High reliability sheathed, beryllia insulated, tungsten-rhenium alloy thermocouple assemblies; their fabrication and EMF stability

Tantalum sheathed, BeO insulated, W-3% Re/W-25% Re thermocouple assemblies were fabricated and their emf drift determined during 2059 hours of exposure at 2073 K in a gaseous helium environment. The sheathed thermocouple assemblies were constructed from aged thermoelements, specially heat-treated BeO insulators, and specially cleaned and etched tantalum sheaths. Their thermal emf drifts ranged from the equivalent of only -0.3 to -0.8 K drift per 1000 hours of exposure at 2073 K. No evidence of any gross chemical attack or degradation of the component materials was found. The emf drift and material behavior of some unsheathed, BeO insulated, W-3% Re/W-25% Re thermocouples at 2250 and 2400 K were also determined. Unsheathed thermocouples tested in an argon environment at 2250 K for 1100 hours and at 2400 K for 307 hours exhibited changes in thermal emf that typically ranged from the equivalent of a few degrees K to as much as +11 K. Post-test examinations of these thermocouples revealed some undesirable material degradation and interaction which included erosion of the BeO insulators and contamination of the thermoelements by tantalum from the tantalum blackbody enclosure in which the thermocouples were contained

The calibration of thermocouples and thermocouple materials /

"April 1989."Includes bibliographical references.Mode of access: Internet

New reference tables for platinum 10% rhodium/platinum and platinum 13% rhodium/platinum thermocouples

NRC publication: Ye