Plasma Electrochemical Synthesis of Graphene-Phosphorene Composite and Its Catalytic Activity towards Hydrogen Evolution Reaction

For the first time, graphene-phosphorene structures were synthesized using the plasma-assisted electrochemical method. The catalytic activity of the composite obtained in the electrolytic plasma mode and its mixtures with few-layer graphene structures toward the hydrogen evolution reaction was studied. A substantial increase in the catalytic activity of the phosphorene structures towards the hydrogen evolution reaction was realized by mixing them with few-layer graphene structures. The catalyst demonstrates excellent activity towards the hydrogen evolution reaction in alkaline media with a low overpotential of 940 mV at a current density of 10 mA·cm−2 and a small Tafel slope of 130 mV dec−1

Plasma Electrochemical Synthesis of Graphene-Phosphorene Composite and Its Catalytic Activity towards Hydrogen Evolution Reaction

For the first time, graphene-phosphorene structures were synthesized using the plasma-assisted electrochemical method. The catalytic activity of the composite obtained in the electrolytic plasma mode and its mixtures with few-layer graphene structures toward the hydrogen evolution reaction was studied. A substantial increase in the catalytic activity of the phosphorene structures towards the hydrogen evolution reaction was realized by mixing them with few-layer graphene structures. The catalyst demonstrates excellent activity towards the hydrogen evolution reaction in alkaline media with a low overpotential of 940 mV at a current density of 10 mA·cm−2 and a small Tafel slope of 130 mV dec−1

A Facile Synthesis of Noble-Metal-Free Catalyst Based on Nitrogen Doped Graphene Oxide for Oxygen Reduction Reaction

A simple method for the mechanochemical synthesis of an effective metal-free electrocatalyst for the oxygen reduction reaction was demonstrated. A nitrogen-doped carbon material was obtained by grinding a mixture of graphene oxide and melamine in a planetary ball mill. The resulting material was characterized by XPS, EPR, and Raman and IR spectroscopy. The nitrogen concentration on the N-bmGO surface was 5.5 at.%. The nitrogen-enriched graphene material (NbmGO has half-wave potential of −0.175/−0.09 V and was shown to possess high activity as an electrocatalyst for oxygen reduction reaction. The electrocatalytic activity of NbmGO can be associated with a high concentration of active sites for the adsorption of oxygen molecules on its surface. The high current retention (93% for 12 h) after continuous polarization demonstrates the excellent long-term stability of NbmGO