Complicated skin, skin structure and soft tissue infections - are we threatened by multi-resistant pathogens?

Tissue infections or skin, skin structure, and deep seated soft tissue infections are general terms for infections of the entire skin layer including the subcutaneous and muscle tissue layers and their respective fascia structures. Infections of the different mediastinal fascias (mediastinitis) and retroperitoneal fascia infections also belong to this category. Due to the variability of their clinical presentation, skin and soft tissue infections can be classified according to different features. The following aspects can be used for classification

Synthesis and thermal analysis of indium-based hydrotalcites of formula Mg6In2(CO3)(OH)16.4H2O

Insight into the unique structure of layered double hydroxides has been obtained using a combination of X-ray diffraction and thermal analysis. Indium containing hydrotalcites of formula Mg4In2(CO3)(OH)12•4H2O (2:1 In-LDH) through to Mg8In2(CO3)(OH)18•4H2O (4:1 In-LDH) with variation in the Mg:In ratio have been successfully synthesised. The d(003) spacing varied from 7.83 Å for the 2:1 LDH to 8.15 Å for the 3:1 indium containing layered double hydroxide. Distinct mass loss steps attributed to dehydration, dehydroxylation and decarbonation are observed for the indium containing hydrotalcite. Dehydration occurs over the temperature range ambient to 205 °C. Dehydroxylation takes place in a series of steps over the 238 to 277 °C temperature range. Decarbonation occurs between 763 and 795 °C. The dehydroxylation and decarbonation steps depend upon the Mg:In ratio. The formation of indium containing hydrotalcites and their thermal activation provides a method for the synthesis of indium oxide based catalysts

Synthesis and thermal stability of hydrotalcites based upon gallium

Hydrotalcites based upon gallium as a replacement for aluminium in hydrotalcite over a Mg/Al ratio of 2:1 to 4:1 were synthesised. The d(003) spacing varied from 7.83 A ° for the 2:1 hydrotalcite to 8.15 A ° for the 3:1 gallium containing hydrotalcite. A comparison is made with the Mg Al hydrotalcite in which the d(003) spacing for the Mg/Al hydrotalcite varied from 7.62 A ° for the 2:1Mg hydrotalcite to 7.98 A ° for the 4:1 hydrotalcite. The thermal stability of the gallium containing hydrotalcite was determined using thermogravimetric analysis. Four mass loss steps at 77, 263–280,485 and 828 degrees C with mass losses of 10.23, 21.55, 5.20 and 7.58% are attributed to dehydration, dehydroxylation and decarbonation. The thermal stability of the galliumcontaining hydrotalcite is slightly less than the aluminium hydrotalcite

Thermal decomposition of the synthetic hydrotalcite woodallite

The thermal stability and thermal decomposition pathways for synthetic woodallite have been determined using thermogravimetry in conjunction with evolved gas mass spectrometry. Chemical analysis showed the formula of the synthesised woodallite to be Mg6.28Cr1.72Cl(OH)16(CO3)0.36⋅8.3H2O and X-ray diffraction confirms the layered LDH structure. Dehydration of the woodallite occurred at 65°C. Dehydroxylation occurred at 302 and 338°C. Both steps were associated with the loss of carbonate. Hydrogen chloride gas was evolved over a wide temperature range centred on 507°C. The products of the thermal decomposition were MgO and a spinel MgCr2O4. Experimentally it was found to be difficult to eliminate CO2 from inclusion in the interlayer during the synthesis of the woodallite compound and in this way the synthesised woodallite resembled the natural mineral