Application of analytical techniques to the unveiling of the glazing technology of medieval pottery from the Belgrade Fortress

Medieval glazed ceramics, dated to the early 15th century, excavated at the Belgrade Fortress, Serbia, were investigated by combining optical microscopy, X-ray powder diffraction (XRPD), scanning electron microscopy with energy-dispersive spectroscopy (SEM-EDS), micro-Raman spectroscopy and multivariate statistical analysis. The decoration and style of the investigated ceramics were characteristic of workshops from different areas of the medieval Serbian State: Ras, Krusevac and Belgrade/Smederevo. Comparison was made with ceramic samples from the same period excavated at the Studenica Monastery, the hitherto earliest workshop discovered, which were used as reference material for the Ras area. Ceramics from the Belgrade Fortress were covered with a transparent, lead-based glaze. The majority of the glazes were produced by application of mixture of lead oxide and quartz to the clay body, whereas only two samples were glazed by application of lead oxide by itself. The brown colours of the glaze originated from Fe-based spinel, whereas copper and iron were responsible for the colouring of the green and yellow glazes. The obtained results revealed glazing technology taken from Byzantine tradition

Formation and Properties of Oxide Coatings with Immobilized Zeolites Obtained by Plasma Electrolytic Oxidation of Aluminum

In this paper, we employed plasma electrolytic oxidation (PEO) of aluminum in a water solution of sodium tungstate (Na2WO42H2O) with the addition of the pure and Ce-loaded zeolites clinoptilolite and 13 X for the preparation of oxide coatings. The obtained coatings were characterized with respect to their morphologies and chemical and phase compositions using scanning electron microscopy coupled with energy-dispersive X-ray spectroscopy, atomic force microscopy, and X-ray diffraction. The prepared coatings contained gamma-alumina, WO3, and metallic tungsten. The surface morphologies of the obtained coatings strongly depended on the PEO processing time; the roughness of all coatings increased with PEO time, while porosity decreased with PEO processing time as a result of microdischarge coalescence and growth. All coatings contained elements originating from the substrate and from the electrolytes. Coatings containing zeolites with Ce showed higher photoactivity than those with immobilized pure zeolites. The highest photocatalytic activity levels were observed for coatings containing immobilized Ce-exchanged clinoptilolite processed for 10 min. It was observed that both clinoptilolite and 13X zeolites improved the features of the PEO coatings in a similar manner, making natural and abundant clinoptilolite an excellent candidate for various applications