Fiber Qualities of Pretreated Betung Bamboo (Dendrocalamusasper) by Mixed Culture of White-rot Fungi with Respect to Its Use for Pulp/paper

Previous research on anatomical structures of pretreated large (betung) bamboo (Dendrocalamusasper) using single culture of white-rot fungi has been investigated, which revealed that the pretreatment caused the decrease in the Runkel ratioas well as the coefficient rigidity and the increase in the flexibility ratio of their corresponding bamboo fibers. However, there is no study reported on the anatomical structure changes of them caused by pretreatment using mixed culture of white-rot fungi. This paper reports the results of the research on paper/pulp quality after different treatments. Pretreatment that used Trametes versicolor fungi and lasted for 45 days inflicted intensive fiber damages compared with those of untreated bamboo (control). Fresh and barkless large (betung) bamboo chips of 2 year's old, and 1.6 cm in length, were inoculated by 10% of mixed culture of white-rot fungi inoculums stock for 30 and 45 days in room temperature. There were four treatment groups of mixed culture, i.e T. versi color and P. ostreatus (TVPO); P. ostreatus and P. chrysosporium (POPC); P. chrysosporium and T.versi color (PCTV); and P.chrysosporium, T.versicolorand P.ostreatus (TVPCPO).After the inoculation period, the chips weremacerated into separate fibers using Scultze method to analyze the fiber dimension and its derived values. The fibers were then observed regarding their macro and microscopic structures by optical microscope. Mixed culture pretreatment of white-rot fungi accelerated improvement of fiber morphology and fiber derived value characteristics, except for Muhlsteph ratio. The fiber derived values oftreated bamboo tended to improve compared to those of untreated bamboo, there by requiring milder pulping conditions. Accordingly, the treated bamboo would indicatively produce a good quality pulp (grade I) based on FAO and LPHH (Forest Product Research Report) requirements. Co-culture treatment using P. chrysosporium and P. ostreatus for 45 days produced the best fiber dimension and its derived value properties. The fungi hypae colonized on the surface area of bamboo followed by mycelium penetration into substrate (bamboo-inner structure). The partial degradation caused by delignification indicatively attributed to the fungi activity was shown in the macroscopic images

The Characteristic Changes of Betung Bamboo (Dendrocalamus Asper) Pretreated by Fungal Pretreatment

The fungal pretreatment effect on chemical structural and morphological changes of Betung Bamboo was evaluated based on its biomass components after being cultivated by white rot fungi, Trametes versicolor. Betung bamboo powder (15 g) was exposed to liquid inoculum of white rot fungi and incubated at 270C for 15, 30 and 45 days. The treated samples were then characterized by FT-IR spectroscopy, X-Ray diffraction and SEM-EDS analyses. Cultivation for 30 days with 5 and 10% loadings retained greater selectivity compared to that of the other treatments. FTIR spectra demonstrated that the fungus affected the decreasing of functional group quantities without changing the functional groups. The decrease in intensity at wave number of 1246 cm-1 (guaiacyl of lignin) was greater than that at wave number of 1328 cm-1 (deformation combination of syringyl and xylan) after fungal treatment. X-ray analysis showed the pretreated samples had a higher crystallinity than the untreated ones which might be due to the cleavage of amorphous fractions of cellulose. The pretreated samples have more fragile than the untreated ones confirmed by SEM. Crystalline allomorph calculated by XRD analysis showed that fungus pretreatment for 30 days has transformed triclinic structure of cellulose to monoclinic structure

Fortifikasi Perekat Lateks Karet Alam-Stirena dengan Isosianat: Karakteristik dan Aplikasinya pada Kayu Lapis (Fortification Of Natural Rubber Lateks-Styrene With Isocyanate: Characteristics And Its Application For Plywood Adhesive)

This study was to evaluate the blending composition effects of natural rubber lateks-styrena (NRL-St)/isocyanate adhesive on their properties and sengon plywood quality. The blending mixture consists of 100/0, 90/10, 80/20, 70/30 and 0/100. Physico-chemical properties of these adhesives in therms of solid content (gravimetric method), pH (pH indicator paper), viscosity (Viscometer Brookfield), and contact angle (Motic software) were characterized. The bond strength (SNI 01-2704-1992) and formaldehyde emission (WKI bottle method) of plywood were also determined. Isocyanate fortification increased the solid content and viscosity of adhesive mixture, while pH was vice versa. The contact angle of adhesive mixture was about 450.Isocyanate fortification onto NRL-St improved plywood bond strength and significant improvement was happened on the composition of 80/20. Plywood hot pressing for 5 minutes increased the bond strength until isocyanate fortification 20%, while 10 minutes hot pressing also improved the bond strength on all of the composition adhesive. Only adhesive mixture of 70/30 that gave the lowest formaldehyde emission and fulfiled E1 standard (<0.1 ppm). Generally,the increasing of hot pressing time tended to decrease formaldehyde emmision of plywood. Bond strength of plywood fulfill SNI standard and E1 standard was isocyanate fortification of 30%

Kemungkinan Pemanfaatan Tandan Kosong Kelapa Sawit sebagai Bahan Baku Pembuatan Papan Serat Berkerapatan Sedang

Tandan kosong kelapa sawit (TKKS) merupakan limbah padat industri minyak kelapa sawit dengan potensi cukup besar (2,5 juta ton per tahun), yang dewasa ini hanya dibuang di tempat, atau dibakar sehingga menimbulkan pencemaran lingkungan. Salah satu USAha dalam mengatasi hal tersebut adalah memanfaatkannya untuk pembuatan papan serat berkerapatan sedang (MDF), sebagaimana dilakukan melalui percobaan skala laboratoris secara batch. Pengolahan pulp TKKS untuk MDF menggunakan proses semi-kimia soda panas terbuka, diikuti dengan perendaman dalam larutan alkali pada suhu kamar, dan sesudahnya diolah secara mekanis menjadi pulp. Sebelum pembentukan lembaran MDF, pada pulp TKKS ditambahkan bahan pengikat/perekat fenol formaldehida (PF). Pembentukan lembaran menggunakan proses basah.Hasil percobaan menunjukkan bahwa perendaman alkali menghasilkan pulp TKKS dengan diameter serat dan lumen lebih besar, dan dinding serat lebih tipis, dibandingkan dengan tanpa perlakuan rendaman. Selanjutnya perendaman alkali ternyata berinteraksi dengan penggunaan perekat PF, sehingga menghasilkan lembaran MDF dengan kerapatan dan sifat kekuatan lebih tinggi; dan penyerapan air dan pengembangan tebal yang lebih rendah, dibandingkan dengan tanpa perendaman. Bebrapa sifat MDF memenuhi persyaratan standard FAO, yaitu kerapatan adalah, modulus patah dan kekuatan reakat internal. Yang belum memenuhi adalah pengembangan tebal, penyerapan air, modulus elastisitas, dan kekuatan memegang sekurup. Diharapkan bisa diperbaiki dengan penggunaan bahan penolak air dan lebih banyak bahan perekat

Pemanfaatan Lignin Hasil Isolasi Dari Lindi Hitam Proses Biopulping Bambu Betung (Dendrocalamus Asper) Sebagai Media Selektif Jamur Pelapuk Putih

Lindi hitam merupakan limbah industri pulp yang belum termanfaatkan dengan baik. Pemanfaatan lignin dari lindi hitam selama ini biasanya hanya digunakan sebagai perekat. Dalam bidang mikrobiologi lignin dari lindi hitam dapat dimanfaatkan sebagai media selektif untuk isolasi jamur pelapuk putih. Tujuan penelitian ini adalah untuk mengetahui manfaat lignin hasil isolasi proses biopulping sebagai media selektif untuk jamur pelapuk putih. Lignin dari lindi hitam hasil biopulping bambu, dengan proses pemasakan soda dan kraft, diisolasi dengan penambahan asam. Padatan lignin kemudian dimurnikan menggunakan larutan dioksan dan ditimbang berat serta dianalisa secara kualitatif menggunakan spektrofotometer. Lignin hasil isolasi ditambahkan pada media agar untuk uji selektifitas jamur pelapuk putih Phanerochaete crysosporium dan Trametes versicolor. Pretreatment bambu pada 30 hari inkubasi menghasilkan lignin yang lebih tinggi jika dibandingkan dengan inkubasi selama 45 hari. Padatan lignin yang diperoleh dari hasil biopulping proses kraft juga lebih tinggi jika dibandingkan pada proses soda. Pengujian selektifitas jamur pada media alkali lignin menunjukkan bahwa fungi T. versicolor mensekresi enzim lebih cepat daripada P. chrysosporium

Pemanfaatan Lignin Hasil Isolasi Dari Lindi Hitam Proses Biopulping Bambu Betung (Dendrocalamus Asper) Sebagai Media Selektif Jamur Pelapuk Putih

Lindi hitam merupakan limbah industri pulp yang belum termanfaatkan dengan baik. Pemanfaatan lignin dari lindi hitam selama ini biasanya hanya digunakan sebagai perekat. Dalam bidang mikrobiologi lignin dari lindi hitam dapat dimanfaatkan sebagai media selektif untuk isolasi jamur pelapuk putih. Tujuan penelitian ini adalah untuk mengetahui manfaat lignin hasil isolasi proses biopulping sebagai media selektif untuk jamur pelapuk putih. Lignin dari lindi hitam hasil biopulping bambu, dengan proses pemasakan soda dan kraft, diisolasi dengan penambahan asam. Padatan lignin kemudian dimurnikan menggunakan larutan dioksan dan ditimbang berat serta dianalisa secara kualitatif menggunakan spektrofotometer. Lignin hasil isolasi ditambahkan pada media agar untuk uji selektifitas jamur pelapuk putih Phanerochaete crysosporium dan Trametes versicolor. Pretreatment bambu pada 30 hari inkubasi menghasilkan lignin yang lebih tinggi jika dibandingkan dengan inkubasi selama 45 hari. Padatan lignin yang diperoleh dari hasil biopulping proses kraft juga lebih tinggi jika dibandingkan pada proses soda. Pengujian selektifitas jamur pada media alkali lignin menunjukkan bahwa fungi T. versicolor mensekresi enzim lebih cepat daripada P. chrysosporium