10 research outputs found
Enhancing the UV/heat stability of LLDPE irrigation pipes via different stabilizer formulations
Herein different stabilizer formulations of linear low-density polyethylene (LLDPE) against UV- and heat-initiated degradation are described. The project aims at outdoor applications, such as irrigation piping and profiles, in the Middle East desert regions, where long-term weathering stability due to high temperatures and solar radiation is important. Two UV/heat formulations, without and with carbon black (CB) as pigment, were incorporated into LLDPE by melt compounding. Neat LLDPE and the stabilized compounds were exposed to accelerated UV and heat aging. Morphological analysis through scanning electron microscopy of the UV-exposed neat LLDPE showed more severe surface cracking compared to the CB-containing LLDPE, while all stabilized compounds did not show any surface degradation. Crack formation was less visible for the thermally aged samples. A significant decrease in molecular weight (MW) was observed for the neat UV-exposed LLDPE, while both unpigmented stabilized compounds showed little change in MW. Mechanical properties, thermal analysis, and carbonyl index results supported the morphological results, which confirmed that CB alone was slightly more effective in protecting the LLDPE against UV initiated degradation, but performed worse against thermal initiated degradation. UV1 and UV2 compounds were efficient against both UV- and heat-initiated degradation, with UV1 performing better for unpigmented compounds, and UV2 for the pigmented ones.This publication was made possible by the NPRP award (NPRP 9-161-1-030) from the Qatar National Research Fund (a member of The Qatar Foundation). We are also grateful to BASF and Sabo for supplying the additives at no cost. We further express our gratitude to Dr. Robert Brüll from Fraunhofer LBF, Darmstadt, Germany for doing the GPC analyses on our samples. The statements made herein are solely the responsibility of the author(s).Scopu
Solid state polymerization of pet/pc extruded blend: effect of reaction temperature on thermal, morphological and viscosity properties
Green Pathways for the Enzymatic Synthesis of Furan-Based Polyesters and Polyamides
The attention towards the utilization of sustainable feedstocks for polymer synthesis has grown exponentially in recent years. One of the spotlighted monomers derived from renewable resources is 2,5-furandicarboxylic acid (FDCA), one of the most promising bio-based monomers, due to its resemblance to petroleum-based terephthalic acid. Very interesting synthetic routes using this monomer have been reported in the last two decades. Combining the use of bio-based monomers and non-toxic chemicals via enzymatic polymerizations can lead to a robust and favorable approach towards a greener technology of bio-based polymer production. In this chapter, a brief introduction to FDCA-based monomers and enzymatic polymerizations is given, particularly focusing on furan-based polymers and their polymerization. In addition, an outline of the recent developments in the field of enzymatic polymerizations is discussed. </p
Artificial weathering and accelerated heat aging studies on low-density polyethylene (Ldpe) produced via autoclave and tubular process technologies
Accelerated (artificial) weathering and thermal aging tests were performed to investigate the effectiveness of different formulations in reducing the UV/heat degradation extent for two low-density polyethylene types (LDPE-A, LDPE-T). The two LDPEs differ in the type and extent of branching due to the applied polymerization process, with LDPE-A being produced in an autoclave and LDPE-T in a tubular reactor. Oligomeric or high molecular weight hindered amine light stabilizer (HALS), and two UV absorbers of benzophenone or hydroxyphenyl-triazine types were equally introduced to both the LDPE grades at a total content of 0.2 wt%. The surface morphology, as well as thermal and mechanical properties, were examined during aging showing a significant degradation extent for the neat samples. In particular, a mechanism of chain scission/branch-ing that resulted in crosslinking was assumed for the neat polyethylenes, after combining the decrease of molecular weight observed in the GPC analysis with the increase in Young's modulus after UV exposure. LDPE-T presented higher photo-ox-idation rates due to its comb-like branched structure and its higher possibility of intermolecular reactions between adjacent chains. Little or no degradation was observed for the stabilized grades, confirming the effectiveness of the selected UV/heat systems in improving the weathering resistance of the two LDPE grades and enhancing their useful lifetime.This publication was made possible by the NPRP award (NPRP 9-161-1-030) from the Qatar National Research Fund (a member of The Qatar Foundation). We are also grateful to BASF and Sabo for supplying the additives at no cost. The statements made herein are solely the responsibility of the author(s).Scopu
Development of value-added polyethylene grades with extended service lifetime: Weathering resistant flame retarded materials for outdoor applications
The current article deals with the development of different novel, tailor-made polyolefin formulations exhibiting both low flammability and high weathering resistance, so as to provide value-added polyethylene grades with extended service lifetime. Two low-density (LDPE) and one linear low-density (LLDPE) polyethylene grades were modified via melt compounding with an additive system comprising: (a) a nitrogen-phosphorous intumescent system for flame retardance and (b) a hindered amine light stabilizer and a benzophenone-type UV absorber for UV/heat stabilization, at a total loading of 30-35 wt%. The target was to reach V0 classification in UL94V flammability tests, while to a large extent maintaining the mechanical properties, such as, tensile and impact strength of the investigated polymers, thus ensuring that the additives do not interfere significantly with the material quality. Subsequently, the compounds were subjected to separate artificial UV and heat aging at 100 C for 1500 h; the formulations showed good flame retardance, even after prolonged artificial weathering, but there was an observable, although acceptable, decrease in the mechanical properties. Nevertheless, all the results show that the developed polyethylene compounds are very promising for outdoor applications, such as, irrigation piping and profiles, where long-term weathering stability is important, and where flame retardance is important for safety during storage.This publication was made possible by the NPRP award (NPRP 9-161-1-030) from the Qatar National Research Fund (a member of The Qatar Foundation). We are also grateful to BASF and Sabo for supplying the additives at no cost. We further express our gratitude to Dr. Mabrouk Ouederni from QAPCO for providing us with the three polyethylene grades. The statements made herein are solely the responsibility of the author(s).Scopu