Recycled cellulose fiber reinforced plaster

This paper aims to develop recycled fiber reinforced cement plaster mortar with a good workability of fresh mixture, and insulation, mechanical and adhesive properties of the final hardened product for indoor application. The effect of the incorporation of different portions of three types of cellulose fibers from waste paper recycling into cement mortar (cement/sand ratio of 1:3) on its properties of workability, as well as other physical and mechanical parameters, was studied. The waste paper fiber (WPF) samples were characterized by their different cellulose contents, degree of polymerization, and residues from paper-making. The cement to waste paper fiber mass ratios (C/WPF) ranged from 500:1 to 3:1, and significantly influenced the consistency, bulk density, thermal conductivity, water absorption behavior, and compressive and flexural strength of the fiber-cement mortars. The workability tests of the fiber-cement mortars containing less than 2% WPF achieved optimal properties corresponding to plastic mortars (140-200 mm). The development of dry bulk density and thermal conductivity values of 28-day hardened fiber-cement mortars was favorable with a declining C/WPF ratio, while increasing the fiber content in cement mortars led to a worsening of the water absorption behavior and a lower mechanical performance of the mortars. These key findings were related to a higher porosity and weaker adhesion of fibers and cement particles at the matrix-fiber interface. The adhesion ability of fiber-cement plastering mortar based on WPF samples with the highest cellulose content as a fine filler and two types of mixed hydraulic binder (cement with finely ground granulated blast furnace slag and natural limestone) on commonly used substrates, such as brick and aerated concrete blocks, was also investigated. The adhesive strength testing of these hardened fiber-cement plaster mortars on both substrates revealed lime-cement mortar to be more suitable for fine plaster. The different behavior of fiber-cement containing finely ground slag manifested in a greater depth of the plaster layer failure, crack formation, and in greater damage to the cohesion between the substrate and mortar for the observed time.Web of Science1411art. no. 298

Characterization of cement composites based on recycled cellulosic waste paper fibres

Nowadays, there is paying an attention to the utilization of natural, renewable and biodegradable resources of raw materials of lignocellulosic character, residues from agricultural crops and wood processing as well as waste from papermaking industry in building composite materials preparing. Also recycled fibres coming from waste paper are considered as valuable material. The objective of this study is to utilize these recycled cellulosic fibres into cement composites and characterise their impact on resulting physical and mechanical properties of fresh and hardened cement composites. Manufactured cement composites contained 0.2%, 0.3% and 0.5% addition of cellulosic fibres. In fresh fibre cement mixtures reduction in workability with increasing amount of cellulose fibres was noticed. Density as well as compressive and flexural strength of 28 and 90 days hardened fibre cement composites was tested. Distribution of cellulosic fibres with 0.5% addition in hardened fibre cement composites was also observed. The results of density determination of 28 and 90 days hardened fibre cement composites showed reduction in their values related to weight lighter concretes. Compressive strengths of fibre cement composites have shown decreasing character with increasing added amount of cellulosic fibres into the mixture up to 0.5%. Maximal decrease in compressive strength values was observed in composites containing 0.5% of cellulosic fibres. However, obtained strength parameter values of hardened composites had satisfying results for their application in construction as nonload bearing building material.Web of Science8136736

Characterization of manmade and recycled cellulosic fibers for their application in building materials

The aim of this study was to characterize two types of cellulosic fibers obtained from bleached wood pulp and unbleached recycled waste paper with different cellulose content (from 47.4 percent up to 82 percent), to compare and to analyze the potential use of the recycled fibers for building application, such as plastering mortar. Changes in the chemical composition, cellulose crystallinity and degree of polymerization of the fibers were found. The recycled fibers of lower quality showed heterogeneity in the fiber sizes (width and length), and they had greater surface roughness in comparison to high purity wood pulp samples. The high purity fibers (cellulose content > 80.0 percent) had greater crystallinity and more homogeneous and smooth surfaces than the recycled fibers. The presence of calcite and kaolinite in all of the recycled cellulosic fibers samples was confirmed, whereas only one wood pulp sample contained calcite. The influence of the chemical composition was reflected in the fiber density values. Changes in the chemical composition and cellulose structure of the fibers affected the specific surface area, porosity and thermo physical properties of the fibers. More favorable values of thermal conductivity were reached for the recycled fibers than for the wood pulp samples. Testing the suitability of the recycled fibers with inorganic impurities originating from the paper-making processes for their use as fillers in plastering mortars (0.5 wt.% fiber content of the total weight of the filler and binder) confirmed their application by achieving a compressive strength value of 28 day-cured fiber-cement mortar required by the standard as well as by measured more favorable value of capillary water absorption coefficient.Web of Science7111145112

Study of thermal analysis of cellulose fibres using into building materials

This paper provides the investigation of thermal analysis of cellulose fibres which will be used into building materials as a partial filler replacement. Cellulosic fibres come from two various sources: bleached wood pulp and unbleached waste paper whereas these natural fibres have different cellulose contents and another manufacturing process. Natural fibres have been widely used as reinforcing fillers in composite materials in recent years. As a result, they are subjected to thermal degradation during composite processing. It is thus of practical significance to understand and predict the thermal decomposition process of natural fibres and the knowledge will help better design the composite process and estimate the influence on composite properties by the thermal decomposition of natural fibres. The results obtained from the thermal analysis of cellulosic fibres showed differences in their thermal decomposition and also differences in the weight loss due to their chemo-mechanical treatment, the presence of impurities and CaCO3 originating from filler in paper making