Melt block copolymerization of epsilon-caprolactone and L-lactide

AB block copolymers of ε-caprolactone and (L)-lactide could be prepared by ring-opening polymerization in the melt at 110°C using stannous octoate as a catalyst and ethanol as an initiator provided ε-caprolactone was polymerized first. Ethanol initiated the polymerization of ε-caprolactone producing a polymer with ε-caprolactone derived hydroxyl end groups which after addition of L-lactide in the second step of the polymerization initiated the ring-opening copolymerization of L-lactide. The number-average molecular weights of the poly(ε-caprolactone) blocks varied fron 1.5 to 5.2 × 103, while those of the poly(L-lactide) blocks ranged from 17.4 to 49.7 × 103. The polydispersities of the block copolymers varied from 1.16 to 1.27. The number-average molecular weights of the polymers were controlled by the monomer/hydroxyl group ratio, and were independent on the monomer/ stannous octoate ratio within the range of experimental conditions studied. When L-lactide was polymerized first, followed by copolymerization of ε-caprolactone, random copolymers were obtained. The formation of random copolymers was attributed to the occurrence of transesterification reactions. These side reactions were caused by the ε-caprolactone derived hydroxyl end groups generated during the copolymerization of ε-caprolactone with prepolymers of L-lactide. The polymerization proceeds through an ester alcoholysis reaction mechanism, in which the stannous octoate activated ester groups of the monomers react with hydroxyl groups

Melt block copolymerization of epsilon-caprolactone and L-lactide

AB block copolymers of ε-caprolactone and (L)-lactide could be prepared by ring-opening polymerization in the melt at 110°C using stannous octoate as a catalyst and ethanol as an initiator provided ε-caprolactone was polymerized first. Ethanol initiated the polymerization of ε-caprolactone producing a polymer with ε-caprolactone derived hydroxyl end groups which after addition of L-lactide in the second step of the polymerization initiated the ring-opening copolymerization of L-lactide. The number-average molecular weights of the poly(ε-caprolactone) blocks varied fron 1.5 to 5.2 × 103, while those of the poly(L-lactide) blocks ranged from 17.4 to 49.7 × 103. The polydispersities of the block copolymers varied from 1.16 to 1.27. The number-average molecular weights of the polymers were controlled by the monomer/hydroxyl group ratio, and were independent on the monomer/ stannous octoate ratio within the range of experimental conditions studied. When L-lactide was polymerized first, followed by copolymerization of ε-caprolactone, random copolymers were obtained. The formation of random copolymers was attributed to the occurrence of transesterification reactions. These side reactions were caused by the ε-caprolactone derived hydroxyl end groups generated during the copolymerization of ε-caprolactone with prepolymers of L-lactide. The polymerization proceeds through an ester alcoholysis reaction mechanism, in which the stannous octoate activated ester groups of the monomers react with hydroxyl groups