Study of the pore structure of ceramics prepared by the slip casting method

The porosity of the slip cast Si3N4 is similar to that of pressed Si3N4 formed at 2500 kg/sq cm. The porosity of cast Si oxynitride is equivalent to that of samples stressed at 10,000 kg/sq cm. Crucibles formed from these materials by slip casting have high thermal shock and corrosion resistance

Определение возраста человека по образцам крови на основании анализа метилирования CpG-динуклеотидов

Based on the bioinformatic and statistical analysis of the GEO-projects to determine the genome-wide profile of human DNA methylation, a list of 27 CpG dinucleotides with a high predictive potential was formed to create models for prediction of the human age from blood samples. The methylation level was determined for 245 samples of individuals from the Republic of Belarus. The correlation coefficients R were calculated, and the mathematical models for determining the age of an individual were constructed. The average accuracy value of the age prediction from blood samples using 12 CpG-dinucleotides was 3.4 years (for men – 3.3, for women – 3.5). The results obtained will be used as a basis for development of calculators for predicting the age of an individual based on the biological traces for forensic experts.На основании биоинформатического и статистического анализа GEO-проектов по определению полногеномного профиля метилирования ДНК человека сформирован перечень из 27 CpG-динуклеотидов с высоким прогностическим потенциалом для создания моделей предсказания возраста человека по образцам крови. Определен уровень метилирования для 245 образцов индивидов из Республики Беларусь, рассчитаны коэффициенты корреляции R и построены математические модели определения возраста человека. Среднее значение точности предсказания возраста по образцам крови с использованием 12 CpG-динуклеотидов составило 3,4 года (для мужчин – 3,3, для женщин – 3,5). Полученные результаты будут положены в основу разработки калькуляторов предсказания возраста индивида по биологическим следам для экспертов-криминалистов

СИНТЕЗ И СВОЙСТВА БИОАКТИВНЫХ ОРГАНОМИНЕРАЛЬНЫХ КОМПОЗИТОВ ДЛЯ ЗАЩИТЫ КЕРАМИЧЕСКИХ ФИЛЬТРУЮЩИХ МАТЕРИАЛОВ

The method of obtaining hybrid organic biocidal structures through the interaction of the guanidine base with alumophosphates and copper hydroxy carbonate has been described. It is established that the reaction products consist of tripolyphosphates and pyrophosphates of aluminum forming ionic bonds with polyhexamethylene guanidine ions and copper (II). It is shown that when applied to the surface of a ceramic filter element at a temperature of 170 °C, a biocidal composite is fixed on them, on average, amounting to 50.0 wt. % of a product that provides the protection of filters from biofouling.Описан метод получения «гибридных» органоминеральных биоцидных структур путем взаимодействия основания полигексаметиленгуанидина с алюмофосфатами и гидрокарбонатом меди. Установлено, что продукты реакции состоят из триполифосфатов и пирофосфатов алюминия, образующих ионные связи с полигексаметиленгуанидином и ионами меди (II). Показано, что при нанесении на поверхности керамических фильтроэлементов при температуре 170 °С биоцидного композита на них закрепляется в среднем 50,0 масс. % продукта, обеспечивающего защиту фильтров от биообрастания