Hydriding, Oxidation, and Ductility Evaluation of Cr-Coated Zircaloy-4 Tubing

Accident-tolerant fuel concepts have been developed recently in diverse research programs. Recent research has shown clear advantages of Cr-coated Zr cladding over bare cladding tubes regarding oxidation behavior under the design basis loss-of-coolant accident condition. However, limited data are available about the hydriding behavior of the Cr coating. For that purpose, Cr-coated Zricaloy-4 tubes were tested to investigate the effects of hydriding, oxidation, and postquench ductility behavior on coated Zr cladding. A high-power impulse magnetron sputtering (HiPIMS) process was used to produce a high-density coating on the Zircaloy-4 tube surface. Coated and uncoated Zircaloy-4 tube specimens underwent one-sided hydriding in a tube furnace filled with pure hydrogen gas at 425 °C. The tubing specimen ends were sealed with Swagelok plugs before the hydriding runs. For uncoated specimens, H analysis of the hydrided specimens indicated that the H content increased as the test time and initial pressure increased. However, almost no change was observed for the coated specimens that were hydrided under the same test conditions. After one-sided hydriding, the hydrided coated and uncoated specimens were exposed to steam at high temperatures for two-sided oxidation studies to simulate accident conditions. The coated specimens showed a slower oxidation: oxygen pickup was 50% lower than the uncoated specimens tested under the same conditions. Ring compression testing was performed to evaluate the embrittlement behavior of the Cr-coated specimens after hydriding and oxidation. The results indicated that the HiPIMS coating provides excellent protection from hydriding and oxidation at high temperatures

Hydriding, Oxidation, and Ductility Evaluation of Cr-Coated Zircaloy-4 Tubing

Accident-tolerant fuel concepts have been developed recently in diverse research programs. Recent research has shown clear advantages of Cr-coated Zr cladding over bare cladding tubes regarding oxidation behavior under the design basis loss-of-coolant accident condition. However, limited data are available about the hydriding behavior of the Cr coating. For that purpose, Cr-coated Zricaloy-4 tubes were tested to investigate the effects of hydriding, oxidation, and postquench ductility behavior on coated Zr cladding. A high-power impulse magnetron sputtering (HiPIMS) process was used to produce a high-density coating on the Zircaloy-4 tube surface. Coated and uncoated Zircaloy-4 tube specimens underwent one-sided hydriding in a tube furnace filled with pure hydrogen gas at 425 °C. The tubing specimen ends were sealed with Swagelok plugs before the hydriding runs. For uncoated specimens, H analysis of the hydrided specimens indicated that the H content increased as the test time and initial pressure increased. However, almost no change was observed for the coated specimens that were hydrided under the same test conditions. After one-sided hydriding, the hydrided coated and uncoated specimens were exposed to steam at high temperatures for two-sided oxidation studies to simulate accident conditions. The coated specimens showed a slower oxidation: oxygen pickup was 50% lower than the uncoated specimens tested under the same conditions. Ring compression testing was performed to evaluate the embrittlement behavior of the Cr-coated specimens after hydriding and oxidation. The results indicated that the HiPIMS coating provides excellent protection from hydriding and oxidation at high temperatures

Burst and oxidation behavior of Cr-coated Zirlo during simulated LOCA testing

Cr-coated Zr-alloys are a near-term cladding concept to improve reactor safety during accident scenarios. Burst and steam oxidation behavior of bare and Cr-coated Zirlo claddings were examined under simulated loss-of-coolant accident conditions. The 4.4 µm coating had no substantial effect on ballooning or opening geometry but did increase burst temperatures at higher pressures. The coating reduced steam oxidation of the cladding compared to bare specimens, but in regions of high strain, the coating developed through-cracks allowing rapid underlying zirconia formation