A hybrid material assembled by anthocyanins from acai fruit intercalated between niobium lamellar oxide

Organic-inorganic hybrid materials can be prepared dispersing organic species into well-defined inorganic nanoblocks. This paper describes the immobilization of natural dyes from the extract of the Brazilian acai-fruit into two types of layered hexaniobate precursors derived from H(2)K(2)Nb(6)O(17): (i) colloidal dispersion of niobate exfoliated nanoparticles and (ii) niobate pre-intercalated with tetraethylammonium cations (TEA(+)). the restacking of exfoliated particles in the presence of acai anthocyanins promotes their intercalation and produces stacked layers showing large basal spacing (ca. 50 angstrom). the TEA(+) pre-intercalated niobate provides particles with lower content of dye species than the exfoliated precursor but with higher degree of organization and regularity according to X-ray diffraction data and images obtained by electron microscopies. Vibrational (FTIR and Raman) and (13)C NMR spectroscopies indicate the presence of flavylium cations in the hybrid materials and spectral profiles characteristic of glycosylated anthocyanidins. According to thermal analysis results, the purplish hybrids materials are more stable than the free acai-dyes. One hybrid sample was heated under air up to 170 degrees C and maintained at this temperature for 240 min. No weight loss events were observed and the sample retained its original color, indicating that the intercalation of anthocyanin into hexaniobate increases its thermal stability. Considering the structural, chemical, optical and thermal properties of the synthesized hybrid materials, they might be good candidates to be investigated for future specialized applications.Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)Instituto do Milenio de Materiais ComplexosUniv São Paulo, Inst Quim, BR-05508000 São Paulo, BrazilUniversidade Federal de São Paulo, Dept Ciencias Exatas & Terra, BR-09972270 Diadema, SP, BrazilUniv Clermont Ferrand, Lab Mat Inorgan, CNRS, UMR 6002, F-63177 Clermont Ferrand, FranceUniversidade Federal de São Paulo, Dept Ciencias Exatas & Terra, BR-09972270 Diadema, SP, BrazilCAPES: 557/07FAPESP: 06/516510Web of Scienc

A hybrid material assembled by anthocyanins from acai fruit intercalated between niobium lamellar oxide

Organic-inorganic hybrid materials can be prepared dispersing organic species into well-defined inorganic nanoblocks. This paper describes the immobilization of natural dyes from the extract of the Brazilian acai-fruit into two types of layered hexaniobate precursors derived from H(2)K(2)Nb(6)O(17): (i) colloidal dispersion of niobate exfoliated nanoparticles and (ii) niobate pre-intercalated with tetraethylammonium cations (TEA(+)). The restacking of exfoliated particles in the presence of acai anthocyanins promotes their intercalation and produces stacked layers showing large basal spacing (ca. 50 angstrom). The TEA(+) pre-intercalated niobate provides particles with lower content of dye species than the exfoliated precursor but with higher degree of organization and regularity according to X-ray diffraction data and images obtained by electron microscopies. Vibrational (FTIR and Raman) and (13)C NMR spectroscopies indicate the presence of flavylium cations in the hybrid materials and spectral profiles characteristic of glycosylated anthocyanidins. According to thermal analysis results, the purplish hybrids materials are more stable than the free acai-dyes. One hybrid sample was heated under air up to 170 degrees C and maintained at this temperature for 240 min. No weight loss events were observed and the sample retained its original color, indicating that the intercalation of anthocyanin into hexaniobate increases its thermal stability. Considering the structural, chemical, optical and thermal properties of the synthesized hybrid materials, they might be good candidates to be investigated for future specialized applications.Brazilian agencies FAPESPCNPqCAPES/COFECUB[557/07]Instituto do Milenio de Materiais ComplexosFAPESP[06/516510