Nitrogen-doped micropores binder-free carbon-sulphur composites as the cathode for long-life lithium-sulphur batteries

Nitrogen-doped micropores-contained carbon nanofibres (NMCNFs) were prepared by carbonizing ZIF-8 grown in liquid-phase along with electrospinning. When NMCNFs act as sulphur host materials in lithium–sulphur batteries, NMCNFs can retard the shuttle effect and dissolution of polysulfides through the synergic action of effective physical confinement to micropores and nitrogen surface chemical absorption. NMCNFs show a capacity up to 636 mAh g−1 after 500 cycles against Li anode

High-performance supercapacitors based on hierarchically porous carbons with a three-dimensional conductive network structure

Clews of polymer nanobelts (CsPNBs) have the advantages of inexpensive raw materials, simple synthesis and large output. Novel clews of carbon nanobelts (CsCNBs) have been successfully prepared by carbonizing CsPNBs and by KOH activation subsequently. From the optimized process, CsCNBs*4, with a specific surface area of 2291 m2 g−1 and a pore volume of up to 1.29 cm3 g−1, has been obtained. Fundamentally, the CsCNBs possess a three-dimensional conductive network structure, a hierarchically porous framework, and excellent hydrophilicity, which enable fast ion diffusion through channels and a large enough ion adsorption/desorption surface to improve electrochemical performance of supercapacitors. The product exhibits a high specific capacitance of 327.5 F g−1 at a current density of 0.5 A g−1 in a three-electrode system. The results also reveal a high-rate capacitance (72.2% capacitance retention at 500 mV s−1) and stable cycling lifetime (95% of initial capacitance after 15 000 cycles). Moreover, CsCNBs*4 provides a high energy density of 29.8 W h kg−1 at a power density of 345.4 W kg−1 in 1 M tetraethylammonium tetrafluoroborate/acetonitrile (TEABF4/AN) electrolyte. These inspiring results imply that this carbon material with a three-dimensional conductive network structure possesses excellent potential for energy storage

A universal strategy to prepare sulfur-containing polymer composites with desired morphologies for lithium−sulfur batteries

Lithium–sulfur (Li–S) batteries are probably the most promising candidates for the next-generation batteries owing to their high energy density. However, Li–S batteries face severe technical problems where the dissolution of intermediate polysulfides is the biggest problem because it leads to the degradation of the cathode and the lithium anode, and finally the fast capacity decay. Compared with the composites of elemental sulfur and other matrices, sulfur-containing polymers (SCPs) have strong chemical bonds to sulfur and therefore show low dissolution of polysulfides. Unfortunately, most SCPs have very low electron conductivity and their morphologies can hardly be controlled, which undoubtedly depress the battery performances of SCPs. To overcome these two weaknesses of SCPs, a new strategy was developed for preparing SCP composites with enhanced conductivity and desired morphologies. With this strategy, macroporous SCP composites were successfully prepared from hierarchical porous carbon. The composites displayed discharge/charge capacities up to 1218/1139, 949/922, and 796/785 mA h g–1 at the current rates of 5, 10, and 15 C, respectively. Considering the universality of this strategy and the numerous morphologies of carbon materials, this strategy opens many opportunities for making carbon/SCP composites with novel morphologies

Optimized synthesis of ultrahigh-surface-area and oxygen-doped carbon nanobelts for high cycle-stability lithium-sulfur batteries

Hierarchical clews of carbon nanobelts (CsCNBs) with ultrahigh specific surface area (2300 m2 g−1) and large pore volume (up to 1.29 cm3 g−1) has been successfully fabricated through carbonization and KOH activation of phenolic resin based nanobelts. The product possesses hierarchically porous structure, three-dimensional conductive network framework, and polar oxygen-rich groups, which are very befitting to load sulfur leading to excellent cycling stability of lithium-sulfur batteries. The composites of CsCNBs/sulfur exhibit an ultrahigh initial discharge capacity of 1245 mA h g−1 and ultralow capacity decay rate as low as 0.162% per cycle after 200 cycles at 0.1 C. Even at high current rate of 4 C, the cells still display a high initial discharge capacity (621 mA h g−1) and ultralow capacity decay rate (only 0.039% per cycle) after 1000 cycles. These encouraging results indicate that polar oxygen-containing functional groups are important for improving the electrochemical performance of carbons. The oxygen-doped carbon nanobelts have excellent energy storage potential in the field of energy storage

Preparation of water-soluble multi-walled carbon nanotubes by Ce(IV)-induced redox radical polymerization

Abstract Poly(acrylic acid), poly(N-isopropylacrylamide) and polyacrylamide functionalized MWNTs were prepared by Ce(IV)-induced redox radical polymerization. The reaction can be conducted in aqueous media at room temperature, and the polymer graft ratio increased with the increase of monomer feed ratio. MWNTs anchored with PAA on the surface are pH sensitive and exhibit a reversible assembly-deassembly response in aqueous solution, whereas those coated with PNIPAM are thermally sensitive. All the polymer-functionalized MWNTs are highly soluble in water to give robust stable black solutions. Such water-soluble MWNTs are promising for biological and biomedical applications

Ultrahigh-content nitrogen-decorated nanoporous carbon derived from metal organic frameworks and its application in supercapacitors

Single electric double-layer capacitors cannot meet the growing demand for energy due to their insufficient energy density. Generally speaking, the supercapacitors introduced with pseudo-capacitance by doping heteroatoms (N, O) in porous carbon materials can obtain much higher capacitance than electric double-layer capacitors. In view of above merits, in this study, nanoporous carbon materials with ultrahigh N enrichment (14.23 wt%) and high specific surface area (942 m2 g−1) by in situ introduction of N-doped MOF (ZTIF-1, Organic ligands 5-methyltetrazole/C2H4N4) were produced. It was found that as supercapacitors' electrode materials, these nanoporous carbons exhibit a capacitance as high as 272 F g-1 at 0.1 A g−1, and an excellent cycle life (almost no attenuation after 10,000 cycles.). Moreover, the symmetric supercapacitors were assembled to further investigate the actual capacitive performance, and the capacitance shows up to 154 F g-1 at 0.1 A g−1. Such excellent properties may be attributed to a combination of a high specific surface area, ultrahigh nitrogen content and hierarchically porous structure. The results shown in this study fully demonstrate that the nanoporous carbon materials containing ultrahigh nitrogen content can be used as a potential electrode material in supercapacitors

Facile synthesis of ultrahigh-surface-area hollow carbon nanospheres and their application in lithium-sulfur batteries

Hollow carbon nanospheres (HCNs) with specific surface areas up to 2949 m2 g−1 and pore volume up to 2.9 cm3 g−1 were successfully synthesized from polyaniline‐co‐polypyrrole hollow nanospheres by carbonization and CO2 activation. The cavity diameter and wall thickness of HCNs can be easily controlled by activation time. Owing to their large inner cavity and enclosed structure, HCNs are desirable carriers for encapsulating sulfur. To better understand the effects of pore characteristics and sulfur contents on the performances of lithium‐sulfur batteries, three composites of HCNs and sulfur are prepared and studied in detail. The composites of HCNs with moderate specific surface areas and suitable sulfur content present a better performance. The first discharge capacity of this composite reaches 1401 mAh g−1 at 0.2 C. Even after 200 cycles, the discharge capacity remains at 626 mAh g−1