Alloy composition effects on oxidation products of VIA, B-1900, 713C, and 738X: A high temperature diffractometer study

High temperature X-ray diffraction studies were performed to investigate isothermal and cyclic oxidation at 1000 and 1100 C of the nickel-base superalloys VIA, B-1900, 713C, and 738X. Oxidation was complex. The major oxides, Al2O3, Cr2O3, and the spinels, formed in amounts consistent with alloy chemistry. The alloys VIA and B-1900 (high Al, low Cr alloys) tended to form Al2O3 and NiAl2O4; 738X (high Cr, low Al) formed Cr2O3 and NiCr2O4. A NiTa2O6 type of oxide formed in amounts approximately proportional to the refractory metal content of the alloy. One of the effects of cycling was to increase the amount of spinels formed

Addition of silicon improves oxidation resistance of nickel based superalloys

Specific weight changes of nickel-base superalloy B-1900 and B-1900 + 1% Si specimens were tested at 1273 K. B-1900 was losing weight at an increasing rate due to spalling of oxide scale while B-1900 + 1% Si was still gaining weight at low, nearly constant rate. Similar comparison in weight change was observed for specimens tested at 1373 K

Failure mechanisms of thermal barrier coatings exposed to elevated temperatures

The failure of a ZrO2-8%Y2O3/Ni-14% Al-0.1% Zr coating system on Rene 41 in Mach 0.3 burner rig tests was characterized. High flame and metal temperatures were employed in order to accelerate coating failure. Failure by delamination was shown to precede surface cracking or spalling. This type of failure could be duplicated by cooling down the specimen after a single long duration isothermal high temperature cycle in a burner rig or a furnace, but only if the atmosphere was oxidizing. Stresses due to thermal expansion mismatch on cooling coupled with the effects of plastic deformation of the bond coat and oxidation of the irregular bond coat are the probable life limiting factors. Heat up stresses alone could not fail the coating in the burner rig tests. Spalling eventually occurs on heat up but only after the coating has already failed through delamination

Effects of silicon additions on oxidation and mechanical behavior of the nickel-base superalloy B-1900

Test specimens with nominal additions of Si were tested in oxidation, thermal fatigue, sulfidation, tension, and stress rupture, and were also extensively studied metallographically. Alloy B-1900 modified with 0.6- or 1.2-wt% Si exhibited oxidation resistance equivalent to that of aluminide-coated B-1900 during cyclic, high-gas-velocity oxidation tests. Resistances to thermal fatigue and sulfidation were improved by the Si additions, but were not superior to aluminide-coated B-1900. Stress-rupture tests at 1000 C of specimens given the standard heat treatment to simulate an aluminide coating cycle showed Si to be detrimental. However, application of another heat treatment increased the rupture life of the alloy with 0.6-wt% Si to that of the unmodified B-1900 given the standard heat treatment

Thermal expansion in the nickel-chromium-aluminum and cobalt-chromium-aluminum systems to 1200 degrees C

Thermal expansion data were obtained on 12 Ni-Cr-Al and 9 Co-Cr-Al alloys by high temperature X-ray diffraction. The data were computer fit to an empirical thermal expansion equation developed in the study. It is shown that the fit is excellent to good, and that the expansion constants depend on phase but not on composition. Phases for the Ni-Cr-Al system and Co-Cr-Al system are given. Results indicate that only alpha Cr has an expansion constant low enough to minimize oxide spalling or coating cracking induced by thermal expansion mismatch