Effect of air-abrasion regimens and fine diamond bur grinding on flexural strength, Weibull modulus and phase transformation of zirconium dioxide

PURPOSE This study evaluated the effect of air abrasion and polishing regimens on the flexural strength of yttrium stabilized polycrystalline tetragonal zirconia (Y-TZP). METHODS From Y-TZP blocks (InCeram 2000 YZ Cubes; Vita Zahnfabrik, Bad Säckingen, Germany) 120 bars (25 mm × 4 mm × 1.2 mm) were obtained according to ISO 6872:2008 and randomly divided into 4 groups: Group C: (control) without surface treatment (n = 30); Group APA: Air abrasion with aluminum oxide (44 µm) (n = 30); Group SC: Silica-coating (CoJet, 30 µm) (n = 30); Group FD: Fine diamond bur (n = 30). Subsequently, all specimens were subjected to 4-point bending test (in distilled water at 37°C) in a universal testing machine (EMIC DL 1000; São José dos Pinhais, Paraná, Brazil); cross-head speed: 0.5 mm/min). The characteristic strength (σ0) of each specimen was obtained from the flexural strength test and evaluated using Weibull analysis. X-ray diffraction analysis was utilized to quantity the monoclinic phase. The surface topography of specimens was analyzed using 3D optical profilometer and scanning electron microscopy (SEM) after surface conditioning methods. The flexural strength data (σ4p) were statistically analyzed by 1-way ANOVA, Tukey test (α = 0.05) and Weibull (m = modulus, σ0 = characteristic strength) were calculated. RESULTS The mean ± standard deviations (MPa) of the groups were as follows: C: 1196.2 ± 284.2a; APA: 1369.7 ± 272.3a; SC: 1207.1 ± 229.7a and FD: 874.4 ± 365.4b. The values (m) and (σ0) were as follows: C: 4.5 and 1308.12; APA: 5.9 and 1477.88; SC: 6.0 and 1300.28; and FD: 2.6 and 985.901, respectively. CONCLUSIONS Air particle abrasion with neither silica nor alumina showed significant difference compared to the control group but grinding with fine diamond bur impaired the flexural strength of the zirconia tested

Effects of cement-curing mode and light-curing unit on the bond durability of ceramic cemented to dentin

The aim of this study was to evaluate the effects of different light-curing units and resin cement curing types on the bond durability of a feldspathic ceramic bonded to dentin. The crowns of 40 human molars were sectioned, exposing the dentin. Forty ceramic blocks of VITA VM7 were produced according to the manufacturer's recommendations. The ceramic surface was etched with 10% hydrofluoric acid / 60s and silanized. The dentin was treated with 37% phosphoric acid / 15s, and the adhesive was applied. The ceramic blocks were divided and cemented to dentin according to resin cement / RC curing type (dual- and photo-cured), light-curing unit (halogen light / QTH and LED), and storage conditions (dry and storage / 150 days + 12,000 cycles / thermocycling). All blocks were stored in distilled water (37°C / 24h) and sectioned (n = 10): G1 - QTH + RC Photo, G2 - QTH + RC Dual, G3 - LED + RC Photo, G4 - LED + RC Dual. Groups G5, G6, G7, and G8 were obtained exactly as G1 through G4, respectively, and then stored and thermocycled. Microtensile bond strength tests were performed (EMIC), and data were statistically analyzed by ANOVA and Tukey's test (5%). The bond strength values (MPa) were: G1 - 12.95 (6.40)ab; G2 - 12.02 (4.59)ab; G3 - 13.09 (5.62)ab; G4 - 15.96 (6.32)a; G5 - 6.22 (5.90)c; G6 - 9.48 (5.99)bc; G7 - 12.78 (11.30)ab; and G8 - 8.34 (5.98)bc. The same superscript letters indicate no significant differences. Different light-curing units affected the bond strength between ceramic cemented to dentin when the photo-cured cement was used, and only after aging (LED > QTH). There was no difference between the effects of dual- and photo-cured resin-luting agents on the microtensile bond strength of the cement used in this study

Resistência de união ao push-out entre resina e dentina radicular: Efeito utilização da solução irrigadora antes da cimentação do pino

Objective: To evaluate the effect of different irrigation solutions prior to post cementation on the resin bonding to bovine root dentine. Material and Methods: 60 bovine roots (16 mm) were prepared to 12 mm with specific drill of a double-tapered fiber post system, included in PMMA, and divided into 6 groups, considering the irrigation solutions (IS) prior to cementation: Gr1- saline solution (control), Gr2- NaOCl 0.5 %, Gr3- NaOCl 1 %, Gr4- NaOCl 2.5 %, Gr5- NaOCl 5 %, Gr6- Chlorexidine 2 % (solution). The root canals were irrigated with IS 20 ml during 10 min. Then they were rinsed with 20 ml of distilled water and dried with paper points. One fiber post was molded with polyvinylsiloxane and 60 posts made of resin cement (PRC) were obtained moments before the cementation. The root canal dentin was etched with H2PO3 37 %/15 s + washing/drying, a multi-bottle etch&rinse adhesive system was applied and the PRC were resin luted with dual resin cement (DuolinkTM, Bisco). Each specimen was cut into 4 slices of ±1.8mm in thickness and submitted to push-out test (1 mm/min). Results: ANOVA showed that bond strength was significantly affected by IS (P<0.0001). The highest bond strengths (MPa) were those for the groups 4 (3.51 ± 1.52) and 5 (3.0 ± 1.16). The groups 1 (0.70 ± 0.30), 2 (0.80 ± 0.24), 3 (1.26 ± 0.57) and 6 (0.90 ± 0.41) were statistically similar to each other. Conclusion: The resin bonding to the root dentine was higher when higher concentrations of hypochlorite solutions were used