Symmetry and its application in metal additive manufacturing (MAM)

Additive manufacturing (AM) is proving to be a promising new and economical technique for the manufacture of metal parts. This technique basically consists of depositing material in a more or less precise way until a solid is built. This stage of material deposition allows the acquisition of a part with a quasi-final geometry (considered a Near Net Shape process) with a very high raw material utilization rate. There is a wide variety of different manufacturing techniques for the production of components in metallic materials. Although significant research work has been carried out in recent years, resulting in the wide dissemination of results and presentation of reviews on the subject, this paper seeks to cover the applications of symmetry, and its techniques and principles, to the additive manufacturing of metals.The authors are grateful to the Basque Government for funding the EDISON project, ELKARTEK 2022 (KK-2022/00070)

Wall fabrication by direct energy deposition (DED) combining mild steel (ER70) and stainless steel (SS 316L): microstructure and mechanical properties

Direct energy deposition is gaining much visibility in research as one of the most adaptable additive manufacturing technologies for industry due to its ease of application and high deposition rates. The possibility of combining these materials to obtain parts with variable mechanical properties is an important task to be studied. The combination of two types of steel, mild steel ER70-6 and stainless steel SS 316L, for the fabrication of a wall by direct energy deposition was studied for this paper. The separate fabrication of these two materials was studied for the microstructurally flawless fabrication of bimetallic walls. As a result of the application of superimposed and overlapped strategies, two walls were fabricated and the microstructure, mechanical properties and hardness of the resulting walls are analyzed. The walls obtained with both strategies present dissimilar regions; the hardness where the most present material is ER70-6 is around 380 HV, and for SS 316L, it is around 180 HV. The average values of ultimate tensile strength (UTS) are 869 and 628 MPa, yield strength (YS) are 584 and 389 MPa and elongation at break are 20% and 36%, respectively, in the cases where we have more ER70-6 in the sample than SS 316L. This indicates an important relationship between the distribution of the materials and their mechanical behavior.The authors are grateful to the Basque Government for funding the ANDREA project ELKARTEK and the EDISON project, ELKARTEK 2022 (KK-2022/00070)