Until this book, most treatments of this topic were inaccessible to nonspecialists. A superb introduction to important areas of modern physics, it covers Feynman diagrams, quasi particles, Fermi systems at finite temperature, superconductivity, vacuum amplitude, Dyson's equation, ladder approximation, and much more. ""A great delight to read."" - Physics Today. 1974 edition

Zirconium Carbide Oxidation: Maltese Cross Formation and Interface Characterization

Oxidation of dense hot-pressed ZrC specimens from 1073 to 1473 K was investigated using an in situ technique: HT-ESEM. Cuboid specimens were monitored on the surface and on edges and corners during oxidation in order to understand the influence of crack formation and propagation on the Maltese cross shape development of the oxide. The oxidation mechanism comprised three steps: (1) delamination of sample edges, (2) crack formation at corners and (3) crack propagation towards the inner core and formation of microcracks parallel to the interface that increase the accessible surface area followed by a drastic volume expansion. The microcrack pattern is found to be repetitive as if a cyclic debonding of the interface occurred. Characterization of the interface by TEM and HRTEM reveale