Comprehensive in vitro and in vivo studies of novel melt-derived Nb-substituted 45S5 bioglass reveal its enhanced bioactive properties for bone healing

The present work presents and discusses the results of a comprehensive study on the bioactive properties of Nb-substituted silicate glass derived from 45S5 bioglass. In vitro and in vivo experiments were performed. We undertook three different types of in vitro analyses: (i) investigation of the kinetics of chemical reactivity and the bioactivity of Nb-substituted glass in simulated body fluid (SBF) by 31P MASNMR spectroscopy, (ii) determination of ionic leaching profiles in buffered solution by inductively coupled plasma optical emission spectrometry (ICP-OES), and (iii) assessment of the compatibility and osteogenic differentiation of human embryonic stem cells (hESCs) treated with dissolution products of different compositions of Nb-substituted glass. The results revealed that Nb-substituted glass is not toxic to hESCs. Moreover, adding up to 1.3 mol% of Nb2O5 to 45S5 bioglass significantly enhanced its osteogenic capacity. For the in vivo experiments, trial glass rods were implanted into circular defects in rat tibia in order to evaluate their biocompatibility and bioactivity. Results showed all Nb-containing glass was biocompatible and that the addition of 1.3 mol% of Nb2O5, replacing phosphorous, increases the osteostimulation of bioglass. Therefore, these results support the assertion that Nb-substituted glass is suitable for biomedical applications

Research on implants and osseointegration

Osseointegration was originally defined as a direct structural and functional connection between ordered living bone and the surface of a load-carrying implant. It is now said that an implant is regarded as osseointegrated when there is no progressive relative movement between the implant and the bone with which it is in direct contact. Although the term osseointegration was initially used with reference to titanium metallic implants, the concept is currently applied to all biomaterials that have the ability to osseointegrate. Biomaterials are closely related to the mechanism of osseointegration; these materials are designed to be implanted or incorporated into the living system with the aims to substitute for, or regenerate, tissues and tissue functions. Objective evaluation of the properties of the different biomaterials and of the factors that influence bone repair in general, and at the bone tissue?implant interface, is essential to the clinical success of an implant. The Biomaterials Laboratory of the Oral Pathology Department of the School of Dentistry at the University of Buenos Aires is devoted to the study and research of the properties and biological effects of biomaterials for dental implants and bone substitutes. This paper summarizes the research work resulting from over 25 years? experience in this field. It includes studies conducted at our laboratory on the local and systemic factors affecting the peri-implant bone healing process, using experimental models developed by our research team. The results of our research on corrosion, focusing on dental implants, as well as our experience in the evaluation of failed dental implants and bone biopsies obtained following maxillary sinus floor augmentation with bone substitutes, are also reported. Research on biomaterials and their interaction with the biological system is a continuing challenge in biomedicine, which aims to achieve optimal biocompatibility and thus contribute to patient health.Fil: Guglielmotti, Maria Beatriz. Universidad de Buenos Aires; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Houssay; ArgentinaFil: Olmedo, Daniel Gustavo. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Houssay; Argentina. Universidad de Buenos Aires; ArgentinaFil: Cabrini, Rómulo L.. Comisión Nacional de Energía Atómica; Argentina. Universidad de Buenos Aires; Argentin

Novel strontium-doped bioactive glass nanoparticles enhance proliferation and osteogenic differentiation of human bone marrow stromal cells

The present study investigates a new family of bioactive glass nanoparticles with and without Sr-doping focusing on the influence of the nanoparticles on human bone marrow stromal cells (hBMSCs) in vitro. The bioactive glass nanoparticles were fabricated by flame spray synthesis and a particle diameter of 30–35 nm was achieved. Glass nanoparticles were undoped (BG 13-93-0Sr) or doped with 5 wt% strontium (Sr) (BG 13-93-5Sr) and used at concentrations of 10 and 100 μg/cm² (particles per culture plate area), respectively. Cells were cultured for 14 days after which the samples were analysed regarding metabolic activity and expression of various bone-specific genes. Cell growth and morphology indicated the high cytocompatibility of the nanoparticulate bioactive glass. The presence of the nanoparticles enhanced cell growth compared to the plain polystyrene control group. At a concentration of 100 μg/cm², Sr-doped particles led to significantly enhanced gene expression of osteocalcin, collagen type 1 and vascular endothelial growth factor. Thus, Sr-doped nanoparticles showing a dose-dependent increase of osteogenic differentiation in hBMSCs are a promising biomaterial for bone regeneration purposes