58 research outputs found
HPDL Remelting of Anodised Al-Si-Cu Cast Alloys Surfaces
The results of the investigations of the laser remelting of the AlSi9Cu4 cast aluminium alloy with the anodised and non-anodised surfacelayer and hardness changes have been presented in this paper. The surface layer of the tested aluminium samples was remelted with thelaser of a continuous work. The power density was from 8,17•103 W/cm2 to 1,63•104 W/cm2. The metallographic tests were conducted inform of light microscope investigations of the received surface layer. The main goal of the investigation was to find the relation betweenthe laser beam power and its power density falling on a material, evaluating the shape and geometry of the remelted layers and theirhardness. As the substrate material two types of surfaces of the casted AlSi9Cu4 alloy were applied – the non–treated as cast surface aswell the anodized surface. As a device for this type of surface laser treatment the High Power Diode Laser was applied with a maximumpower of 2.2 kW and the dimensions of the laser beam focus of 1.8 x 6.8 mm. By mind of such treatment it is also possible to increasehardness as well eliminate porosity and develop metallurgical bonding at the coating-substrate interface. Suitable operating conditions forHPDL laser treatment were finally determined, ranging from 1.0 to 2.0 kW. Under such conditions, taking into account the absorptionvalue, the effects of laser remelting on the surface shape and roughness were studied. The results show that surface roughness is reducedwith increasing laser power by the remelting process only for the non-anodised samples, and high porosity can be found in the with highpower remelted areas. The laser influence increases with the heat input of the laser processing as well with the anodisation of the surface,because of the absorption enhancement ensured through the obtained alumina layer
The effect of heat treatment conditions on the structure evolution and mechanical properties of two binary Al-Mg aluminium alloys
The presented investigation results were carried out on two binary aluminium-magnesium alloys. The article focuses on the influence of heat treatment conditions on the precipitation response of AlMg3 and AlMg5 aluminium alloy, microstructure evolution and strength of the alloys. The microstructure variation was analysed using a scanning electron microscope and an optical microscope in order to characterise the microstructure in a heat treated condition. Tensile tests and hardness measurements were carried out to investigate the effect of heat treatment on the mechanical properties
Perspectives of using polyester waste complete for the manufacture of finished products using the 3D printing method
The effect of long-term impact of elevated temperature on changes in the microstructure of inconel 740H alloy
This paper presents the results of investigations on microstructure changes after the long-term impact of temperature. The microstructure investigations were carried out by light microscopy and scanning electron microscopy. The qualitative and quantitative identification of the existing precipitates was carried out using X-ray phase composition analysis. The effect of elevated temperature on precipitation processes of test material were described. The obtained results of investigations form part of the material characteristics of new-generation alloys, which can be indirectly associated with the stability of functional properties under the simultaneous effect of high temperature and stress
Surface Quality Research for Selective Laser Melting of Ti-6Al-4V Alloy
One of the innovative technology of producing the components is Selective Laser Melting (SLM) belongs to additive manufacturing techniques. SLM technology has already been successfully applied in the automotive, aerospace and medical industries. Despite progress in material flexibility and mechanical performances, relatively poor surface finish still presents a significant weakness in the SLM process
- …