Identification of chemically modified peptide from poly(D,L-lactide-co-glycolide) microspheres under in vitro release conditions

The purpose of this research was to study the chemical reactivity of a somatostatin analogue octreotide acetate, formulated in microspheres with polymers of varying molecular weight and co-monomer ratio under in vitro testing conditions. Poly(D,L-lactide-co-glycolide) (PLGA) and poly(D,L-lactide) (PLA) microspheres were prepared by a solvent extraction/evaporation method. The microspheres were characterized for drug load, impurity content, and particle size. Further, the microspheres were subjected to in vitro release testing in acetate buffer (pH 4.0) and phosphate buffered saline (PBS) (pH 7.2). In acetate buffer, 3 microsphere batches composed of low molecular weight PLGA 50∶50, PLGA 85∶15, and PLA polymers (≤10 kDa) showed 100% release with minimal impurity formation (<10%). The high molecular weight PLGA 50∶50 microspheres (28 kDa) displayed only 70% cumulative release in acetate buffer with significant impurity formation (∼24%). In PBS (pH 7.4), on the other hand, only 50% release was observed with the same low molecular weight batches (PLGA 50∶50, PLGA 85∶15, and PLA) with higher percentages of hydrophobic impurity formation (ie, 40%, 26%, and 10%, respectively). In addition, in PBS, the high molecular weight PLGA 50∶50 microspheres showed only 20% drug release with ∼60% mean impurity content. The chemically modified peptide impurities inside microspheres were structurally confirmed through Fourier transform-mass spectrometry (FT-MS) and liquid chromatography/mass spectrometry (LC-MS/MS) analyses after extraction procedures. The adduct compounds were identified as covalently modified conjugates of octreotide with lactic and glycolic acid monomers within polymeric microspheres. The data suggest that due to steric hindrance factors, polymers with greater lactide content were less amenable to the formation of adduct impurities compared with PLGA 50∶50 copolymers

A Novel Injection-Molded Capsular Device for Oral Pulsatile Delivery Based on Swellable/Erodible Polymers

The feasibility of injection molding was explored in the preparation of a novel capsular device for oral pulsatile/delayed delivery based on swellable/erodible polymers. For this purpose, a mold intended to be coupled with a bench-top injection-molding press was designed. This was expected to enable the preparation of matching capsule cap and body items within a single manufacturing cycle and the selection of differing shell thicknesses (300, 600, and 900 μm). Hydroxypropylcellulose (Klucel® EF, LF, and GF) was employed as the release-controlling polymer in admixture with polyethylene glycol 1500 (10%, w/w) as the plasticizer. After preliminary trials aimed at the setup of operating conditions, Klucel® EF and LF capsule shells with satisfactory technological properties were manufactured. The performance of capsular devices filled with a tracer drug powder was studied by means of a modified USP31 disintegration apparatus. Typical in vitro delayed release patterns were thereby obtained, with lag time increasing as a function of the wall thickness. A good correlation was found between the latter parameter and t10%, i.e., the time to 10% release, for both polymer grades employed. On the basis of the overall results, the investigated technique was proven suitable for the manufacturing of an innovative pulsatile release platform

Preparation and stability of poly(ethylene glycol) (PEG)ylated octreotide for application to microsphere delivery

The purpose of this study was to prepare poly(ethylene glycol) (PEG)ylated octreotide and investigate the stability against acylation by polyester polymers such as poly(lactic acid) and poly(lactic-co-glycolic acid). Octreotide was modified by reaction with monomethoxy PEG-propionaldehyde (molecular weight 5,000) in the presence of sodium cyanoborohydride. The mono-PEGylated fraction was isolated by reverse-phase high-performance liquid chromatography (HPLC) and characterized by matrixassisted laser desorption/ionization time-of-flight mass spectrometry (MALDI-TOF MS). Circular dichroism demonstrated no significant secondary structural differences between mono-PEGylated octreotide (mono-PEG-octreotide) and intact octreotide. As a test system for the stability study against acylation reaction, lactic acid (LA) solutions with various concentrations and pH values were prepared with water dilution and subsequent accelerated equilibration at 90°C for 24 hours. Native octreotide was found to be acylated in all the diluted LA solutions with different concentrations (42.5%, 21.3%, and 8.5%, wt/wt) and pH values (2.25, 1.47, and 1.85, respectively). The remaining amounts of intact octreotide continuously decreased to 50% through 30 days of incubation at 37°C. MALDI-TOF MS identified the octreotide to be acylated by LA units. However, acylation reaction of mono-PEG-octreotide in LA solutions was negligible, and the remaining amounts of intact one through 30 days of incubation in LA solutions were also comparable to the initial concentration. These data suggest that mono-PEG-octreotide may prevent the acylation reaction in degrading PLA microspheres and possibly serve as a new source for somatostatin microsphere formulation