Sintesis Nano Kristalin Komposit Alumina-zirkonia Dengan Template Pulp Oryza Sativa Melalui Metode Kalsinasi Prekursor

Nano kristalin komposit alumina-zirkonia disintesis melalui metode kalsinasi prekursor dengan pulp oryza sativasebagai template serta Al(NO3)3.9H2O dan ZrCl4 sebagai prekursor dengan komposisi molar 80:20. Pencampuranprekursor, pelarut, dan pulp menggunakan ultra turrax T25 pada RPM 15000 selama 3 menit sebanyak 3 kali.Kalsinasi yang ditujukan untuk memperbaiki morfologi dan pembentukan fasa dilakukan pada temperatur 900,1000, 1100, 1200, dan 1250°C. Untuk mengetahui sifat-sifat dari material komposit yang terbentuk, dilakukankarakterisasi X-Ray Diffraction (XRD) dan Scanning Electron Microscope (SEM). Dari hasil XRD, dapatdiidentifikasi fasa dari komposit yang muncul, yaitu tetragonal-zirkonia, monoklinik-zirkonia, dan δ-alumina. Fasatunggal tetragonal-zirkonia muncul pada sampel yang dikalsinasi pada temperatur 900-1100°C, sementarasampel yang dikalsinasi pada temperatur yang lebih tinggi menghasilkan fasa campuran antara tetragonalzirkoniadan monoklinik-zirkonia. Dari hasil SEM, terlihat bahwa morfologi partikel memiliki bentuk menyerupaibentuk dari pulp, yang mana bentuk ini merupakan akibat dari pencampuran dengan kecepatan tinggi

Zirkonia untuk Aplikasi Material Restorasi Gigi

Dalam paparan ini akan diulas perkembangan zirkonia sebagai material restorasi gigi beserta prospeknya untuk masa depan

Synthesis of zeolite and y-alumina nanoparticles as ceramic membranes for desalination applications

Development of ceramic membrane for desalination is gaining interest in order to provide fresh water for human's life. In this work, a ceramic membrane was developed by coating of porous geopolymer with nanoparticles of gamma alumina (γ-Al2O3) (Al membrane), zeolite (Z membrane), and its combination (Al-Z membrane) which were synthesized through a sol-gel method. Nanoparticles of γ-Al2O3 exhibit rod structures with 10-20 nm in diameter and 40-70 nm in length, a surface area of 326.26 m2/g, total pore volume of 0.10 cm3/g, and an average pore diameter of 2.10 nm. Zeolite nanoparticles were obtained from a composition of 6Na2O: 0.55Al2O3: SiO2: 150H2O having particle sizes in the range from 100 to 400 nm, a surface area of 97.32 m2/g, total pore volume of 0.80 cm3/g, and an average pore diameter of 11.19 nm. The performance of membranes was evaluated by measuring the salt rejection and the flux of NaCl 1% (w/v) solution that was passed through the membrane. The Z membrane demonstrated the highest salt rejection, up to 87.88%, whereas the Al-Z membrane reached 68%. The Al membrane exhibited the lowest salt rejection rate, amounted to 57.14%. The highest flux was obtained using Al membrane, which was to 3.43 × 103 L/m2h on the 54.29% rejection value; whereas the Z membrane reached 3.28 × 103 L/m2h on the 87.88% salt rejection value, and the lowest flux of 2.91 × 103 L/m2h showed by the Al-Z membrane at the 62% salt rejection value. It is promising to use the synthesized γ-Al2O3 and zeolite nanoparticles as alternative ceramic membrane materials to be applied in the desalination