. Os dados foram organizados em tabelas de acordo com as características analisadas e o tipo de exame (teórico ou prático). O teste de qui-quadrado apontou que não houve diferença estatisticamente significativa entre as provas teórica e prática (p ≥ 0.05). A estrutura dental que os alunos mais acertaram em ambas as provas foi o cíngulo (79%) e a de menor porcentagem de acerto na associação das 2 provas foi a bossa palatina (19%). Os achados são baseados somente nos resultados do desempenho dos alunos com relação à identificação e localização das estruturas anatômicas de um dente anterior. Dentro das limitações deste estudo, concluiu-se que, para os dados avaliados, não foi possível observar uma relação entre os conhecimentos teóricos adquiridos pelos alunos e seu desempenho prático na escultura