Thermal Decomposition of Some Linear Perfluoroalkanes in an Inconel Tube
The products of the pyrolysis reactions of perfluoropropane, perfluoroethane, and carbon tetrafluoride in an Inconel bomb are described. The values for the energy of activation and frequency factor for the first-order pyrolysis reactions are respectively: (1) 80 kcal. per mole and 2x10(exp14) sec.(exp-1) for perfluoropropane; (2) 53 kcal. per mole and 3x10(exp7) sec.(exp-1) for perfluoroethane; and (3) 96 kcal. per mole and 4x10(exp13) sec.(exp-1) for carbon tetrafluoride
The alkaline zinc electrode as a mixed potential system
Cathodic and anodic processes for the alkaline zinc electrode in 0.01 molar zincate electrolyte (9 molar hydroxide) were investigated. Cyclic voltammograms and current-voltage curves were obtained by supplying pulses through a potentiostat to a zinc rotating disk electrode. The data are interpreted by treating the system as one with a mixed potential; the processes are termed The zincate and corrosion reactions. The relative proportions of the two processes vary with the supplied potential. For the cathodic region, the cathodic corrosion process predominates at higher potentials while both processes occur simultaneously at a lower potential (i.e., 50 mV). For the anodic region, the anodic zincate process predominates at higher potentials while the anodic corrosion process is dominant at lower potential (i.e., 50 mV) if H2 is present
Oxidation and hot corrosion of hot-pressed Si3N4 at 1000 deg C
The oxidation and hot corrosion of a commercial, hot-pressed Si3N4 were investigated at 1000 C under an atmosphere of flowing O2. For the hot corrosion studies, thin films of Na2SO4 were airbrushed on the Si3N4 surface. The hot corrosion attack was monitored by the following techniques: continuous weight measurements, SO2 evolution, film morphology, and chemical analyses. Even though the hot corrosion weight changes after 25 hr were relatively small, the formation of SiO2 from oxidation of Si3N4 was an order of magnitude greater in the presence of molten Na2SO4. The formation of a protective SiO2 phase at the Si3N4 surface is minimized by the fluxing action of the molten Na2SO4 thereby allowing the oxidation of the Si3N4 to proceed more rapidly. A simple process is proposed to account for the hot corrosion process
Ionic conductivity of lanthanum fluoride
Electrical conductivity of lanthanum fluoride single crystal with calcium impuritie
Solubility, stability, and electrochemical studies of sulfur-sulfide solutions in organic solvents
A preliminary study of the sulfur electrode in organic solvents suggests that the system warrants further investigation for use in a low temperature (100 deg to 120 C) Na-S secondary battery. A qualitative screening was undertaken at 120 C to determine the solubilities and stabilities of Na2S and Na2S2 in representatives of many classes of organic solvents. From the screening and quantitative studies, two classes of solvents were selected for work; amides and cyclic polyalcohols. Voltammetric and Na-S cell charge discharge studies of sulfide solutions in organic solvents (e.g., N, N-dimethylformamide) at 120 C suggested that the reversibilities of the reactions on Pt or high density graphite were moderately poor. However, the sulfur electrode was indeed reducible (and oxidizable) through the range of elemental sulfur to Na2S. Reactions and mechanisms are proposed for the oxidation reduction processes occurring at the sulfur electrode
Conductivities of the ionic complexes of two cyclic polyethers
The conductivities of the solid potassium thiocyanate complex of both dicyclohexyl-18-crown-6 and dibenzo-18-crown-6 were measured at 300K (27 C). Saturated aqueous potassium thiocyanate and graphite were used as ion-transporting and ion-blocking electrodes, respectively. The ionic conductivity predominated for both samples, but it was many orders of magnitude smaller than the value previously reported. The ionic conductivity of the dicyclohexyl complex (the better conductor) was 0.000003 ohm/cm. Crown complexes, in general, do not appear promising as potassium ion solid electrolytes contrary to claims in the patent literature
Search for solid conductors of Na(+) and K(+) ions: Five new conductors
Five conductors of three structure types were discovered which, as solids, can transport Na(+) or K(+) ions with conductivities of approximately .00001/(omega cm) at 300 K. These compounds are: (1) the pyrochlores NaTaWO6 and NaTa2O5F, both with an activation energy for conduction delta E of 21 kJ/mole; (2) the bodycentered cubic form of NaSbO3, with delta E = 42 kJ/mole; and (3) the niobates 2Na2O with 3Nb2O5 and 2K2O with 3Nb2O5, with the alkali ions probably in open layers of the incompletely determined structure; delta E = 17 kJ/mole. On the basis of approximately 40 structure types, some generalizations were made regarding the relation between structure and ionic transport
Reactions of NaCl with Gaseous SO3, SO2, and O2
Hot corrosion of gas turbine engine components involves deposits of Na2SO4 which are produced by reactions between NaCl and oxides of sulfur. For the present investigation, NaCl single crystals were exposed at 100 to 850 C to gaseous mixtures of SO3, SO2, and O2. The products formed during this exposure depend, primarily, on the temperatures. The four product films were: NaCl-SO3; Na2S2O7; Na2SO4; and NaCl-Na2SO4. The kinetics of the reactions were measured
Conductivity of boules of single crystal sodium beta-alumina
The ionic and electrochemical polarization characteristics of two boules of single crystal sodium beta-alumina (Na2O.8Al2O3), 2 cm in diameter, were investigated over the range of 25 to 300 C using 2- and 4-probe ac and dc techniques with reversible and ion-blocking electrodes. Textural (or internal) polarization at 27 C was present only in boule 1 which cleaved easily. Interfacial polarization, using solid sodium electrodes, was present at 27 C in the 2-probe conductivities for both boules. Cleaning with liquid sodium at 300 C reduced its magnitude, but some interfacial polarization was still present in the 2-probe conductivities for boule 2 below about 140 C. Above 140 C, with liquid sodium electrodes, the 2-probe conductivities, essentially polarization-free, were given by KT = 3300 exp(-3650/RT). The conductivity of boule 2 at 180 C remained essentially constant with increasing current density up to about 140 milliamps per square centimeter
- …