Fabrication of Worm-Like Nanorods and Ultrafine Nanospheres of Silver Via Solid-State Photochemical Decomposition

Worm-like nanorods and nanospheres of silver have been synthesized by photochemical decomposition of silver oxalate in water by UV irradiation in the presence of CTAB and PVP, respectively. No external seeds have been employed for the synthesis of Ag nanorods. The synthesized Ag colloids have been characterized by UV-visible spectra, powder XRD, HRTEM, and selected area electron diffraction (SAED). Ag nanospheres of average size around 2 nm have been obtained in the presence of PVP. XRD and TEM analyses revealed that top and basal planes of nanorods are bound with {111} facets. Williamson–Hall plot has revealed the presence of defects in the Ag nanospheres and nanorods. Formation of defective Ag nanocrystals is attributed to the heating effect of UV-visible irradiation

A Rapid Synthesis of Oriented Palladium Nanoparticles by UV Irradiation

Palladium nanoparticles of average size around 8 nm have been synthesized rapidly by UV irradiation of mixture of palladium chloride and potassium oxalate solutions. A rod-shaped palladium oxalate complex has been observed as an intermediate. In the absence of potassium oxalate, no Pd nanoparticles have been observed. The synthesized Pd nanoparticles have been characterized by powder X-ray diffraction (XRD), transmission electron microscopy (TEM), selective area electron diffraction and energy dispersive analysis by X-rays (EDAX) analyses. XRD analysis indicates the preferential orientation of catalytically active {111} planes in Pd nanoparticles. A plausible mechanism has been proposed for the formation of anisotropic Pd nanoparticles

Thermal decomposition as route for silver nanoparticles

Single crystalline silver nanoparticles have been synthesized by thermal decomposition of silver oxalate in water and in ethylene glycol. Polyvinyl alcohol (PVA) was employed as a capping agent. The particles were spherical in shape with size below 10 nm. The chemical reduction of silver oxalate by PVA was also observed. Increase of the polymer concentration led to a decrease in the size of Ag particles. Ag nanoparticle was not formed in the absence of PVA. Antibacterial activity of the Ag colloid was studied by disc diffusion method

Synthesis of Indium Nanowires by Galvanic Displacement and Their Optical Properties

<p>Abstract</p> <p>Single crystalline indium nanowires were prepared on Zn substrate which had been treated in concentrated sulphuric acid by galvanic displacement in the 0.002 mol L^&#8722;1In₂(SO₄)₃-0.002 mol L^&#8722;1SeO₂-0.02 mol L^&#8722;1SDS-0.01 mol L^&#8722;1citric acid aqueous solution. The typical diameter of indium nanowires is 30 nm and most of the nanowires are over 30 &#956;m in length. XRD, HRTEM, SAED and structural simulation clearly demonstrate that indium nanowires are single-crystalline with the tetragonal structure, the growth direction of the nanowires is along [100] facet. The UV-Vis absorption spectra showed that indium nanowires display typical transverse resonance of SPR properties. The surfactant (SDS) and the pretreatment of Zn substrate play an important role in the growth process. The mechanism of indium nanowires growth is the synergic effect of treated Zn substrate (hard template) and SDS (soft template).</p