Spin-1/2 Triangular Lattice with Orbital Degeneracy in a Metallic Oxide Ag2NiO2

A novel metallic and magnetic transition metal oxide Ag2NiO2 is studied by means of resistivity, magnetic susceptibility, specific heat and X-ray diffraction. The crystal structure is characterized by alternating stacking of a Ni3+O2 layer and a (Ag2)+ layer, the former realizing a spin-1/2 triangular lattice with eg orbital degeneracy and the latter providing itinerant electrons. It is found that the NiO2 layer exhibits orbital ordering at Ts = 260 K and antiferromagnetic spin ordering at TN = 56 K. Moreover, a moderately large mass enhancement is found for the itinerant electrons, suggesting a significant contribution from the nearly localized Ni 3d state to the Ag 5s state that forms a broad band.Comment: 9 pages, 5 figures, to be published in Rapid Communications, Phys. Rev.

Thermal Conductivity of the Pyrochlore Superconductor KOs2O6: Strong Electron Correlations and Fully Gapped Superconductivity

To elucidate the nature of the superconducting ground state of the geometrically frustrated pyrochlore KOs2O6 (Tc=9.6K), the thermal conductivity was measured down to low temperatures (~Tc/100). We found that the quasiparticle mean free path is strikingly enhanced below a transition at Tp=7.5K, indicating enormous electron inelastic scattering in the normal state. In a magnetic field the conduction at T ->0K is nearly constant up to ~0.4Hc2, in contrast with the rapid growth expected for superconductors with an anisotropic gap. This unambiguously indicates a fully gapped superconductivity, in contrast to the previous studies. These results highlight that KOs2O6 is unique among superconductors with strong electron correlations.Comment: 5 pages, 4 figures, accepted for publication in Phys. Rev. Let

Room temperature ferromagnetic behavior in the hollandite-type titanium oxide

A hollandite-type K(x)Ti(8)O(16) polycrystalline sample has been prepared and studied by magnetization, resistivity and x-ray photoelectron spectroscopy (XPS). Room temperature ferromagnetic behavior is observed in the magnetic hysteresis measurement. The sample shows a semiconductive temperature dependence in the resistivity measurement. Analysis of the Ti 2p(3/2) core-level XPS spectrum indicates that the titanium ions have a mixed valence of Ti(4+) and Ti(3+). In addition, the valence band spectrum reveals that the 3d electrons tend to localize on Ti(3+) ions in the hollandite-type TiO(2) lattice. Also, analysis of the valence band spectrum shows that the prepared sample is a wide-gap oxide with a band gap of 3.6 eV. These results indicate that the present hollandite-type K(x)Ti(8)O(16) sample can be classified as a TiO(2)-based wide-gap semiconductor with Curie temperature above room temperature. Room temperature ferromagnetism (RTFM) decreases in the sample prepared under a strong reducing gas atmosphere, accompanied with the decrease in the resistivity. The results imply that the localized 3d electrons are responsible for the RTFM of the K(x)Ti(8)O(16) sample

Activation volumes in CoPtCr-SiO2 perpendicular recording media

CoPtCr-SiO2 perpendicular recording media with varying levels of SiO2 were examined by two different methods to determine the activation volume. The first is based on the sweep-rate dependence of the remanence coercivity using Sharrock's equation. The second is based on the measurement of the fluctuation field from time-dependence data, determined using a magneto-optical Kerr effect (MOKE) magnetometer. The values of V-act measured at the coercivity for both methods are almost the same, with the fluctuation field and activation volumes increasing with the SiO2 content. The difference between V-act and the grain volume measured directly from bright-field TEM images decreases as the SiO2 content increases due to the reduction of intergranular exchange coupling. The experimental results indicate that values of V-act obtained from single- and double-layered media are consistent. It was also found that the coercivity and normalized hysteresis loop slope at coercivity varied with SiO2 content, with the coercivity peaking at 8 at % SiO2 (nearly 26 vol% SiO2)

Simplified expression of shielded MR head response for double-layerperpendicular medium

科研費報告書収録論文(課題番号:09355012・基盤研究(A)(2)・H9～H11/研究代表者:中村, 慶久/垂直ハード磁気ディスク装置を用いる超大容量ストレージシステムの研究

Discrete track media simulations for 600 Gb/in∧2 recording

Discrete track perpendicular recording media were simulated to determine the optimum conditions for achieving an areal density of 600 Gbits/in∧2. For a 90 nm track pitch the best performance was obtained form a medium with 60 nm land and 80 nm wide write pole. Comparisons with continuous media showed higher on- and off-track signal-to-noise ratio in some discrete track media, mainly due to the absence of erase band noise. Reducing the average grain size narrowed the differences between the two types of media, resulting in almost identical performance for an average grain size of 6 n

NMR Observation of Rattling Phonons in the Pyrochlore Superconductor KOs2O6

We report nuclear magnetic resonance studies on the beta-pyrochlore oxide superconductor KOs2O6. The nuclear relaxation at the K sites is entirely caused by fluctuations of electric field gradient, which we ascribe to highly anharmonic low frequency oscillation (rattling) of K ions. A phenomenological analysis shows a crossover from overdamped to underdamped behavior of the rattling phonons with decreasing temperature and its sudden sharpening below the superconducting transition temperature Tc. Absence of the Hebel-Slichter peak in the relaxation rate at the O sites below Tc also indicates strong electron-phonon coupling.Comment: 4 pages, 3 figure

Intergranular exchange pinning effects in perpendicular recordingmedia

科研費報告書収録論文(課題番号:09355012・基盤研究(A)(2)・H9～H11/研究代表者:中村, 慶久/垂直ハード磁気ディスク装置を用いる超大容量ストレージシステムの研究