7 research outputs found
Thermal Structural Transitions and Carbon Dioxide Adsorption Properties of Zeolitic Imidazolate Framework‑7 (ZIF-7)
As a subset of the
metal–organic frameworks, zeolitic imidazolate
frameworks (ZIFs) have potential use in practical separations as a
result of flexible yet reliable control over their pore sizes along
with their chemical and thermal stabilities. Among many ZIF materials,
we explored the effect of thermal treatments on the ZIF-7 structure,
known for its promising characteristics toward H<sub>2</sub> separations;
the pore sizes of ZIF-7 (0.29 nm) are desirable for molecular sieving,
favoring H<sub>2</sub> (0.289 nm) over CO<sub>2</sub> (0.33 nm). Although
thermogravimetric analysis indicated that ZIF-7 is thermally stabile
up to ∼400 °C, the structural transition of ZIF-7 to an
intermediate phase (as indicated by X-ray analysis) was observed under
air as guest molecules were removed. The transition was further continued
at higher temperatures, eventually leading toward the zinc oxide phase.
Three types of ZIF-7 with differing shapes and sizes (∼100
nm spherical, ∼400 nm rhombic-dodecahedral, and ∼1300
nm rod-shaped) were employed to elucidate (1) thermal structural transitions
while considering kinetically relevant processes and (2) discrepancies
in the N<sub>2</sub> physisorption and CO<sub>2</sub> adsorption isotherms.
The largest rod-shaped ZIF-7 particles showed a delayed thermal structural
transition toward the stable zinc oxide phase. The CO<sub>2</sub> adsorption
behaviors of the three ZIF-7s, despite their identical crystal structures,
suggested minute differences in the pore structures; in particular,
the smaller spherical ZIF-7 particles provided reversible CO<sub>2</sub> adsorption isotherms at ∼30–75 °C, a typical
temperature range of flue gases from coal-fired power plants, in contrast
to the larger rhombic-dodecahedral and rod-shaped ZIF-7 particles,
which exhibited hysteretic CO<sub>2</sub> adsorption/desorption behavior
Soluble ICAM-5 affects an increase in GluA1 surface staining along dendrites in particular.
<p>Figure 4 shows data from live cell surface staining for GluA1 in control and ICAM-5 treated hippocampal neurons at 14 and 21 DIV. Indicated cultures were treated with 2.5 µg/ml soluble ICAM-5 and surface staining performed 1 hour later. Representative images are shown in A and C, while quantitative data is shown in B and D. The mean and standard error for percent control values were 100 +/- 8.8, n=21 for the DIV 14 control group; 187.5 +/- 16.4, n=16 for the DIV 14 ICAM-5 group; 100 +/- 5.8, n=25 for the DIV 21 control group; and 146.3 +/- 7.9, n=25 for the DIV 21 ICAM-5 group. Differences in GluA1 staining between control and ICAM-5 treated cultures are significant at <i>p</i>< 0.01 (*) at both 14 and 21 DIV.</p
Schematic representation of MMP-dependent ICAM-5 signaling at the synapse.
<p>In figure 6 we show a hypothetical model in which MMPs are rapidly released from preformed peri-synaptic stores to cleave ICAM-5 (green and lavender) at a membrane proximal site. The released N terminal fragment can bind unengaged integrins (red ovals) to stimulate intracellular signaling cascades leading to increased phosphorylation and membrane insertion of GluA1 subunits. Following ectodomain shedding, the C terminal fragment of ICAM-5 could undergo additional processing followed by internalization and degradation. It is worth noting that following MMP or ADAM mediated shedding, select CAMs are further processed by intramembranous proteolysis. ICDs thus generated may be degraded or, in some cases, influence gene transcription.</p
The ICAM-5 ectodomain stimulates an increase in surface levels of the glutamate receptor subunit GluA1.
<p>Rat hippocampal neurons were unstimulated (control) or stimulated for 60 min. with 1 µg/ml of the ICAM-5 ectodomain (R & D Systems). Surface proteins were then biotinylated, and biotinylated proteins pulled down to be analyzed by Western blot. As can be appreciated, ICAM-5 was associated with an increase in surface GluA1 (A). Blots from separate experiments are shown. Densitometric analysis showing the fold increase in GluA1 band intensity in ICAM-5 versus control treated cultures in shown in (B). The mean and standard error for the fold increase from 6 replicate experiments is shown, and the difference between control and ICAM-5 groups is significant at <i>p</i> < 0.1 (*<i>p</i>=0.05). A representative blot for GluA2 in surface protein preparations is shown in (C), and densitometric analysis showing the fold change in GluA2 band intensity from 3 replicate experiments follows in (D). The mean and standard error for the fold change from 3 replicate experiments is shown, and the difference between control and ICAM-5 groups is not significant (<i>p</i>= 0.6).</p
The ICAM-5 ectodomain affects an increase in mini excitatory post synaptic current (mEPSC) frequency.
<p>Stimulation of rat hippocampal neurons with 1 µg/ml ICAM-5 ectodomain (60 min. pretreatment) is associated with an increase in mEPSC frequency. In these experiments, 1,468 events from 11 control cells and 2353 events from 16 ICAM-5 stimulated cells were evaluated using standard techniques [74]. Representative tracings are shown in (A) while the average mEPSC frequency is shown in (B) and amplitude in (C). The difference between mEPSC frequency in control and ICAM treated neurons was significant (*<i>p</i> < 0.05, Student’s <i>t</i> test).</p
Phosphorylation of GluA1 at serine-845 is increased by soluble ICAM-5.
<p>Rat hippocampal neurons were unstimulated (control) or treated for 60 min. with 1 µg/ml of soluble ICAM-5 and lysates tested by Western blot for phospho-serine 845 GluA1. A representative blot is shown in (A) while densitometric analysis of blots from 5 experiments using distinct cultures is shown in (B). The mean and standard error for the fold increase is shown, and the fold increase is significant at <i>p</i> < 0.1 (*<i>p</i>= 0.06).</p
Thermosensitive Structural Changes and Adsorption Properties of Zeolitic Imidazolate Framework‑8 (ZIF-8)
We compared four types of ZIF-8 with
varying sizes and shapes to
determine their thermal-structural stability and derive appropriate
thermal activation conditions and correlation between structural characteristics
and adsorption properties. Under air, the ZIF-8 phase for all the
samples was converted completely into the zinc oxide phase above ∼300
°C, though thermalgravimetric analysis (TGA) indicated that the
original structure was stable to ∼300–350 °C. Longer
exposures (∼30 d) suggested that thermal activation at ∼200
°C was appropriate for the removal of guest and/or solvent molecules
under air without structural damage. Despite no noticeable change
in X-ray diffraction (XRD) patterns after activation at 250 °C
under air, the resulting BET surface areas and CO<sub>2</sub> adsorption
amounts (at 1 bar and 30 °C) of ZIF-8s were reduced to ∼44–54
and ∼72–87%, respectively, as compared to those of appropriately
activated ZIF-8s. It appears that after the activation at 250 °C
under air, some Zn and N atoms were dissociated and converted to ZnOH
and NOH, respectively, causing the partial structural damage of ZIF-8s