Uncatalyzed synthesis, thermal and mechanical properties of polyurethanes based on poly(epsilon-caprolactone) and 1,4-butane diisocyanate with uniform hard segment

Polyurethanes based on poly(epsilon-caprolactone) (PCL) (750-2800g/mol) and 1,4-butane diisocyanate (BDI) with different soft segment lengths and constant uniform hard segment length were synthesized in absence of catalysts for the production of a degradable meniscus scaffold. First the polyesterdiols were endcapped with BDI yielding a macrodiisocyanate with a minimal amount of side reactions and a functionality of 2.0. Subsequently, the macrodiisocyanates were extended with 1,4-butanediol in order to obtain the corresponding polyurethane. The polyurethanes had molecular weights between 78 and 160 kg/mol.Above molar masses of 1900 g/mol of the polyesterdiol crystalline PCL was found while the hard segment showed an increase in melting point from 78 to 122 degreesC with increasing hard segment content. It was estimated that the percentage crystallinity of the hard segment varied between 92 and 26%. The Young's modulus varied between 30 and 264 MPa, the strain at break varied between 870 and 1200% and tear strengths varied between 97 and 237 kJ/m(2). (C) 2004 Elsevier Ltd. All rights reserved.</p

Changes in articular cartilage after meniscectomy and meniscus replacement using a biodegradable porous polymer implant

Purpose: To evaluate the long-term effects of implantation of a biodegradable polymer meniscus implant on articular cartilage degeneration and compare this to articular cartilage degeneration after meniscectomy. Methods: Porous polymer polycaprolacton-based polyurethane meniscus implants were implanted for 6 or 24 months in the lateral compartment of Beagle dog knees. Contralateral knees were meniscectomized, or left intact and served as controls. Articular cartilage degeneration was evaluated in detail using India ink staining, routine histology, immunochemistry for denatured (Col2-¾M) and cleaved (Col2-¾Cshort) type II collagen, Mankin’s grading system, and cartilage thickness measurements. Results: Histologically, fibrillation and substantial immunohistochemical staining for both denatured and cleaved type II collagen were found in all three treatment groups. The cartilage of the three groups showed identical degradation patterns. In the 24 months implant group, degradation appeared to be more severe when compared to the 6 months implant group and meniscectomy group. Significantly more cartilage damage (India ink staining, Mankin’s grading system, and cartilage thickness measurements) was found in the 24 months implant group compared to the 6 months implant group and meniscectomy group. Conclusion: Degradation of the cartilage matrix was the result of both mechanical overloading as well as localized cell-mediated degradation. The degeneration patterns were highly variable between animals. Clinical application of a porous polymer implant for total meniscus replacement is not supported by this study.

Acromioclavicular joint reconstruction with coracoacromial ligament transfer using the docking technique

<p>Abstract</p> <p>Background</p> <p>Symptomatic Acromioclavicular (AC) dislocations have historically been surgically treated with Coracoclavicular (CC) ligament reconstruction with transfer of the Coracoacromial (CA) ligament. Tensioning the CA ligament is the key to success.</p> <p>Methods</p> <p>Seventeen patients with chronic, symptomatic Type III AC joint or acute Type IV and V injuries were treated surgically. The distal clavicle was resected and stabilized with CC ligament reconstruction using the CA ligament. The CA ligament was passed into the medullary canal and tensioned, using a modified 'docking' technique. Average follow-up was 29 months (range 12–57).</p> <p>Results</p> <p>Postoperative ASES and pain significantly improved in all patients (p = 0.001). Radiographically, 16 (94%) maintained reduction, and only 1 (6%) had a recurrent dislocation when he returned to karate 3 months postoperatively. His ultimate clinical outcome was excellent.</p> <p>Conclusion</p> <p>The docking procedure allows for tensioning of the transferred CA ligament and healing of the ligament in an intramedullary bone tunnel. Excellent clinical results were achieved, decreasing the risk of recurrent distal clavicle instability.</p

Clinical knee findings in floor layers with focus on meniscal status

<p>Abstract</p> <p>Background</p> <p>The aim of this study was to examine the prevalence of self-reported and clinical knee morbidity among floor layers compared to a group of graphic designers, with special attention to meniscal status.</p> <p>Methods</p> <p>We obtained information about knee complaints by questionnaire and conducted a bilateral clinical and radiographic knee examination in 134 male floor layers and 120 male graphic designers. After the exclusion of subjects with reports of earlier knee injuries the odds ratio (OR) with 95% confidence intervals (CI) of knee complaints and clinical findings were computed among floor layers compared to graphic designers, using logistic regression. Estimates were adjusted for effects of body mass index, age and knee straining sports. Using radiographic evaluations, we conducted side-specific sensitivity analyses regarding clinical signs of meniscal lesions after the exclusion of participants with tibiofemoral (TF) osteoarthritis (OA).</p> <p>Results</p> <p>Reports of knee pain (OR = 2.7, 95% CI = 1.5–4.6), pain during stair walking (OR = 2.2, 95% CI = 1.3–3.9) and symptoms of catching of the knee joint (OR = 2.9, 95% CI = 1.4–5.7) were more prevalent among floor layers compared to graphic designers. Additionally, significant more floor layers than graphic designers had clinical signs suggesting possible meniscal lesions: a positive McMurray test (OR = 2.4, 95% CI = 1.1–5.0) and TF joint line tenderness (OR = 5.4, 95% CI = 2.4–12.0). Excluding floor layers (n = 22) and graphic designers (n = 15) with radiographic TF OA did not alter this trend between the two study groups: a positive McMurray test (OR = 2.2, 95% CI = 1.0–4.9), TF joint line tenderness (OR = 5.0, 95% CI = 2.0–12.5).</p> <p>Conclusion</p> <p>Results indicate that floor layers have a high prevalence of both self-reported and clinical knee morbidity. Clinical knee findings suggesting possible meniscal lesions were significant more prevalent among floor layers compared to a group of low-level exposed graphic designers and an association with occupational kneeling could be possible. However, causality cannot be confirmed due to the cross-sectional study design.</p

Clinical knee findings in floor layers with focus on meniscal status

<p>Abstract</p> <p>Background</p> <p>The aim of this study was to examine the prevalence of self-reported and clinical knee morbidity among floor layers compared to a group of graphic designers, with special attention to meniscal status.</p> <p>Methods</p> <p>We obtained information about knee complaints by questionnaire and conducted a bilateral clinical and radiographic knee examination in 134 male floor layers and 120 male graphic designers. After the exclusion of subjects with reports of earlier knee injuries the odds ratio (OR) with 95% confidence intervals (CI) of knee complaints and clinical findings were computed among floor layers compared to graphic designers, using logistic regression. Estimates were adjusted for effects of body mass index, age and knee straining sports. Using radiographic evaluations, we conducted side-specific sensitivity analyses regarding clinical signs of meniscal lesions after the exclusion of participants with tibiofemoral (TF) osteoarthritis (OA).</p> <p>Results</p> <p>Reports of knee pain (OR = 2.7, 95% CI = 1.5–4.6), pain during stair walking (OR = 2.2, 95% CI = 1.3–3.9) and symptoms of catching of the knee joint (OR = 2.9, 95% CI = 1.4–5.7) were more prevalent among floor layers compared to graphic designers. Additionally, significant more floor layers than graphic designers had clinical signs suggesting possible meniscal lesions: a positive McMurray test (OR = 2.4, 95% CI = 1.1–5.0) and TF joint line tenderness (OR = 5.4, 95% CI = 2.4–12.0). Excluding floor layers (n = 22) and graphic designers (n = 15) with radiographic TF OA did not alter this trend between the two study groups: a positive McMurray test (OR = 2.2, 95% CI = 1.0–4.9), TF joint line tenderness (OR = 5.0, 95% CI = 2.0–12.5).</p> <p>Conclusion</p> <p>Results indicate that floor layers have a high prevalence of both self-reported and clinical knee morbidity. Clinical knee findings suggesting possible meniscal lesions were significant more prevalent among floor layers compared to a group of low-level exposed graphic designers and an association with occupational kneeling could be possible. However, causality cannot be confirmed due to the cross-sectional study design.</p

Tissue ingrowth polymers and degradation of two biodegradable porous with different porosities and pore sizes

Commonly, spontaneous repair of lesions in the avascular zone of the knee meniscus does not occur. By implanting a porous polymer scaffold in a knee meniscus defect, the lesion is connected with the abundantly vascularized knee capsule and heating can be realized. Ingrowth of fibrovascular tissue and thus healing capacity depended on porosity, pore sizes and compression modulus of the implant, To study the lesion healing potential, two series of porous polyurethanes based on 50/50 epsilon-caprolactone/L-lactide with different porosities and pore sizes were implanted subcutaneously in rats. Also, in vitro degradation of the polymer was evaluated. The porous polymers with the higher porosity, more interconnected macropores, and interconnecting micropores of at least 30 mum showed complete ingrowth of tissue before degradation had started. In implants with the lower macro-porosity and micropores of 10-15 mum degradation of the polymer occurred before ingrowth was completed. Directly after implantation and later during degradation of the polymer, PMN cells infiltrated the implant. In between these phases the foreign body reaction remained restricted to macrophages and giant cells. We can conclude that both foams seemed not suited for implantation in meniscal reconstruction while either full ingrowth of tissue was not realized before polymer degradation started or the compression modulus was too low, Therefore, foams must be developed with a higher compression modulus and more connections with sufficient diameter between the macropores. (C) 2002 Elsevier Science Ltd. All rights reserved