Nuevo material compuesto de matriz geopolimérica activado con ceniza de cascarilla de arroz y KOH: Desempeño a alta temperatura

Geopolymers were produced using an environmentally friendly alkali activator (based on Rice Husk Ash and potassium hydroxide). Aluminosilicates particles, carbon and ceramic fibres were used as reinforcement materials. The effects of reinforcement materials on the flexural strength, linear-shrinkage, thermophysical properties and microstructure of the geopolymers at room and high temperature (1200 ÅãC) were studied. The results indicated that the toughness of the composites is increased 110.4% for geopolymer reinforced by ceramic fibres (G-AF) at room temperature. The presence of particles improved the flexural behaviour 265% for geopolymer reinforced by carbon fibres and particles after exposure to 1200 .C. Linear-shrinkage for geopolymer reinforced by ceramic fibres and particles and the geopolymer G-AF compared with reference sample (without fibres and particles) is improved by 27.88% and 7.88% respectively at 900 ÅãC. The geopolymer materials developed in this work are porous materials with low thermal conductivity and good mechanical properties with potential thermal insulation applications for building applications.Compuestos geopoliméricos fueron producidos usando un activador alcalino alternativo (basado en ceniza de cascarilla de arroz e hidróxido de potasio), partículas aluminosilicatos, fibras de carbono y cerámicas. Se estudió el efecto de fibras y partículas en la resistencia a la flexión, contracción lineal, propiedades termofísicas y microestructura de los geopolímeros a temperatura ambiente y 1200 °C. Los resultados indican que la tenacidad se incrementó 110.4% para el geopolímero reforzado con fibras cerámicas (G-AF) a temperatura ambiente. La presencia de partículas mejora el comportamiento a la flexión 265% para el geopolímero reforzado con fibras de carbono y partículas después de la exposición a 1200 °C. La contracción lineal para el geopolímero reforzado con fibras cerámicas y partículas y el geopolímero G-AF es mejorada 27.88% y 7.88% respectivamente a 900 ºC con respecto al material sin refuerzo. Los materiales geopoliméricos desarrollados en este estudio son materiales porosos de baja conductividad térmica y buenas propiedades mecánicas con potencial aplicación en la industria de la construcción como aislantes térmicos

Síntesis de polvos de BaTiO₃ por mecanoquímica

The barium titanato, BaTiO3, is one of the electronic ceramics with more history of technological application in the industry of the ceramic capacitores. The actual technological demands, and the high quality required for the electronic devices, have driven to new alternatives of prosecution of these materials and to optimize the traditional techniques of raw materials synthesis it prevails. An alternative synthesis is to use the mechanical energy to modify the physiochemical properties of the dispersed system and to favor the obtaining of powders of BaTiO3. In this work the results are indicated obtained when using mechanical activation, physicochemistry, in the obtaining of the BaTiO3. It has been analyzed the effect of the time of mill and the nature of the precursor of the titanium on the transformation of phases in the samples during the thermal treatment to that are subjected. X-ray diffraction, DRX, was used to study the phases evolution and infrared spectroscopy, FTIR, to determine the functional groups present in the samples.<br><br>El titanato de bario, BaTiO3, es uno de los cerámicos electrónicos con mayor historia de aplicación tecnológica en la industria de los capacitores cerámicos. Las demandas tecnológicas actuales, y la alta calidad requerida para los dispositivos electrónicos, han conducido a nuevas alternativas de procesamiento de estos materiales y a optimizar las técnicas tradicionales de síntesis de materia prima. Una alternativa de síntesis es utilizar la energía mecánica para modificar las propiedades fisicoquímicas del sistema disperso y favorecer la obtención de polvos de BaTiO3. En este trabajo se indican los resultados obtenidos al utilizar activación mecánica, mecanoquímica, en la obtención del BaTiO3. Se ha analizado el efecto del tiempo de molienda y la naturaleza del precursor del titanio sobre la transformación de fases que experimentan las muestras durante el tratamiento térmico a que son sometidas. Para estudiar la evolución de fases se utilizó difracción de rayos-x, DRX, y espectroscopia infrarroja, FTIR, para determinar los grupos funcionales presentes en las muestras

Calculo de Parámetros Electrónicos Para el Grafito Bernal

<abstract language="eng">Using ab-initio calculation, we have computed different electronic parameters associated with the transport coefficients of graphite Bernal. Software CRYSTAL¹ was used with a Pople standard STO- 21G* basis set. Different hamiltonians were tested, choosing a restricted Hartree-Fock one, because it generated the best qualitative results. All graphites studied present a valence bandwidth near 0.60 a.u., in agreement with the literature. In hexagonal Bernal graphite the splitting of the valence P band was accentuated, and E F = -0.00140 a.u. The surface Fermi is located around the HKH edge of the first Brillouin zone. In general such surfaces present a central electron orbit of maximal size in the plane, which diminish in size when the z component of the <IMG SRC="http:/img/fbpe/mr/v5n2/11049s6.gif">vector moves in KH direction. Integrating on the surface Fermi calculates the time relaxation parallel and the time relaxation perpendicular and finally we evaluate the parallel and perpendicular resistivity