Efficiency of defects formation in spinel under high energy electron and gamma beam irradiation

There were provided the comparative investigations of the efficiency of optical absorption centers formation in magnesium aluminates spinel (single crystals and ceramics) at the influence of high energy gamma or electron beams. It was revealed that at gamma irradiation in the single crystals and ceramics the most probably the hole centers are formed which were created primarily at growth defects: cationic vacancies and anti-site defects. After electron irradiation of different fluences in absorption spectra there were observed bands related to hole centers (defects in the cationic sub-lattice) which practically does not change, while the concentration of electron centers (defects in the anion sub-lattice) grows proportionally to the electron fluence.Виконано порiвняльнi дослiдження ефективностi створення оптичних центрiв поглинання в магнiй- алюмiнiєвiй шпiнелi (монокристалiв та керамiки) пiд дiєю високоенергетичних гама-квантiв та електронiв. Показано, що гама-опромiнення монокристалiв та керамiки призводить переважно до створення дiркових центрiв, якi формуються на ростових дефектах: катiонних вакансiях та дефектах анти-структури. Пiсля електронного опромiнення рiзними флюенсами в спектрах поглинання спостерiгаються смуги, зумовленi дiрковими центрами (дефекти в катiоннiй пiдгратцi), концентрацiя яких практично не змiнилась, в той час як концентрацiя електронних центрiв (дефекти в анiоннiй пiдгратцi) росте пропорцiйно флюєнсу електронiв.Проведены сравнительные исследования эффективности образования оптических центров поглощения в магний-алюминиевой шпинели (монокристаллов и керамики) при воздействии высокоэнергетических гамма-квантов и электронов. Установлено, что гамма облучение монокристаллов и керамики приводит преимущественно к образованию дырочных центров, которые формируются на ростовых дефектах: катионных вакансиях и дефектах антиструктуры. После электронного облучения до различных флюенсов в спектрах поглощения наблюдаются полосы, обусловленные дырочными центрами (дефекты в катионной подрешетке), концентрация которых практически не изменилась, в то время как концентрация электронных центров (дефектов в анионной подрешетке) растет пропорционально флюенсу электронов

Defects formation in spinel crystals under electron and gamma beam irradiation

There were investigated the optical absorption centers formation in magnesium aluminate spinel crystals at the action of high energy gamma or electron beams. It was revealed that at gamma irradiation the most probably the hole centers are formed to compare with that in electron irradiation. At electron beam irradiation the temperature of sample was raised which leads to thermal annealing of unstable radiation-induced centers.Проведено дослідження утворення оптичних центрів поглинання в монокристалах магнійалюмінієвої шпінелі під дією високоенергетичних гама- або електронних пучків. Установлено, що гама-опромінення призводить переважно до утворення діркових центрів. При електронному опроміненні настає підвищення температури зразка, що призводить до термічного відпалу нестабільних радіаційно-наведених центрів.Проведены исследования образования оптических центров поглощения в монокристаллах магний-алюминиевой шпинели при воздействии высокоэнергетических гамма- или электронных пучков. Установлено, что гамма-облучение приводит преимущественно к образованию дырочных центров. При электронном облучении происходит повышение температуры образца, что приводит к термическому отжигу нестабильных радиационно-наведенных центров