Experimental analysis of wear resistance of compacts of fine-dispersed iron powder and tungsten monocarbide nanopowder produced by impulse pressing

The paper presents the results of studying the structure and wear resistance of compacts produced from fine dispersed reduced iron powder (average particle size 3–5μm) with the addition of tungsten carbide (WC) nanopowder with the average particle size of 25–30 nm. The mass fraction of tungsten carbide (wolfram carbide) in the powder composition was 5% and 10% of the total mass. Impulse pressing was conducted using the modified Kolsky method at compacting temperatures of 20 °C to 300 °C. The produced compacts had relative density of over 90%. Metallographic studies using the scanning electronic microscopy method on a TESCAN VEGA II electronic microscope have shown that the produced compacts have a fairly homogeneous fine-grained structure, with a uniform pattern of pore distribution, the form of the pores being close to spherical. X-ray microanalysis using an INCA Energy 250 energy-dispersion spectrometer with scanning along the surface line and transversal laps testifies to the fact that, in the considered temperature range, dynamic compaction does not lead to any noticeable changes in the distribution of the Fe, W and C elements over the bulk of the specimens. The conducted measurements of micro-hardness of the compacts have shown that it increases considerably with the pressing temperature. The produced compacts were tested for wear resistance in a dry friction regime, using the ‘rotating disk – stationary specimen’ configuration. Mass loss of the compacts as a function of testing time is presented. Wear resistance of compacts depends on pressing temperature and concentration of the WC powder in the matrix of reduced iron. It has been experimentally determined that maximal wear resistance is observed in the compacts with the mass fraction of WC equal to 10%, produced at a pressing temperature of 300 °C

Mechanical Response Change in Fine Grain Concrete Under High Strain and Stress Rates

International audienceExperimental results on assessing the effects of strain and stress rates on the behavior of fine-grain concretes are presented. Specimens of fine-grain and fiberreinforced concretes were dynamically tested using the Kolsky method and its modification, the “Brazilian test”. As a result of the experiments, values of the Dynamic Increase Factor (DIF) were determined for both the materials studied. Their curves as a function of strain and stress rates were constructed. The experimental data is compared with the theoretically obtained values of DIF as a function of strain rate available in the literatur

Strain-Rate Dependency of a Unidirectional Filament Wound Composite under Compression

This article presents the results of experimental studies concerning the dynamic deformation and failure of a unidirectional carbon fiber reinforced plastic (T700/LY113) under compression. The test samples were manufactured through the filament winding of flat plates. To establish the strain rate dependencies of the strength and elastic modulus of the material, dynamic tests were carried out using a drop tower, the Split Hopkinson Pressure Bar method, and standard static tests. The samples were loaded both along and perpendicular to the direction of the reinforcing fiber. The applicability of the obtained samples for static and dynamic tests was confirmed through finite element modeling and the high-speed imaging of the deformation and failure of samples during testing. As a result of the conducted experimental studies, static and dynamic stress-strain curves, time dependencies of deformation and the stress and strain rates of the samples during compression were obtained. Based on these results, the strain rate dependencies of the strength and elasticity modulus in the strain rate range of 0.001–600 1/s are constructed. It is shown that the strain rate significantly affects the strength and deformation characteristics of the unidirectional carbon fiber composites under compression. An increase in the strain rate by 5 orders of magnitude increased the strength and elastic modulus along the fiber direction by 42% and 50%, respectively. Perpendicular loading resulted in a strength and elastic modulus increase by 58% and 50%, respectively. The average strength along the fibers at the largest studied strain rate was about 1000 MPa. The obtained results can be used to design structural elements made of polymer composite materials operating under dynamic shock loads, as well as to build models of mechanical behavior and failure criteria of such materials, taking into account the strain rate effects

Incongruity-resolution humorous strategies in image macro memes

In previous research (Yus 2016, 2017), a classification of jokes was proposed depending on how the humorous incongruity-resolution strategy was achieved. Twelve cases were isolated resulting from the combination of several parameters: (1) a differentiation between discourse-based incongruities and frame-based incongruities; (2) the location of the incongruity-triggering element (setup or punchline); and (3) three types of resolution: discourse-, frame- and implication-based. This paper proposes a similar taxonomy of incongruity-resolution patterns for a specific type of internet discourse: the image macro meme. The resulting seven-case taxonomy inherits some of the features of that were proposed for verbal jokes, albeit exhibiting the extent to which the image plays a specific role in the successful meme-centred humorous strategy