27 research outputs found
Auger Spectroscopy of Hydrogenated Diamond Surfaces
An energy shift and a change of the line shape of the carbon core-valence-valence Auger spectra are observed for diamond surfaces after their exposure to an electron beam, or annealing at temperatures higher then 950 C. The effect is studied for both natural diamond crystals and chemical-vapor-deposited diamond films. A theoretical model is proposed for Auger spectra of hydrogenated diamond surfaces. The observed changes of the carbon Auger line shape are shown to be related to the redistribution of the valence-band local density of states caused by the hydrogen desorption from the surface. One-electron calculation of Auger spectra of diamond surfaces with various hydrogen coverages are presented. They are based on self-consistent wave functions and matrix elements calculated in the framework of the local-density approximation and the self-consistent linear muffin-tin orbital method with static core-hole effects taken into account. The major features of experimental spectra are explained
Electron Emission Observations from As-Grown and Vacuum-Coated Chemical Vapor Deposited Diamond
Field emission has been observed from chemical vapor deposited diamond grown on Mo and Si substrates. Emission was observed at fields as low as 20 kV/cm. The samples were tested in the as-grown form, and after coating with thin films of Au, CsI, and Ni. The emission current was typically maximum at the onset of the applied field, but was unstable, and decreased rapidly with time from the as-grown films. Thin Au layers, approximately 15 nm thick, vacuum deposited onto the diamond samples significantly improved the stability of the emission current at values approximately equal to those from uncoated samples at the onset of the applied field. Thin layers of CsI, approximately 5 nm thick, were also observed to improve the stability of the emission current but at values less than those from the uncoated samples at the onset of the applied field. While Au and CsI improved the stability of the emission, Ni was observed to have no effect
Negative Electron Affinity Effect on the Surface of Chemical Vapor Deposited Diamond Polycrystalline Films
Strong negative electron affinity effects have been observed on the surface of as-grown chemical vapor deposited diamond using Secondary Electron Emission. The test samples were randomly oriented and the surface was terminated with hydrogen. The effect appears as an intensive peak in the low energy part of the spectrum of the electron energy distribution and may be described in the model of effective negative electron affinity
Thermionic Emission of Single-Wall Carbon Nanotubes Measured
Researchers at the NASA Glenn Research Center, in collaboration with the Rochester Institute of Technology, have investigated the thermionic properties of high-purity, single-wall carbon nanotubes (SWNTs) for use as electron-emitting electrodes. Carbon nanotubes are a recently discovered material made from carbon atoms bonded into nanometer-scale hollow tubes. Such nanotubes have remarkable properties. An extremely high aspect ratio, as well as unique mechanical and electronic properties, make single-wall nanotubes ideal for use in a vast array of applications. Carbon nanotubes typically have diameters on the order of 1 to 2 nm. As a result, the ends have a small radius of curvature. It is these characteristics, therefore, that indicate they might be excellent potential candidates for both thermionic and field emission